Method of treating glass forming molds and the like
Assignee: Graham Packaging Plastic Products Inc
•
Filing: 1979-10-09
•
Granted: 1981-04-28
•
Expires: 1999-10-09
Abstract
Abstract The present invention relates to a process for treating molten glass contacting surfaces including forming molds, gob chutes, neck rings, and the like, with an organic solution of a metal organic phosphate having a finely-divided lubricious filler dispersed therein, the dispersion being used to coat such glass contacting surfaces and the coating being heated to form a degradation product having improved glass releasing and wear-resistant properties. The coating forms a solid film lubricant especially adapted for use in manufacturing glass articles providing quick release of the molded glass articles, a protective lubricant layer for the glass contacting surfaces, and eliminating the need for frequent swabbing of such surfaces, especially mold surfaces with oily compositions.
Inventors
- 👤 Ian M. Thomas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 07:44
CPC Classifications
C; C03; C03B; C03B40/00; C03B40/02
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
80 words
A process wherein molten glass is shaped in a glass forming mold, said mold having a lubricated glass forming surface, the improvement wherein said glass forming surface is coated with a continuous imperforate solid film lubricant layer comprised of the heated degradation product of a metal organic phosphate having a finely-divided lubricous filler dispersed therein, said solid film layer being present in sufficient thickness to provide a glass releasing quality and extended wear lift to said layer within said mold.
Claim 2
Dependent Claim
80 words
A process wherein molten glass is shaped in a glass forming mold, said mold having a lubricated glass forming surface, the improvement wherein said glass forming surface is coated with a continuous imperforate solid film lubricant layer comprised of the heated degradation product of a metal organic phosphate having a finely-divided lubricous filler dispersed therein, said solid film layer being present in sufficient thickness to provide a glass releasing quality and extended wear lift to said layer within said mold.
Claim 3
Dependent Claim
80 words
A glass forming mold for shaping molten glass consisting of a hollow cavity having a lubricated glass forming surface, the improvement wherein said glass forming surface is coated with a continuous imperforate solid film lubricant layer comprised of the heated degradation product of a metal organic phosphate having a finely-divided lubricous filler dispersed therein, said solid film layer being present in sufficient thickness to provide a glass releasing quality and extended wear life to said layer within said mold cavity.
Claim 4
Dependent Claim
80 words
A glass forming mold for shaping molten glass consisting of a hollow cavity having a lubricated glass forming surface, the improvement wherein said glass forming surface is coated with a continuous imperforate solid film lubricant layer comprised of the heated degradation product of a metal organic phosphate having a finely-divided lubricous filler dispersed therein, said solid film layer being present in sufficient thickness to provide a glass releasing quality and extended wear life to said layer within said mold cavity.
Claim 5
Dependent Claim
47 words
The improvement in accordance with claim 2, wherein said metal to phosphorus ratio in said metal organic phosphate comprises about 1.0/2.0 to 3.5, and the metal of said metal organic phosphate is selected from the group consisting of aluminum, magnesium and aluminum in combination, and mixtures thereof.
Claim 6
Dependent Claim
23 words
The improvement in accordance with claim 2, wherein said finely-divided lubricous filler to degraded metal organic phosphate ratio ranges from 30-70 to 70-30.
Claim 7
Dependent Claim
40 words
The improvement in accordance with claim 2, wherein said finely-divided lubricous filler is selected from the group consisting of graphite, boron nitride, carbon black, silica, mica, talc, clay, molydenum, tungsten, chromium, molydenum disulfide, tungsten disulfide, lead sulfide, and mixtures thereof.
Claim 8
Dependent Claim
14 words
The improvement in accordance with claim 2, wherein said finely-divided lubricous filler is graphite.
Claim 9
Dependent Claim
15 words
The improvement in accordance with claim 2, wherein said finely-divided lubricous filler is boron nitride.
Claim 10
Dependent Claim
16 words
The improvement in accordance with claim 2, wherein said metal organic phosphate is aluminum organic phosphate.
Claim 11
Dependent Claim
17 words
The improvement in accordance with claim 2, wherein said metal organic phosphate is magnesium aluminum organic phosphate.
Claim 12
Dependent Claim
32 words
The improvement in accordance with claim 2, wherein said metal organic phosphate is dissolved in an anyhdrous organic solvent selected from the group consisting of methoxyethanol, ethoxyethanol, butoxyethanol, methanol, and mixtures thereof.
