Assignee: Oerlikon Metco US Inc
•
Filing: 1978-08-23
•
Granted: 1981-06-30
•
Expires: 1998-08-23
Abstract
Abstract A self-bonding flame spray wire capable of forming a readily grindable coating formed of a sheath of aluminum and a compacted powder core containing a major portion of nickel and stainless steel and a minor portion of aluminum and metal oxide. The core may contain from about 10 to 90 percent, and preferably about 61 percent, by weight nickel, about 10 to 90, and preferably 30, percent by weight stainless steel, from 1 to 10 percent by weight, and preferably 5 percent by weight, aluminum, from 1/4 to 10 percent by weight, and preferably 4 percent by weight, of the metal oxide which may, for example, be cobalt oxide or zirconium oxide, and is most preferably zirconium oxide.
Inventors
- 👤 Edward R. Novinski
- 👤 John H. Harrington
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 23:04
CPC Classifications
C; C23; C23C; C23C4/00; C23C4/04; C23C4/06; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063; Y10T428/12097; Y10T428/12222
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
81 words
A self-bonding flame spray wire capable of forming a readily grindable coating, comprising a sheath of aluminum and a compacted powder core containing about 10 to 90% by weight of nickel, about 10 to 90% by weight of stainless steel, about 1 to 10% aluminum, and about 1/4 to 10% metal oxide, based on the total powder compacted core, said stainless steel and metal oxide content being in sufficient quantity and proportions that when sprayed will produce a readily grindable coating.
Claim 2
Dependent Claim
81 words
A self-bonding flame spray wire capable of forming a readily grindable coating, comprising a sheath of aluminum and a compacted powder core containing about 10 to 90% by weight of nickel, about 10 to 90% by weight of stainless steel, about 1 to 10% aluminum, and about 1/4 to 10% metal oxide, based on the total powder compacted core, said stainless steel and metal oxide content being in sufficient quantity and proportions that when sprayed will produce a readily grindable coating.
Claim 3
Dependent Claim
25 words
A flame spray wire according to claim 1, in which said nickel in said compacted powder core is present in the amount of about 61%.
Claim 4
Dependent Claim
28 words
A flame spray wire according to claim 1, in which said stainless steel in said compacted powder core is present in the amount of about 30% by weight.
Claim 5
Dependent Claim
27 words
A flame spray wire according to claim 1, in which said aluminum in said compacted powder core is present in the amount of about 5% by weight.
Claim 6
Dependent Claim
28 words
A flame spray wire according to claim 1, in which said metal oxide in said compacted powder core is present in the amount of about 4% by weight.
Claim 7
Dependent Claim
83 words
A flame spray wire according to claim 1, in which said nickel in said compacted powder core is present in the amount of about 61%, in which said stainless steel in said compacted powder core is present in the amount of about 30%, in which said aluminum in said compacted powder core is present in the amount of about 5% by weight, and in which said metal oxide in said compacted powder core is present in the amount of about 4% by weight.
Claim 8
Dependent Claim
21 words
A flame spray wire according to any one of claims 1 to 6, in which said metal oxide is zirconium oxide.
Claim 9
Dependent Claim
21 words
A flame spray wire according to any one of claims 1 to 6, in which said metal oxide is cobalt oxide.
References Cited (Backward Citations)
US2588421A
Cited
US3332753A
Cited
US3322515A
Cited
US3695951A
Cited
US3844729A
Cited
US3890174A
Cited
US4060653A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-29 | 1984-12-29 | 1985-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-29 | 1988-12-29 | 1989-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-29 | 1992-12-29 | 1993-06-30 | $7700.00 | Window Closed / Lapsed |