Intumescent fire retardant composites
Assignee: 3M Co
•
Filing: 1979-06-28
•
Granted: 1981-06-16
•
Expires: 1999-06-28
Abstract
Abstract The disclosure relates to flexible heat expanding, fire retardant composite materials comprising an intumescent component in granular form, an organic binder component such as an elastomer, an organic char-forming component and fillers such as clay, silica, synthetic organic staple fibers or inorganic fiberglass or ceramic fibers. These composites, when subjected to heat at about 110° C., can intumesce up to ten times their original volume.
Inventors
- 👤 Roger L. Langer
- 👤 Richard R. Licht
- 👤 Alan J. Marlor
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 12:35
CPC Classifications
C; C09; C09K; C09K21/00; C09K21/14; C08; C08K; C08K3/00; C08K3/34; C09D; C09D5/00; C09D5/18; C09D5/185; Y; Y10; Y10S; Y10S521/00; Y10S521/907
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
129 words
Dense, solid, flexible, heat expandable, fire retardant composite material capable of subsisting substantially indefinitely in sheet or putty form and having increased thermal insulating and sealing efficiency when exposed to temperatures above about 110° C., and capable of expanding at least up to two times its original volume consisting essentially of about 15 to 80 weight percent of sodium silicate in granular form as the intumescent component, the individual sodium silicate granules each enlarging solely upon the application of heat, about 15 to 40 weight percent of a polychloroprene binder component, up to about 40 weight percent of a phenol-formaldehyde organic char-forming resin and up to about 50 weight percent filler comprising up to about 20 weight percent active filler and up to about 40 weight percent inactive filler.
Claim 2
Dependent Claim
129 words
Dense, solid, flexible, heat expandable, fire retardant composite material capable of subsisting substantially indefinitely in sheet or putty form and having increased thermal insulating and sealing efficiency when exposed to temperatures above about 110° C., and capable of expanding at least up to two times its original volume consisting essentially of about 15 to 80 weight percent of sodium silicate in granular form as the intumescent component, the individual sodium silicate granules each enlarging solely upon the application of heat, about 15 to 40 weight percent of a polychloroprene binder component, up to about 40 weight percent of a phenol-formaldehyde organic char-forming resin and up to about 50 weight percent filler comprising up to about 20 weight percent active filler and up to about 40 weight percent inactive filler.
Claim 3
Dependent Claim
46 words
Fire retardant composite material of claim 1 wherein said granular sodium silicate has particle sizes of from about 0.2 to about 2.0 mm., a moisture content of about 5 to about 30 percent and a SiO 2 to Na 2 O ratio of 2 to 3.75:1.
Claim 4
Dependent Claim
19 words
Fire retardant composite material of claim 2 having a Shore "A" durometer of from about 35 to about 95.
Claim 5
Dependent Claim
129 words
Dense, solid, flexible, heat expandable, fire retardant composite material capable of subsisting substantially indefinitely in sheet or putty form and having increased thermal insulating and sealing efficiency when exposed to temperatures above about 110° C., and capable of expanding to about ten times its original volume consisting essentially of about 52 weight percent of granular sodium silicate, 95 weight percent of the particles being greater than 0.2 mm., said particles each enlarging solely upon the application of heat, said sodium silicate having a moisture content of about 19 percent, about 23 weight percent of a polychloroprene rubber, about 6 weight percent of powdered phenol-formaldehyde resin, and about 19 weight percent of a filler comprising about 11 weight percent of active filler and about 8 weight percent of inactive filler.
Claim 6
Dependent Claim
129 words
Dense, solid, flexible, heat expandable, fire retardant composite material capable of subsisting substantially indefinitely in sheet or putty form and having increased thermal insulating and sealing efficiency when exposed to temperatures above about 110° C., and capable of expanding to about ten times its original volume consisting essentially of about 52 weight percent of granular sodium silicate, 95 weight percent of the particles being greater than 0.2 mm., said particles each enlarging solely upon the application of heat, said sodium silicate having a moisture content of about 19 percent, about 23 weight percent of a polychloroprene rubber, about 6 weight percent of powdered phenol-formaldehyde resin, and about 19 weight percent of a filler comprising about 11 weight percent of active filler and about 8 weight percent of inactive filler.
References Cited (Backward Citations)
US2650206A
Cited
US2664405A
Cited
US2880183A
Cited
US2947647A
Cited
US3786004A
Cited
US3766100A
Cited
US4057519A
Cited
US4129696A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-15 | 1984-12-15 | 1985-06-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-15 | 1988-12-15 | 1989-06-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-15 | 1992-12-15 | 1993-06-16 | $7700.00 | Window Closed / Lapsed |