US4269742A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Epoxy resin hardening agents from Mannich bases and method for curing
Assignee: Lanxess Organometallics GmbH
•
Filing: 1979-12-03
•
Granted: 1981-05-26
•
Expires: 1999-12-03
Abstract
Abstract Amine compounds, adaptable to use as a hardener for epoxy compounds, prepared by the reaction, with amine exchange and liberation of secondary amine, of a Mannich base and a member selected from the group consisting of aminoamides, aminoimidazolines, aminoamides containing an imidazoline group, and polyamines, said Mannich base being prepared by reacting formaldehyde, a monophenol or polyphenol, and a secondary amine are disclosed, as are a method of making epoxy polyadducts (i.e. cured epoxy resins) by the reaction of said amine hardener compounds with an epoxy compound and the epoxy polyadducts (i.e. cured epoxy resins) so prepared.
Inventors
- 👤 Ulrich Goeke
- 👤 Michael Richter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:29
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/62; C08G59/621; C08G59/623; C08L; C08L63/00
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
126 words
The method of curing an epoxy resin to form a crosslinked duroplast product, which method comprises reacting an epoxy compound having an average of more than one epoxy group per molecule with a liquid amine compound having an average of more than two active amine hydrogen atoms per molecule, which liquid amine compound is prepared by the reaction, with amine exchange and liberation of secondary amine, of a Mannich base and an amount of a member selected from the group consisting of aminoamides, aminoimidazolines, aminoamides containing an imidazoline group, and polyamines such that the amine compound reaction product has an average of more than two active hydrogen atoms per molecule, said Mannich base being prepared by reacting formaldehyde, a monophenol or polyphenol, and a secondary amine.
Claim 2
Independent Claim
126 words
The method of curing an epoxy resin to form a crosslinked duroplast product, which method comprises reacting an epoxy compound having an average of more than one epoxy group per molecule with a liquid amine compound having an average of more than two active amine hydrogen atoms per molecule, which liquid amine compound is prepared by the reaction, with amine exchange and liberation of secondary amine, of a Mannich base and an amount of a member selected from the group consisting of aminoamides, aminoimidazolines, aminoamides containing an imidazoline group, and polyamines such that the amine compound reaction product has an average of more than two active hydrogen atoms per molecule, said Mannich base being prepared by reacting formaldehyde, a monophenol or polyphenol, and a secondary amine.
Claim 3
Dependent Claim
27 words
A method as in claim 1 wherein said epoxy compound and said liquid amine compound are reacted at a temperature between room temperature and about 5° C.
Claim 4
Dependent Claim
201 words
A method as in claim 1 wherein said aminoamides, aminoimidazolines, and aminoamides containing an imidazoline group are prepared by condensing an acid component comprising an acid selected from the group consisting of (a1) monocarboxylic acids having 2 to 22 carbon atoms; (a2) the polymerization products of unsaturated higher fatty acids having 16 to 22 carbon atoms; (a3) copolymers of unsaturated fatty acids having 16 to 22 carbon atoms with aromatic vinyl compounds, (a4) adducts of unsaturated fatty acids with unsaturated lower monocarboxylic and dicarboxylic acids; (a5) acids prepared by reacting unsaturated fatty acids with CO and water; (a6) epoxidized unsaturated higher fatty acids; (a7) aliphatic, hydroaromatic, araliphatic and aromatic dicarboxylic and polycarboxylic acids having 6 to 36 carbon atoms; (a8) acids which are prepared by the addition of phenols to unsaturated monocarboxylic or dicarboxylic acids; and (a9) amino acids or lactams, with an amine component comprising a polyamine selected from the group consisting of (aa1) polyethylene polyamines; (aa2) polypropylene polyamines; (aa3) aliphatic polyamines; (aa4) cycloaliphatic polyamines; (aa5) heterocyclic polyamines; and (aa6) polyether amines, said acid component and amine component being reacted in such amounts that the ratio of amino groups to carboxyl groups in the reaction mixture is greater than one.
Claim 5
Dependent Claim
27 words
A method as in claim 3 wherein said epoxy compound and said liquid amine compound are reacted at a temperature between room temperature and about 5° C.
Claim 6
Dependent Claim
48 words
A method as in claim 1 wherein said polyamines are selected from the group consisting of (a10) polyethylene polyamines; (a11) polypropylene polyamines and polyamines obtained by the cyanethylation of polyamines followed by hydrogenation; (a12) aliphatic polyamines; (a13) cycloaliphatic polyamines; (a14) heterocyclic polyamines; (a15) polyetheramines; and (a16) aromatic amines.
Claim 7
Dependent Claim
27 words
A method as in claim 5 wherein said epoxy compound and said liquid amine compound are reacted at a temperature between room temperature and about 5° C.
Claim 8
Dependent Claim
18 words
A method as in claim 1 wherein said liquid amine compound contains at least one tertiary amino group.
Claim 9
Dependent Claim
27 words
A method as in claim 7 wherein said epoxy compound and said liquid amine compound are reacted at a temperature between room temperature and about 5° C.
Claim 10
Dependent Claim
24 words
A method as in claim 1 wherein said Mannich base is prepared from a phenol selected from the group consisting of phenol and 4,4'-dihydroxydiphenylpropane-2,2.
Claim 11
Dependent Claim
27 words
A method as in claim 9 wherein said epoxy compound and said liquid amine compound are reacted at a temperature between room temperature and about 5° C.
Claim 12
Dependent Claim
27 words
A method as in claim 1 wherein said epoxy compound and said liquid amine compound are reacted together with a conventional amine hardening agent for epoxy compounds.
Claim 13
Dependent Claim
11 words
A cured epoxy resin prepared by the method of claim 1.
Claim 14
Dependent Claim
11 words
A cured epoxy resin prepared by the method of claim 3.
Claim 15
Dependent Claim
11 words
A cured epoxy resin prepared by the method of claim 5.
Claim 16
Dependent Claim
11 words
A cured epoxy resin prepared by the method of claim 7.
Claim 17
Dependent Claim
11 words
A cured epoxy resin prepared by the method of claim 9.
Claim 18
Dependent Claim
11 words
A cured epoxy resin prepared by the method of claim 11.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-25 | 1984-11-24 | 1985-05-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-25 | 1988-11-24 | 1989-05-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-25 | 1992-11-24 | 1993-05-26 | $7700.00 | Window Closed / Lapsed |