Urea formaldehyde foam
Assignee: Borden Products Ltd
•
Filing: 1974-05-28
•
Granted: 1976-09-07
•
Expires: 1994-05-28
Abstract
Abstract A foaming system includes a foaming agent solution and a resin solution. In a preferred embodiment, the foaming agent solution includes from 1.6 to 4.8 mmols of dibutyl naphthalene sulfonic acid as surfactant, from 5 to 20 mmols of phosphoric acid as catalyst and foam intumescent agent, from 0 to 45.5 mmols of resorcinol as foam anti-collapsing agent, from 9.1 to 54.6 mmols of chloral hydrate as fire retardant agent and sufficient water to make a solution of about 5% solids concentration. The resin solution includes urea formaldehyde resin produced by reacting from 1.0 to 2.4 mols of formaldehyde per mol of urea, from 6.5 to 500 mmols polyethylene glycol as foam charring component, from 0.3 to 1.2 mmols of calcium chloride as foam uniform cell size component, from 3 - 310 mmols of dicyandiamide as foam hydrolysis resistance component, from 2 - 30 mmols of sodium bromide as foam aging component, from 0 - 150 mmols of furfuryl alcohol as formaldehyde odor masking component and sufficient water to prepare a solution of 40 to 45% solids concentration. One part by weight of the foaming agent solution is frothed and then from 0.9 to 1.5 parts by weight of the resin solution is sprayed on the froth to obtain foam.
Inventors
- 👤 Marcel Widmann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 12:51
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/30; C08J9/0004; C08K; C08K5/00; C08K5/04; C08K5/05; C08K5/16; C08J2361/00; C08J2361/20; C08J2361/22; C08J2361/24; Y; Y10; Y10S; Y10S260/00; Y10S260/24; Y10S521/00; Y10S521/907
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
150 words
An aqueous resin solution for making foam which is flame-retardant, intumescent and has thermal and sound insulating properties comprising a condensation product of urea and formaldehyde in the ratio of 1.0 to 2.4 mols of formaldehyde per mol of urea; from 6.5 to 500 mmols of a foam charring component selected from ethylene glycol and polyalkylene glycols having from 2 to 8 carbon atoms in the alkylene moiety and a molecular weight of up to 200, glycerine, pentaerythrytol, sugars, propylene glycol and mixtures thereof; from 0.3 to 1.2 mmols of a component to provide uniform cell size in the foam selected from alkaline earth metal ions in the form of water-soluble salts; from 3 to 310 mmols of a foam hydrolysis resistance component selected from dicyandiamide, guanylurea, calcium cyanamide, guanidine derivatives and hexamethylenetetramine; and from 2 to 30 mmols of a foam aging component selected from water-soluble alkali metal halogens.
Claim 2
Dependent Claim
150 words
An aqueous resin solution for making foam which is flame-retardant, intumescent and has thermal and sound insulating properties comprising a condensation product of urea and formaldehyde in the ratio of 1.0 to 2.4 mols of formaldehyde per mol of urea; from 6.5 to 500 mmols of a foam charring component selected from ethylene glycol and polyalkylene glycols having from 2 to 8 carbon atoms in the alkylene moiety and a molecular weight of up to 200, glycerine, pentaerythrytol, sugars, propylene glycol and mixtures thereof; from 0.3 to 1.2 mmols of a component to provide uniform cell size in the foam selected from alkaline earth metal ions in the form of water-soluble salts; from 3 to 310 mmols of a foam hydrolysis resistance component selected from dicyandiamide, guanylurea, calcium cyanamide, guanidine derivatives and hexamethylenetetramine; and from 2 to 30 mmols of a foam aging component selected from water-soluble alkali metal halogens.
Claim 3
Dependent Claim
42 words
The resin solution of claim 1 wherein amount of said charring component is from 20 to 250 mmols, that of uniform cell size component is from 0.48 to 0.78 mmols, and that of hydrolysis resistance component is from 7 to 31 mmols.
Claim 4
Dependent Claim
61 words
The resin solution of claim 2 wherein said charring component is selected from polyethylene glycols; said aging component is sodium bromide; said hydrolysis resistance component is dicyandiamide; and said uniform cell size component is calcium chloride; said solution also includes up to 150 mmols of formaldehyde odor masking component selected from furfuryl alcohol, furfural, phenols, essential oils, triethylamine and mixtures thereof.
