Adhesive-coated impregnated polyurethane foam

Claim 2

A process for producing a resilient, non-porous, significantly non-absorbent pressure-sensitive adhesive tape that consists essentially of impregnating a substrate of open-celled, high density, flexible, resilient polyurethane foam with a polychloroprene latex, compressing said latex-impregnated substrate to cause said latex to penetrate through said polyurethane foam and permitting said substrate to return to its pre-compressed state; depositing a layer of a pressure-sensitive adhesive upon said impregnated substrate, and curing each of said polychloroprene and pressure-sensitive adhesive simultaneously or in separate steps.

Claim 3

A method as claimed in claim 1, wherein said pressure-sensitive adhesive is an acrylic resin and is deposited upon a release tape and brought into contact with said impregnated substrate whereupon said adhesive is cured thereon.

Claim 4

A process as claimed in claim 2, wherein said impregnated substrate is compressed to within a range between one-third to two-thirds of its thickness immediately prior to compression.

Claim 5

A process as claimed in claim 3, wherein said compression is effected to about one-half of the thickness of said impregnated substrate in its pre-compressed state immediately prior to compression.

Claim 6

A process for producing a resilient, pressure-sensitive adhesive tape that consists essentially of impregnating an open-cell, flexible, polyurethane foam substrate, said foam, prior to impregnation, having a density of 20 pounds per cubic inch to 60 pounds per cubic inch and wherein the open-cell structure thereof as represented by absence of cell membranes is within the range of about 17 percent to about 100 percent, with a polychloroprene latex having a Brookfield viscosity of from 23 centipoises to 250 centipoises, compressing the polychloropreneimpregnated substrate so formed, and permitting said substrate to return to its immediately pre-compressed state; coating the resulting impregnated substrate with an acrylic resin adhesive; and curing said polychloroprene and adhesive thereon simultaneously or in separate steps.

Claim 7

A process for producing a resilient, pressure-sensitive adhesive tape that consists essentially of impregnating an open-cell, flexible, polyurethane foam substrate, said foam, prior to impregnation, having a density of 20 pounds per cubic inch to 60 pounds per cubic inch and wherein the open-cell structure thereof as represented by absence of cell membranes is within the range of about 17 percent to about 100 percent, with a polychloroprene latex having a Brookfield viscosity of from 23 centipoises to 250 centipoises, compressing the polychloropreneimpregnated substrate so formed, and permitting said substrate to return to its immediately pre-compressed state; coating the resulting impregnated substrate with an acrylic resin adhesive; and curing said polychloroprene and adhesive thereon simultaneously or in separate steps.

Claim 8

A process as claimed in claim 5, wherein said foam, prior to impregnation, has a density of 40 pounds per cubic inch.

Claim 9

A process as claimed in claim 5, wherein said latex has a specific gravity of from 1.10 to 1.12 and a solids content by weight of 50 percent to 60 percent.

Claim 10

A process as claimed in claim 5, wherein said impregnated polychloroprene is initially cured; said coating of acrylic resin adhesive is deposited upon said impregnated substrate and said adhesive is thereupon cured.

Claim 11

A process as claimed in claim 5, wherein said pressuresensitive adhesive is an acrylic resin.