Process for production of monofilaments from polyvinylidene fluoride
Assignee: Dynamit Nobel AG
•
Filing: 1979-08-24
•
Granted: 1981-04-28
•
Expires: 1999-08-24
Abstract
Abstract A process for the production of monofilaments of polyvinylidene fluoride is disclosed wherein polyvinylidene fluoride is plasticized in an extruder and fed to an extrusion die and passed through an extrusion nozzle orifice to enter a liquid cooling medium having a thermal conductivity of under 0.4 W/m °K., a viscosity at 100° C. of over 0.5 cp and a density at 100° C. of over 1.1 g/cm 3 . Extusion is performed by passing the plasticized polyvinylidene fluoride over separate extrusion zones such as by passing the polyvinylidene fluoride over a first extrusion zone maintained at a first extrusion temperature and thereafter passing the polyvinylidene fluoride through a second extrusion zone maintained at a temperature of 10 to 30 percent higher than the preceeding extrusion zone. An apparatus for carrying out the process is also described.
Inventors
- 👤 Egon Lang
- 👤 Wilhelm Nachtigall
- 👤 Joachim Stark
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 14:30
CPC Classifications
D; D01; D01F; D01F6/00; D01F6/02; D01F6/08; D01F6/12; D01D; D01D4/00; D01D4/02; D01D5/00; D01D5/08; D01D5/088; D01D5/0885
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
111 words
A process for the production of a monofilament of polyvinylidene fluoride which comprises: A. extruding polyvinylidene fluoride through a die over a first path and a first extrusion temperature and thereafter over a subsequent path at a temperature of 10 to 30 degrees C. higher than the temperature of said first path and B. then passing the so extruded polyvinylidene fluoride through a cooling bath maintained at a temperature of 60° to 140° C., said cooling bath containing a cooling medium having a thermal conductivity of under 0.40 W/m °K, a viscosity at 100° C. of over 0.5 cp and a density at 100° C. of over 1.1 g/cm 3 .
Claim 2
Dependent Claim
111 words
A process for the production of a monofilament of polyvinylidene fluoride which comprises: A. extruding polyvinylidene fluoride through a die over a first path and a first extrusion temperature and thereafter over a subsequent path at a temperature of 10 to 30 degrees C. higher than the temperature of said first path and B. then passing the so extruded polyvinylidene fluoride through a cooling bath maintained at a temperature of 60° to 140° C., said cooling bath containing a cooling medium having a thermal conductivity of under 0.40 W/m °K, a viscosity at 100° C. of over 0.5 cp and a density at 100° C. of over 1.1 g/cm 3 .
Claim 3
Dependent Claim
26 words
A process according to claim 1 wherein the so extruded monofilament is immersed in a cooling medium to a depth ranging from 200 to 2000 mm.
Claim 4
Dependent Claim
25 words
A process according to claim 2 wherein the so extruded monofilament is immersed in the cooling medium to a depth from 500 to 1000 mm.
Claim 5
Dependent Claim
12 words
A process according to claim 1 wherein the cooling medium comprises glycerin.
Claim 6
Dependent Claim
20 words
A process according to claim 1 wherein the cooling medium is maintained at a temperature of 90° to 110° C.
Claim 7
Dependent Claim
19 words
A process according to claim 1 wherein the cooling medium has a thermal conductivity of under 0.3 W/m °K.
Claim 8
Dependent Claim
20 words
A process according to claim 6 wherein the cooling medium has a viscosity at 100° C. of over 1.4 cp.
Claim 9
Dependent Claim
21 words
A process according to claim 7 wherein the cooling medium has a density of over 1.2 g/cm 3 at 100° C.
Claim 10
Dependent Claim
22 words
A process according to claim 1 wherein the monofilaments are treated, after cooling in the cooling medium to remove cooling medium therefrom.
Claim 11
Dependent Claim
28 words
A process according to claim 1 wherein the monofilament traverses an air space of 10 to 250 milimeters following extrusion and prior to entry into the cooling medium.
Claim 12
Dependent Claim
22 words
A process according to claim 10 wherein the air space which is traversed by the monofilament is 50 to 100 mm long.
Claim 13
Dependent Claim
20 words
A process according to claim 1, wherein the monofilament extruded and cooled has a diameter of 0.2 to 1.1 mm.
Claim 14
Dependent Claim
13 words
A process according to claim 1, wherein the polyvinylidene fluoride is melt spun.
Claim 15
Dependent Claim
27 words
A process according to claim 1, wherein the polyvinylidene chloride is melt spun into a cooling medium comprising 1,2-ethandiol or mixtures with water and glycol or glycerin.
Claim 16
Dependent Claim
25 words
A process according to claim 1, wherein the temperature of the subsequent path is 15° to 25° C. higher than that of the first path.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-27 | 1984-10-27 | 1985-04-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-27 | 1988-10-27 | 1989-04-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-27 | 1992-10-27 | 1993-04-28 | $7700.00 | Window Closed / Lapsed |