Manufacture of activated carbon
Assignee: Siebe Gorman and Co Ltd
•
Filing: 1979-09-07
•
Granted: 1981-06-23
•
Expires: 1999-09-07
Abstract
Abstract Activated carbon is made by pre-treating a fibrous cellulose material with a Lewis acid comprising one or more selected halides, drying and softening the treated material, suspending the material from a frame in a tensionless manner, heating the suspended material in a furnace to effect carbonization of the cellulosic material in an environment which is substantially non-reactive towards that material, activating the suspended carbonized material at an elevated temperature in an atmosphere comprising an activating gas until the desired degree of activation has been produced, and thereafter cooling the furnace, the furnace having at least one heating element at its base and at least one heating element arranged on or in a side wall, each heating element being spaced apart from the suspended material.
Inventors
- 👤 Keith Simpson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 08:46
CPC Classifications
B; B01; B01D; B01D39/00; B01D39/08; B01D39/083; A; A24; A24D; A24D3/00; A24D3/06; A24D3/16; A24D3/163; B01D39/086; C; C01; C01B; C01B32/00; C01B32/30; C01B32/312; C01B32/336; C01B32/354; C01B32/382; B01D2239/00; B01D2239/04; B01D2239/10; B01D2239/12; B01D2239/1233; B01D2239/1291
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
214 words
A batch process for the manufacture of activated carbon, which comprises; (a) treating a fibrous cellulosic material by contacting it with at least one Lewis acid selected from the group consisting of halides of zinc, aluminum, calcium, magnesium, iron, barium, ammonium and chromium; (b) drying the treated material; (c) subjecting the dried material to a mechanical softening treatment; (d) suspending the softened material from a frame in a tensionless manner, said frame being positioned within a furnace adapted to effect carbonisation of the cellulosic material, the furnace having at least one heating element at its base and at least one heating element arranged on a side wall, each heating element being spaced apart from the suspended material, whereby said suspending places a plurality of the fibers in the fibrous cellulosic material transverse across the furnace; (e) heating the suspended material in said furnace to effect carbonisation of the cellulosic material; in an environment which is substantially non-reactive towards the material, said heat being directed into the suspended material from a first direction on the side of the suspended material and from a second direction beneath the suspended material; (f) activating the suspended carbonised material in an activating gas until the desired degree of activation has been produced; and (g) thereafter cooling the activated material.
Claim 2
Dependent Claim
214 words
A batch process for the manufacture of activated carbon, which comprises; (a) treating a fibrous cellulosic material by contacting it with at least one Lewis acid selected from the group consisting of halides of zinc, aluminum, calcium, magnesium, iron, barium, ammonium and chromium; (b) drying the treated material; (c) subjecting the dried material to a mechanical softening treatment; (d) suspending the softened material from a frame in a tensionless manner, said frame being positioned within a furnace adapted to effect carbonisation of the cellulosic material, the furnace having at least one heating element at its base and at least one heating element arranged on a side wall, each heating element being spaced apart from the suspended material, whereby said suspending places a plurality of the fibers in the fibrous cellulosic material transverse across the furnace; (e) heating the suspended material in said furnace to effect carbonisation of the cellulosic material; in an environment which is substantially non-reactive towards the material, said heat being directed into the suspended material from a first direction on the side of the suspended material and from a second direction beneath the suspended material; (f) activating the suspended carbonised material in an activating gas until the desired degree of activation has been produced; and (g) thereafter cooling the activated material.
Claim 3
Dependent Claim
16 words
A process as claimed in claim 1, wherein the fibrous cellulosic material comprises a cellulosic fabric.
Claim 4
Dependent Claim
23 words
A process as claimed in claim 2, wherein the height of the fabric configuration suspended from the frame does not exceed 5 meters.
Claim 5
Dependent Claim
16 words
A process as claimed in claim 3, wherein the said height does not exceed 2 meters.
Claim 6
Dependent Claim
18 words
A process as claimed in claim 2, wherein the fabric is suspended in the form of a spiral.
Claim 7
Dependent Claim
32 words
A process as claimed in claim 2, wherein the distance between suspension points of adjacent turns or folds of the suspended fabric is in the range of from 1 to 5 cm.
Claim 8
Dependent Claim
28 words
A process as claimed in claim 2, wherein the distance between suspension points along each individual turn or fold of the suspended fabric does not exceed 15 cm.
Claim 9
Dependent Claim
39 words
A process as claimed in claim 1, wherein the distance between the suspended configuration and the inside of the furnace, measured before any shrinkage of the material has occurred, is in the range of from 10 to 20 cm.