Claim 5
Dependent Claim
28 words
The resin solution of claim 3 having solids concentration of 30 to 60% wherein the formaldehyde odor masking agent is selected from furfuryl alcohol, furfural and mixtures thereof.
Claim 6
Dependent Claim
162 words
A flame-retardant, intumescent foam which has thermal and sound insulating properties prepared from a mixture of (a) an aqueous urea-formaldehyde resin solution and (b) an aqueous foaming agent solution containing an acid curing agent, the resin solution comprising a condensation product of urea and formaldehyde in the ratio of 1.0 to 2.4 mols of formaldehyde per mol of urea; from 6.5 to 500 mmols of a foam charring agent selected from ethylene glycol and polyalkylene glycols containing from 2 to 8 carbon atoms in the alkylene moiety and having a molecular weight up to 200, glycerine, pentaerythrytol, sugars and mixtures thereof; from 0.3 to 1.2 mmols of a component to provide uniform cell size in the foam selected from water-soluble alkaline earth metal salts; from 3 to 310 mmols of a foam hydrolysis resistance component selected from dicyandiamide, guanylurea, calcium cyanamide, guanidine derivatives, hexamethylene tetramine; and from 2 to 30 mmols of a foam aging component selected from water-soluble alkali metal halogens.
Claim 7
Dependent Claim
162 words
A flame-retardant, intumescent foam which has thermal and sound insulating properties prepared from a mixture of (a) an aqueous urea-formaldehyde resin solution and (b) an aqueous foaming agent solution containing an acid curing agent, the resin solution comprising a condensation product of urea and formaldehyde in the ratio of 1.0 to 2.4 mols of formaldehyde per mol of urea; from 6.5 to 500 mmols of a foam charring agent selected from ethylene glycol and polyalkylene glycols containing from 2 to 8 carbon atoms in the alkylene moiety and having a molecular weight up to 200, glycerine, pentaerythrytol, sugars and mixtures thereof; from 0.3 to 1.2 mmols of a component to provide uniform cell size in the foam selected from water-soluble alkaline earth metal salts; from 3 to 310 mmols of a foam hydrolysis resistance component selected from dicyandiamide, guanylurea, calcium cyanamide, guanidine derivatives, hexamethylene tetramine; and from 2 to 30 mmols of a foam aging component selected from water-soluble alkali metal halogens.
Claim 8
Dependent Claim
40 words
Foam of claim 5 wherein amount of said charring component is from 20 to 250 mmols, that of uniform cell size component is from 0.48 to 0.78 mmols, and that of hydrolysis resistance component is from 7 to 31 mmols.
Claim 9
Dependent Claim
59 words
Foam of claim 6 wherein said charring component is selected from polyethylene glycols; said aging component is sodium bromide; said hydrolysis resistance component is dicyandiamide; and said uniform cell size component is calcium chloride; said solution also includes up to 150 mmols of formaldehyde odor masking component selected from furfuryl alcohol, furfural, phenols, essential oils, triethylamine and mixtures thereof.
Claim 10
Dependent Claim
31 words
Foam of claim 7 wherein said resin solution has solids concentration of 30 to 60% and wherein the formaldehyde odor masking agent is selected from furfuryl alcohol, furfural and mixtures thereof.
Claim 11
Dependent Claim
96 words
Foam of claim 5 wherein said foaming agent solution comprises from 1.6 to 4.8 mmols of a surfactant selected from alkyl and aryl free sulfonic acids having from 9 to 20 carbon atoms per molecule; from 5 to 20 mmols of an intumescent agent selected from phosphoric and sulfuric acids; and from 9.1 to 54.6 mmols of a fire retardant agent selected from chloral, chloral hydrate, dibromobutene diol, dibromopropanols, derivatives obtained by reacting chloral with ammonia, alkanols, alkylene glycols, acetone, phenols or other compounds having at least one active hydrogen, and mixtures of said fire retardants.
Claim 12
Dependent Claim
32 words
Foam of claim 9 wherein said surfactant is dibutyl naphthalene sulfonic acid, said fire retardant agent is chloral hydrate and said foaming agent solution has a solids concentration of 2 to 17%.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-07 | 1980-03-08 | 1980-09-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-07 | 1984-03-08 | 1984-09-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-07 | 1988-03-08 | 1988-09-07 | $7700.00 | Window Closed / Lapsed |