Oxide cathode and process for production thereof
Assignee: Hitachi Ltd
•
Filing: 1978-12-13
•
Granted: 1981-06-16
•
Expires: 1998-12-13
Abstract
Abstract An oxide cathode wherein a base is made of an alloy comprising Ni as a main component and at least one reducing element selected from the group consisting of Mg, W, Zr, Si, Al and C, and the surface of the base is coated with an alkaline earth oxide layer containing at least BaO, the BaO content in the inner portion of the oxide layer contacting with the base being lower than that in the superficial portion of the oxide layer, if desired, forming a roughened layer made of powdered Ni or the like between the base and the inner portion of the oxide layer, can inhibit the formation of interface layer of, e.g. Ba 3 WO 6 and maintain stable thermion emitting characteristics for a long period of time.
Inventors
- 👤 Takao Kawamura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 13:43
CPC Classifications
H; H01; H01J; H01J1/00; H01J1/02; H01J1/13; H01J1/14; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12049; Y10T428/12056
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
111 words
In an oxide cathode wherein an oxide layer comprising oxides of alkaline earth metals including Ba is formed on the surface of a base made of an alloy comprising Ni as a main component and at least one reducing element selected from the group consisting of Mg, W, Zr, Si, C and Al, the improvement which comprises 0-40% by mole BaO content in the inner portion of the oxide layer contacting with the base and 40-80% by mole BaO content in the superficial portion of the oxide layer, wherein the content of BaO in said inner portion being 20-80% by mole less than the content of BaO in said superficial portion.
Claim 2
Dependent Claim
111 words
In an oxide cathode wherein an oxide layer comprising oxides of alkaline earth metals including Ba is formed on the surface of a base made of an alloy comprising Ni as a main component and at least one reducing element selected from the group consisting of Mg, W, Zr, Si, C and Al, the improvement which comprises 0-40% by mole BaO content in the inner portion of the oxide layer contacting with the base and 40-80% by mole BaO content in the superficial portion of the oxide layer, wherein the content of BaO in said inner portion being 20-80% by mole less than the content of BaO in said superficial portion.
Claim 3
Dependent Claim
56 words
An oxide cathode according to claim 1, wherein a roughened layer made of powdered Ni or metal powder containing Ni as a main component and at least one reducing element selected from the group consisting of Mg, Si, Al, C, W and Zr is formed between the base and the inner portion of the oxide layer.
Claim 4
Dependent Claim
27 words
An oxide cathode according to claim 1 or 2, wherein the BaO content in the inner portion of the oxide layer contacting with the base is zero.
Claim 5
Dependent Claim
137 words
In a process for producing an oxide cathode comprising coating one or more carbonates of alkaline earth metals including Ba on the surface of a base made of an alloy comprising Ni as a main component and at least one reducing element selected from the group consisting of Mg, W, Zr, Si, C and Al, and forming an oxide layer of the alkaline earth metals by pyrolysis of the alkaline earth carbonates, the improvement which comprises coating 0-40% by mole of BaCO 3 content in the inner portion of the carbonate layer contacting with the base and 20-80% by mole of BaCO 3 content in the superficial portion of the carbonate layer, wherein the content of BaCO 3 in the inner portion is 20-80% by mole less than the content of BaCO 3 in the superficial portion.
Claim 6
Dependent Claim
137 words
In a process for producing an oxide cathode comprising coating one or more carbonates of alkaline earth metals including Ba on the surface of a base made of an alloy comprising Ni as a main component and at least one reducing element selected from the group consisting of Mg, W, Zr, Si, C and Al, and forming an oxide layer of the alkaline earth metals by pyrolysis of the alkaline earth carbonates, the improvement which comprises coating 0-40% by mole of BaCO 3 content in the inner portion of the carbonate layer contacting with the base and 20-80% by mole of BaCO 3 content in the superficial portion of the carbonate layer, wherein the content of BaCO 3 in the inner portion is 20-80% by mole less than the content of BaCO 3 in the superficial portion.
