Calcined polyhydroxysilicate polymer reaction product

Claim 2

A shaped structure formed from the reaction of a non fibrous calcined residue of chrysotile asbestos derived from chrysotile asbestos tailings having a particle size extending from fibrous to -325 mesh and a hydroxy-containing polymer selected from the group consisting of a phenol-formaldehyde polymer, a resorcinol-formaldehyde polymer, a phenol-resorcinol-formaldehyde polymer and an epoxy resin, said shaped structure being characterized by the total absence of any fibrous material, the new product representing a characteristic repeating magnesium oxide-resin bond of the formula: ##STR8## wherein in R is the residue of said hydroxy-containing polymer, the amount of calcined residue of chrysotile asbestos tailings being from 5 to 90% by weight and the amount of polymer being from 90 to 5% by weight.

Claim 3

The shaped structure of claim 1, wherein the polymer is a phenol-formaldehyde polymer.

Claim 4

The shaped structure of claim 1, wherein the polymer is an epoxy resin.

Claim 5

The shaped structure of claim 1, wherein the polymer is a resorcinol-formaldehyde polymer.

Claim 6

The shaped structure of claim 1, wherein the polymer is a mixture of phenol-formaldehyde and resorcinol-formaldehyde.

Claim 7

A process which comprises calcining chrysotile asbestos tailings having a particle size of from -28 to -325 mesh at a temperature within the range of from 700° to 900° C., mixing the calcined residue with a hydroxy-containing polymer selected from the group consisting of phenol-formaldehyde polymers, resorcinol-formaldehyde polymers, phenol-resorcinol-formaldehyde polymers and epoxy resins, and shaping said reaction mixture in a mold under pressure at a temperature ranging from 100° to 170° C. when the hydroxy-containing polymer is other than an epoxy resin and at room temperature when the hydroxy-containing resin is an epoxy resin.

Claim 8

A process which comprises calcining chrysotile asbestos tailings having a particle size of from -28 to -325 mesh at a temperature within the range of from 700° to 900° C., mixing the calcined residue with a hydroxy-containing polymer selected from the group consisting of phenol-formaldehyde polymers, resorcinol-formaldehyde polymers, phenol-resorcinol-formaldehyde polymers and epoxy resins, and shaping said reaction mixture in a mold under pressure at a temperature ranging from 100° to 170° C. when the hydroxy-containing polymer is other than an epoxy resin and at room temperature when the hydroxy-containing resin is an epoxy resin.

Claim 9

The process of claim 6, which comprises calcining a chrysotile asbestos tailing having a -200 mesh at a temperature of about 900° C., mixing said calcined material with a phenol-formaldehyde resin, shaping the mixture thus obtained in a mold heated to a temperature of from 135° to 160° C. under a pressure of about 800 psi.

Claim 10

The process of claim 6, which comprises calcining a chrysotile asbestos tailing having a -200 mesh at a temperature of about 900° C., mixing said calcined material with an epoxy resin, shaping the mixture thus obtained in a mold at room temperature under a pressure of from 50 to 100 psi.

Claim 11

A process for preparing a shaped structure which comprises calcining chrysotile asbestos tailings having a particle size of from -28 to -325 mesh thereby to obtain a basic anhydrous oxide of the formula: ##STR9## mixing said basic anhydrous oxide with an acidic hydroxy-containing polymer selected from phenol-formaldehyde polymers, resorcinol-formaldehyde polymers, phenol-resorcinol-formaldehyde polymers and epoxy resins, reacting said mixture in a mold at a temperature of from 100° to 170° C. and under a pressure of from 700 to 900 psi when the hydroxy-containing polymer is other than an epoxy resin and at room temperature and a pressure of from 50 to 100 psi when the hydroxy-containing polymer is an epoxy resin whereby there is obtained a shaped structure devoid of any fibrous material and characterized by a repeating unit of magnesium oxide-resin bond of the formula: ##STR10## wherein R is the residue of the hydroxy-containing polymer.

Claim 12

A process for preparing a shaped structure which comprises calcining chrysotile asbestos tailings having a particle size of from -28 to -325 mesh thereby to obtain a basic anhydrous oxide of the formula: ##STR9## mixing said basic anhydrous oxide with an acidic hydroxy-containing polymer selected from phenol-formaldehyde polymers, resorcinol-formaldehyde polymers, phenol-resorcinol-formaldehyde polymers and epoxy resins, reacting said mixture in a mold at a temperature of from 100° to 170° C. and under a pressure of from 700 to 900 psi when the hydroxy-containing polymer is other than an epoxy resin and at room temperature and a pressure of from 50 to 100 psi when the hydroxy-containing polymer is an epoxy resin whereby there is obtained a shaped structure devoid of any fibrous material and characterized by a repeating unit of magnesium oxide-resin bond of the formula: ##STR10## wherein R is the residue of the hydroxy-containing polymer.