Antilumping expandable styrene polymers
Assignee: Lyondell Chemical Technology LP
•
Filing: 1980-06-30
•
Granted: 1981-05-26
•
Expires: 2000-06-30
Abstract
Abstract Expandable styrene polymer particles are surface-coated with conjugated diene elastomers to prevent the particles from lumping together during expansion. The coating is applied by adding 0.05-0.25 part of conjugated diene elastomer to an aqueous suspension containing 100 parts of polymer particles during the impregnation of the mixture with a blowing agent.
Inventors
- 👤 Elizabeth A. Blommers
- 👤 William J. Poole
- 👤 Alvin R. Ingram
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 10:50
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/22; C08J9/224; C08J9/16; C08J9/18; C08J2325/00
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
109 words
In a process for making expandable styrene polymer particles by suspending styrene polymer particles in water containing a suspending agent, heating the suspension to a temperature between 60° and 150° C., and thereafter impregnating said particles with a blowing agent, the improvement comprising dissolving 0.04 to 0.25 weight percent based on the polymer particles of a conjugated diene elastomer in a portion or all of the blowing agent, adding the solution of elastomer and the remaining blowing agent, it any, to the suspended polymer particles to impregnate the particles with blowing agent and coat the particles with elastomer, whereby the final particles have reduced lumping during pre-expansion with heat.
Claim 2
Dependent Claim
109 words
In a process for making expandable styrene polymer particles by suspending styrene polymer particles in water containing a suspending agent, heating the suspension to a temperature between 60° and 150° C., and thereafter impregnating said particles with a blowing agent, the improvement comprising dissolving 0.04 to 0.25 weight percent based on the polymer particles of a conjugated diene elastomer in a portion or all of the blowing agent, adding the solution of elastomer and the remaining blowing agent, it any, to the suspended polymer particles to impregnate the particles with blowing agent and coat the particles with elastomer, whereby the final particles have reduced lumping during pre-expansion with heat.
Claim 3
Dependent Claim
22 words
The process of claim 1 wherein said conjugated diene elastomer is selected from homopolymers of conjugated dienes and diene block copolymer rubbers.
Claim 4
Dependent Claim
85 words
The process of claim 2 wherein said conjugated diene block copolymer rubber is selected from the group consisting of graded block, A-B diblock, radial or star block, A-B-A triblock and A-B-A hydrogenated triblock rubbers, wherein A represents essentially polymerized vinyl aromatic monomer with a minor amount of conjugated diene, B represents essentially conjugated diene polymer with a minor amount of vinyl aromatic monomer, and the rubbers contain from 2 to 50% by weight vinyl aromatic monomer and 50 to 98% by weight of conjugated diene.
Claim 5
Dependent Claim
29 words
The process of claims 1, 2 or 3 wherein the diene in the conjugated diene elastomer is selected from the group consisting of butadiene, isoprene, chloroprene, 2,3-dimethylbutadiene and piperylene.
References Cited (Backward Citations)
US2862834A
Cited
US2857339A
Cited
US2857340A
Cited
US3060138A
Cited
US3277026A
Cited
US3819546A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-25 | 1984-11-24 | 1985-05-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-25 | 1988-11-24 | 1989-05-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-25 | 1992-11-24 | 1993-05-26 | $7700.00 | Window Closed / Lapsed |