Claim 7
Dependent Claim
60 words
A process for producing an oxide cathode according to claim 4, wherein a roughened layer made of powdered Ni or metal powder containing Ni as a main component and at least one reducing element selected from the group consisting of Mg, Si, Al, C, W and Zr is formed between the base and the inner portion of the carbonate layer.
Claim 8
Dependent Claim
32 words
A process for producing an oxide cathode according to claim 4 or 5, wherein a BaCO 3 content in the inner portion of the carbonate layer contacting with the base is zero.
Claim 9
Dependent Claim
52 words
A process for producing an oxide cathode according to claim 4 or 5, wherein a plurality of carbonate layers having gradually increasing amounts of BaCO 3 are coated on the base one after one, the BaCO 3 content in the inner portion of the carbonate layer contacting with the base being zero.
Claim 10
Dependent Claim
69 words
An oxide cathode comprising a base of a Ni alloy having at least one reducing element selected from the group consisting of Mg, W, Zr, Si, C and Al and an oxide coating on the base comprising an inner oxide layer and an outer oxide layer, the inner oxide layer having a BaO content that is 20-80% by mole less than the content of BaO in the outer layer.
Claim 11
Dependent Claim
69 words
An oxide cathode comprising a base of a Ni alloy having at least one reducing element selected from the group consisting of Mg, W, Zr, Si, C and Al and an oxide coating on the base comprising an inner oxide layer and an outer oxide layer, the inner oxide layer having a BaO content that is 20-80% by mole less than the content of BaO in the outer layer.
Claim 12
Dependent Claim
22 words
An oxide cathode according to claim 8, wherein the BaO content in the inner oxide layer adjacent to the base is zero.
Claim 13
Dependent Claim
111 words
A process for producing an oxide cathode comprising coating a base of a Ni alloy having at least one reducing element selected from the group consisting of Mg, W, Zr, Si, C and Al, with at least two alkaline earth metal carbonate layers having different BaCO 3 contents, the layer with the lowest BaCO 3 content being applied on the base first and then being covered with a layer of a higher BaCO 3 content, the layer with the lowest BaCO 3 content having 20-80% by mole less BaCO 3 content than the layer with higher BaCO 3 content, and pyrolyzing the alkaline earth metal carbonate layers to form oxide layers.
Claim 14
Dependent Claim
111 words
A process for producing an oxide cathode comprising coating a base of a Ni alloy having at least one reducing element selected from the group consisting of Mg, W, Zr, Si, C and Al, with at least two alkaline earth metal carbonate layers having different BaCO 3 contents, the layer with the lowest BaCO 3 content being applied on the base first and then being covered with a layer of a higher BaCO 3 content, the layer with the lowest BaCO 3 content having 20-80% by mole less BaCO 3 content than the layer with higher BaCO 3 content, and pyrolyzing the alkaline earth metal carbonate layers to form oxide layers.
Claim 15
Dependent Claim
40 words
A process for producing an oxide cathode according to claim 10, wherein the first alkaline earth metal carbonate layer coated on the base is a composite salt comprising 50% by mole SrCO 3 and 50% by mole CaCO 3 .
Claim 16
Dependent Claim
46 words
A process for producing an oxide cathode according to claim 11, wherein the last alkaline earth metal carbonate layer coated on the base is a composite salt comprising 47% by mole BaCO 3 , 43% by mole SrCO 3 and 10% by mole CaCO 3 .
Claim 17
Dependent Claim
36 words
A process for producing an oxide cathode according to claim 11, wherein the BaCO 3 content in the first layer is 20 to 80% by mole less than the BaCO 3 content in the last layer.
References Cited (Backward Citations)
US2716716A
Cited
US2848644A
Cited
US3170772A
Cited
US3842309A
Cited
US3719856A
Cited
US3879830A
Cited
US4083811A
Cited
US4147954A
Cited
US4101800A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-15 | 1984-12-15 | 1985-06-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-15 | 1988-12-15 | 1989-06-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-15 | 1992-12-15 | 1993-06-16 | $7700.00 | Window Closed / Lapsed |