Method of preparing steel-backed antifriction alloy, composite strips and products therefrom
Assignee: Metal Leve SA Industria e Commercio
•
Filing: 1979-09-11
•
Granted: 1981-05-12
•
Expires: 1999-09-11
Abstract
Abstract A method of improving steel-backed antifriction alloy; composite strips and products therefrom, wherein the antifriction alloys previously deposited on the steel backing strip are subjected throughout the strip length to a spot-by-spot fusion operation performed by a highly-concentrated energy beam (electron or other), the intensity and displacement rate of said beam being adjusted in respect of the composite strip in such a manner as to afford a spot-by-spot fusion of the anti-friction alloys to a depth equal to the anti-friction layer thickness; and a method wherein concentration of said energy beam is adjusted so as to enable the mass surrounding any given melting spot to cause an abrupt cooling of said spot when the energy beam is moved to an adjoining spot.
Inventors
- 👤 Duraid Mahrus
- 👤 Antonio C. Paulos
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 08:48
CPC Classifications
C; C23; C23C; C23C24/00; C23C24/08; C23C24/10; C22; C22F; C22F3/00; F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/06; F16C33/14; F16C2223/00; F16C2223/30; F16C2223/44; Y; Y10; Y10S; Y10S148/00; Y10S148/902; Y10S148/903; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12701
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
241 words
A method for preparing an anti-friction bearing material composite comprising a steel backing-strip supporting at the interface therewith, on at least one side of said strip, an anti-friction alloy coating, said alloy of said coating consisting essentially of a higher-melting, hard-metal matrix phase having homogenously distributed therethrough a lower melting soft-metal inclusion phase, which comprises coating said steel strip with a metal mixture comprising said hard metal admixed with said soft metal, locally fusing said coated mixture from its outer surface to its interface with said steel backing strip by local impingement of a concentrated high-energy beam on said coating to form a uniform molten pool area of said higher melting and lower melting alloy at the area of impingement of said beam, and abruptly cooling and solidifying said molten pool by moving said beam-impinging area from said fused area to an adjacent locale and by conducting the fusion energy from said fused area by conduction into cooler portions of said coated strip to form in said cooled area a homogeneous solid dispersion of said soft-metal inclusion phase in said hard-metal matrix phase, and fusing and cooling successive areas of said coating by traversing locales of said coated strip until the entire area of said coated strip has been successively fused and solidified to provide the bearing material composite comprising the alloycoated steel strip wherein said alloy consists of substantially said soft-metal inclusion phase homogenously dispersed in said hard-metal matrix phase.
Claim 2
Independent Claim
241 words
A method for preparing an anti-friction bearing material composite comprising a steel backing-strip supporting at the interface therewith, on at least one side of said strip, an anti-friction alloy coating, said alloy of said coating consisting essentially of a higher-melting, hard-metal matrix phase having homogenously distributed therethrough a lower melting soft-metal inclusion phase, which comprises coating said steel strip with a metal mixture comprising said hard metal admixed with said soft metal, locally fusing said coated mixture from its outer surface to its interface with said steel backing strip by local impingement of a concentrated high-energy beam on said coating to form a uniform molten pool area of said higher melting and lower melting alloy at the area of impingement of said beam, and abruptly cooling and solidifying said molten pool by moving said beam-impinging area from said fused area to an adjacent locale and by conducting the fusion energy from said fused area by conduction into cooler portions of said coated strip to form in said cooled area a homogeneous solid dispersion of said soft-metal inclusion phase in said hard-metal matrix phase, and fusing and cooling successive areas of said coating by traversing locales of said coated strip until the entire area of said coated strip has been successively fused and solidified to provide the bearing material composite comprising the alloycoated steel strip wherein said alloy consists of substantially said soft-metal inclusion phase homogenously dispersed in said hard-metal matrix phase.
Claim 3
Dependent Claim
20 words
The method as defined in claim 1 wherein the fusion of the coated alloys is performed under an oxide-protective atmosphere.
Claim 4
Dependent Claim
26 words
The method as defined in claim 1, wherein solidification of fused areas is accelerated by means of an additional cooling provided by gas or water blasts.
Claim 5
Dependent Claim
13 words
The anti-friction bearing material composite prepared according to the method of claim 1.
Claim 6
Dependent Claim
16 words
The method as defined in claim 1 wherein said high energy beam is an electron beam.
Claim 7
Dependent Claim
30 words
The method as defined in claim 5, wherein displacement of the electron beam is obtained by moving the coated strip lengthwise simultaneously with a crosswise reciprocating motion of the beam.
Claim 8
Dependent Claim
48 words
The method as defined in claim 5, wherein the structure of the alloy coating is provided with a fine diffusion of the softer phase or phases by means of successive local area fusions carried out by an electron beam throughout the length and thickness of said antifriction alloy.
Claim 9
Independent Claim
136 words
The method for preparing anti-friction bearings and washers from steel-backed anti-friction bearing material composites which comprises coating of said steel strip with a metal mixture comprising a higher melting hard-metal admixed with a lower melting soft-metal, subjecting said coating on said steel strip to successive area-by area fusion through its thickness to its interface with the strip by a highly concentrated energy beam until the entire area of said strip has been fused, cooling each area of fusion to solidification by the abrupt removal of said energy beam and the conduction of the heat of fusion from said area to form an anti-friction alloy coating on said strip, said alloy consisting essentially of said soft-metal homogenously dispersed as an inclusion phase in a hard-metal matrix, and fashioning bearings and washers from said anti-friction alloy-coated steel strip.
Claim 10
Independent Claim
136 words
The method for preparing anti-friction bearings and washers from steel-backed anti-friction bearing material composites which comprises coating of said steel strip with a metal mixture comprising a higher melting hard-metal admixed with a lower melting soft-metal, subjecting said coating on said steel strip to successive area-by area fusion through its thickness to its interface with the strip by a highly concentrated energy beam until the entire area of said strip has been fused, cooling each area of fusion to solidification by the abrupt removal of said energy beam and the conduction of the heat of fusion from said area to form an anti-friction alloy coating on said strip, said alloy consisting essentially of said soft-metal homogenously dispersed as an inclusion phase in a hard-metal matrix, and fashioning bearings and washers from said anti-friction alloy-coated steel strip.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-11 | 1984-11-10 | 1985-05-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-11 | 1988-11-10 | 1989-05-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-11 | 1992-11-10 | 1993-05-12 | $7700.00 | Window Closed / Lapsed |