Abstract A method for producing stable urea-formaldehyde polymers which have reduced aldehyde vapor emissions during their production and use is disclosed, such urea-formaldehyde polymers particularly useful in the production of urea-formaldehyde insulating foam and as adhesives in the production of plywood and particleboard. An alkali or alkaline earth metal borohydride is added to the urea-formaldehyde resin solution prior to or during cure thereof. The boroydride reacts with free formaldehyde in the resin solution or any free formaldehyde subsequently generated in the resin due to hydrolytic break down. The amount of borohydride added the resin solution should be sufficient to reduce the emission of free formaldehyde therefrom.
A method of producing a cellular foam having reduced aldehyde vapor emission during use thereof, comprising: dispensing a foaming gas into an aqueous resin solution of a condensation product of urea and formaldehyde, the aqueous resin containing an aqueous surfactant foaming agent, an acid curing catalyst and a sufficient amount of an alkali or alkaline earth metal borohydride to reduce any free formaldehyde emitted from the foam.
Claim 2
Independent Claim
67 words
A method of producing a cellular foam having reduced aldehyde vapor emission during use thereof, comprising: dispensing a foaming gas into an aqueous resin solution of a condensation product of urea and formaldehyde, the aqueous resin containing an aqueous surfactant foaming agent, an acid curing catalyst and a sufficient amount of an alkali or alkaline earth metal borohydride to reduce any free formaldehyde emitted from the foam.
Claim 3
Dependent Claim
18 words
The method of claim 1, wherein the molar ratio of urea to formaldehyde ranges from 1.0:1 to 2.0:1.