Claim 10
Dependent Claim
28 words
A process as claimed in claim 1, wherein there is a plurality of circumferentially extending heating elements arranged at spaced intervals up the side wall of the furnace.
Claim 11
Dependent Claim
32 words
A process as claimed in claim 1, wherein there is a plurality of upwardly extending heating elements arranged in a circumferentially extending array in or on the side wall of the furnace.
Claim 12
Dependent Claim
34 words
A process as claimed in claim 1, wherein the heating elements are arranged to maintain a uniform temperature up the side wall of the furnace in the region occupied by the suspended fibrous material.
Claim 13
Dependent Claim
25 words
A process as claimed in claim 1, wherein the base of the furnace is provided with heating elements arranged in the form of a cross.
Claim 14
Dependent Claim
25 words
A process as claimed in claim 1, wherein the heating elements are arranged to transfer heat to the suspended material by direct radiation and convection.
Claim 15
Dependent Claim
26 words
A process as claimed in claim 1, wherein the rate at which the heating of the furnace is increased does not exceed 6° C. per minute.
Claim 16
Dependent Claim
18 words
A process as claimed in claim 14, wherein the said rate does not exceed 4° C. per minute.
Claim 17
Dependent Claim
26 words
A process as claimed in claim 1, wherein the rate at which the heating of the furnace is increased is at least 1.5° C. per minute.
Claim 18
Dependent Claim
33 words
A process as claimed in claim 1, wherein the rate at which the heating of the furnace is increased during carbonisation of the fibrous cellulosic material does not exceed 3° C. per minute.
Claim 19
Dependent Claim
37 words
A process as claimed in claim 1, wherein the rate at which the heating of the furnace is increased during activation of the fibrous material is greater than the rate of increase during carbonisation of the material.
Claim 20
Dependent Claim
19 words
A process as claimed in claim 1, wherein a temperature of at least 870° C. is established during activation.
Claim 21
Dependent Claim
19 words
A process as claimed in claim 19, wherein a temperature of at least 900° C. is established during activation.
Claim 22
Dependent Claim
18 words
A process as claimed in claim 1, wherein the temperature established during activation does not exceed 1000° C.
Claim 23
Dependent Claim
18 words
A process as claimed in claim 21, wherein the temperature established during activation does not exceed 950° C.
Claim 24
Dependent Claim
25 words
A process as claimed in claim 1, wherein the maximum temperature established during activation is in the range of from 910° C. to 930° C.
Claim 25
Dependent Claim
41 words
A process as claimed in claim 1, wherein the temperature of the furnace is held during carbonisation for a period of from 15 to 60 minutes within a 10° C. band in the range of form 315° C. to 350° C.
Claim 26
Dependent Claim
18 words
A process as claimed in claim 24, wherein the said band extends from 315° C. to 325° C.
Claim 27
Dependent Claim
41 words
A process as claimed in claim 1, wherein the temperature of the furnace is held during carbonisation for a period of from 15 to 60 minutes within a 10° C. band in the range of from 130° C. to 315° C.
Claim 28
Dependent Claim
38 words
A process as claimed in claim 1, wherein during activation the furnace is maintained at a temperature within the range of from 870° to 1000° C. for a period of at least 30 minutes before cooling is commenced.
Claim 29
Dependent Claim
37 words
A process as claimed in claim 1, wherein during activation the furnace is maintained at a temperature in the range of from 870° to 1000° C. for a period not exceeding 45 minutes before cooling is commenced.
Claim 30
Dependent Claim
34 words
A process as claimed in claim 1, wherein the carbonisation is conducted in an atmosphere comprising at least one inert gas selected from the group consisting of nitrogen, carbon dioxide, helium, argon and steam.
Claim 31
Dependent Claim
24 words
A process as claimed in claim 1, wherein the atmosphere in the furnace during activation comprises at least one of carbon dioxide and steam.
Claim 32
Dependent Claim
26 words
A process as claimed in claim 1, wherein the carbonisation and activation of the material is conducted under a pressure not exceeding 25 cm. of water.
Claim 33
Dependent Claim
30 words
A process as claimed in claim 1, wherein a current of gas is passed through the furnace during carbonisation to remove volatile decomposition products formed during carbonisation of the material.
Claim 34
Dependent Claim
16 words
A process as claimed in claim 1, wherein said group of Lewis acids consists of chlorides.
Claim 35
Dependent Claim
19 words
A process as claimed in claim 1, wherein the mechanical softening treatment is effected with a textile breaking machine.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-22 | 1984-12-22 | 1985-06-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-22 | 1988-12-22 | 1989-06-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-22 | 1992-12-22 | 1993-06-23 | $7700.00 | Window Closed / Lapsed |