Claim 13
Dependent Claim
89 words
In a process wherein molten glass is shaped in a glass-forming mold, said mold having a wear-resistant lubricated glass forming surface, the improvement wherein said glass forming surface is coated with a non-aqueous, non-acidic organic solution of a metal organic phosphate having a finely-divided lubricous filler dispersed therein, said coating being converted by heating to at least 200° C. into a degradation product constituting a solid film lubricant layer having sufficient thickness to provide a glass releasing quality and extended wear life to said lubricant layer within said molded.
Claim 14
Dependent Claim
89 words
In a process wherein molten glass is shaped in a glass-forming mold, said mold having a wear-resistant lubricated glass forming surface, the improvement wherein said glass forming surface is coated with a non-aqueous, non-acidic organic solution of a metal organic phosphate having a finely-divided lubricous filler dispersed therein, said coating being converted by heating to at least 200° C. into a degradation product constituting a solid film lubricant layer having sufficient thickness to provide a glass releasing quality and extended wear life to said lubricant layer within said molded.
Claim 15
Dependent Claim
26 words
The improvement in accordance with claim 11, wherein said degraded metal organic phosphate and said lubricous filler are present on about a 50--50 weight percent basis.
Claim 16
Dependent Claim
26 words
The process in accordance with claim 11, wherein said metal organic phosphate is selected from the group consisting aluminum organic phosphate and magnesium aluminum organic phosphate.
Claim 17
Dependent Claim
15 words
The process in accordance with claim 11, wherein said finely divided lubricous filler comprises graphite.
Claim 18
Dependent Claim
15 words
The process in accordance with claim 11, wherein said finely-divided lubricous filler comprises boron nitride.
Claim 19
Dependent Claim
32 words
The process in accordance with claim 11, wherein said metal organic phosphate is dissolved in an anhydrous organic solvent selected from the group consisting of methoxyethanol, ethoxyethanol, butoxyethanol, methanol, and mixtures thereof.
Claim 20
Dependent Claim
106 words
A process of treating a glass forming mold for forming molten glass charges to provide a wear-resistant lubricated glass forming surface comprising the steps of coating the glass forming surface of said mold with a non-aqueous, non-acidic organic solution of a metal organic phosphate having a finely-divided lubricous filler dispersed therein, heating the said forming surface and coating to a temperature of at least 200° C. for a period of at least a few minutes to form a degradation product constituting a solid film lubricant layer having sufficient thickness to provide a glass releasing quality and extended wear life to said lubricant layer within said mold.
Claim 21
Dependent Claim
106 words
A process of treating a glass forming mold for forming molten glass charges to provide a wear-resistant lubricated glass forming surface comprising the steps of coating the glass forming surface of said mold with a non-aqueous, non-acidic organic solution of a metal organic phosphate having a finely-divided lubricous filler dispersed therein, heating the said forming surface and coating to a temperature of at least 200° C. for a period of at least a few minutes to form a degradation product constituting a solid film lubricant layer having sufficient thickness to provide a glass releasing quality and extended wear life to said lubricant layer within said mold.
Claim 22
Dependent Claim
102 words
A process of treating a molten glass contacting surface to provide a wear-resistant lubricated glass contacting surface comprising the steps of coating the glass contacting surface with a non-aqueous, non-acidic organic solution of a metal organic phosphate having a finely-divided lubricous filler dispersed therein, heating the said glass contacting surface and coating to a temperature of at least about 200° C. for a period of at least a few minutes to form a degradation product constituting a solid film lubricant having sufficient thickness to provide a glass releasing quality and extended wear life to said lubricant layer on said glass contacting surface.
Claim 23
Dependent Claim
102 words
A process of treating a molten glass contacting surface to provide a wear-resistant lubricated glass contacting surface comprising the steps of coating the glass contacting surface with a non-aqueous, non-acidic organic solution of a metal organic phosphate having a finely-divided lubricous filler dispersed therein, heating the said glass contacting surface and coating to a temperature of at least about 200° C. for a period of at least a few minutes to form a degradation product constituting a solid film lubricant having sufficient thickness to provide a glass releasing quality and extended wear life to said lubricant layer on said glass contacting surface.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-27 | 1984-10-27 | 1985-04-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-27 | 1988-10-27 | 1989-04-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-27 | 1992-10-27 | 1993-04-28 | $7700.00 | Window Closed / Lapsed |