Patent US4272490A successfully refreshed from Google Patents.
US4272490A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Hydrometallurgical process for the treatment of ores
Assignee: 698638 Alberta Ltd
•
Filing: 1978-06-28
•
Granted: 1981-06-09
•
Expires: 1998-06-28
Abstract
Abstract A process for the recovery of uranium values from uranium-bearing material by sulphuric acid leaching when the material also contains siliceous matter which is at least partly soluble in sulphuric acid. The process comprises leaching the material with sulphuric acid in an aqueous slurry under oxidizing conditions at a temperature within the range of from about 65° C. to about 200° C. and at elevated pressure, with sulphuric acid being present in a quantity only slightly in excess of the amount required to dissolve the uranium and any other element whose dissolution is desired, to produce an insoluble residue containing siliceous matter and a leach solution containing dissolved values of uranium and any other desired element.
Inventors
- 👤 Verner B. Sefton
- 👤 Ian M. Masters
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 20:14
CPC Classifications
C; C22; C22B; C22B60/00; C22B60/02; C22B60/0204; C22B60/0217; C22B60/0221; C22B60/0226; C22B60/0234; C22B23/00; C22B23/04; C22B23/0407; C22B23/0415; C22B23/043; C22B23/0453; C22B23/0461; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
121 words
A process for the recovery of uranium values from uranium-bearing material by sulphuric acid leaching when the material also contains siliceous matter which is at least partly soluble in sulphuric acid, iron and arsenic, said process comprising leaching said material with sulphuric acid in an aqueous slurry under oxidizing conditions at a temperature within the range of from about 65° C. to about 200° C. and at elevated pressure, said sulphuric acid being present in a quantity slightly in excess of the amount required to dissolve the uranium and any other element whose dissolution is desired to produce an insoluble residue containing siliceous matter and ferric arsenate, and a leach solution containing dissolved values by uranium and said any other element.
Claim 2
Dependent Claim
121 words
A process for the recovery of uranium values from uranium-bearing material by sulphuric acid leaching when the material also contains siliceous matter which is at least partly soluble in sulphuric acid, iron and arsenic, said process comprising leaching said material with sulphuric acid in an aqueous slurry under oxidizing conditions at a temperature within the range of from about 65° C. to about 200° C. and at elevated pressure, said sulphuric acid being present in a quantity slightly in excess of the amount required to dissolve the uranium and any other element whose dissolution is desired to produce an insoluble residue containing siliceous matter and ferric arsenate, and a leach solution containing dissolved values by uranium and said any other element.
Claim 3
Dependent Claim
26 words
A process according to claim 1 wherein the material is leached at a temperature in the range of from about 125° C. to about 200° C.
Claim 4
Dependent Claim
46 words
A process according to claim 1 wherein the material also contains nickel, and the leach solution also contains dissolved nickel values, with said sulphuric acid being present during leaching in a quantity slightly in excess of the amount required to dissolve the uranium and the nickel.
Claim 5
Dependent Claim
30 words
A process according to claim 1 wherein said oxidizing conditions are provided by oxygen at a partial pressure in the range of from about 20 psi to about 200 psi.
Claim 6
Dependent Claim
40 words
A process according to claim 1 wherein, during leaching, the aqueous slurry is agitated at a minimum amount consistent with the maintenance of adequate oxidizing conditions throughout the slurry and the maintenance of adequate suspension of solids in the slurry.
Claim 7
Dependent Claim
34 words
A process according to claim 1 wherein cations selected from the group consisting of sodium, potassium and ammonium are present during the leach to cause the formation of an insoluble jarosite compound with iron.
Claim 8
Dependent Claim
33 words
A process according to claim 8 wherein sodium ions are added as sodium sulphate to provide a concentration in the range of from about 0.2 to about 0.4 moles per mole of iron.
Claim 9
Dependent Claim
41 words
A process according to claim 1 wherein the material also contains aluminum, and cations selected from the group consisting of sodium, potassium and ammonium are present during the leach to cause the formation of an insoluble alunite compound with the aluminum.
Claim 10
Dependent Claim
33 words
A process according to claim 6 wherein sodium ions are added as sodium sulphate to provide a concentration in the range of from about 0.2 to about 0.4 moles per mole of aluminum.
Claim 11
Dependent Claim
48 words
A process according to claim 3 wherein uranium values are removed from the dissolved uranium and nickel containing leach solution, and the remaining nickel containing solution is treated with ferric ions to remove arsenic in said solution as ferric arsenate before recovery of nickel values from said solution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-08 | 1984-12-08 | 1985-06-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-08 | 1988-12-08 | 1989-06-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-08 | 1992-12-08 | 1993-06-09 | $7700.00 | Window Closed / Lapsed |