Self-hardening composition and composite therefrom
Assignee: HERA Corp A CORP OF NEW MEXICO
•
Filing: 1980-01-25
•
Granted: 1981-04-21
•
Expires: 2000-01-25
Abstract
Abstract A self-hardening composition consists essentially of 3-5% by weight of an alkaline earth metal chloride, 0.5-1.5% by weight of calcium metasilicate, 0.5-1.5% by weight of sodium fluorosilicate, 30-40% by weight of sodium silicate, 0.02-0.04% by weight of aluminum silicate clay and water. Composites made therefrom can include expanded aggregate material and/or reinforcing fibers, as extenders, or to impart control over the open curing time to preset requirements.
Inventors
- 👤 Dennis J. Hacker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:05
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/24; C04B28/26
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
42 words
A self-hardening composition consisting essentially of 3-5% by weight of an alkaline earth metal chloride, 0.5-1.5% by weitht of calcium metasilicate, 0.5-1.5% by weight of sodium fluorosilicate, 30-40% by weight of sodium silicate, 0.02-0.04% by weight of aluminum silicate clay and water.
Claim 2
Dependent Claim
42 words
A self-hardening composition consisting essentially of 3-5% by weight of an alkaline earth metal chloride, 0.5-1.5% by weitht of calcium metasilicate, 0.5-1.5% by weight of sodium fluorosilicate, 30-40% by weight of sodium silicate, 0.02-0.04% by weight of aluminum silicate clay and water.
Claim 3
Dependent Claim
15 words
The composition of claim 1, wherein the alkaline earth metal chloride is CaCl2.MgCl 2 .
Claim 4
Dependent Claim
12 words
The composition of claim 1, wherein the aluminum silicate clay is kaolin.
Claim 5
Dependent Claim
15 words
The composition of claim 1, wherein the amount of sodium silicate is 35-39% by weight.
Claim 6
Dependent Claim
14 words
The composition of claim 4, wherein the ratio Na 2 O:SiO 2 is 1:1.65-3.9.
Claim 7
Dependent Claim
40 words
The composition of claim 1, wherein the alkaline earth metal chloride is CaCl2.MgCl 2 , the aluminum silicate clay is kaolin, the amount of sodium silicate is 35-30% by weight, and the molar ratio Na 2 O:SiO 2 is 1:1.65-3.9.
Claim 8
Dependent Claim
23 words
A self-hardening composite material comprising 10-35% by weight of the composition of claim 1, admixed with an expanded aggregate material or reinforcing fibers.
Claim 9
Dependent Claim
14 words
A laminate comprising a composite of claim 7, firmly adhered to a facing sheet.
Claim 10
Dependent Claim
24 words
The composite material of claim 7, wherein the expanded aggregate material is cellular perlite, vermiculite, cellular glass, expanded slag, cellular diatomite, or cellular pumice.
Claim 11
Dependent Claim
14 words
The composite of claim 7, wherein the reinforcing fiber is fiberglass or mineral fibers.
Claim 12
Dependent Claim
33 words
The composite of claim 8, wherein the reinforcing fiber is fiberglass or mineral fiber and the expanded cellular aggregate material is cellular perlite, vermiculite, cellular glass, expanded slag, cellular diatomite, or cellular pumice.
References Cited (Backward Citations)
US3138471A
Cited
US3203813A
Cited
US3450548A
Cited
US3483006A
Cited
US3508936A
Cited
US3837872A
Cited
US3837872B1
Cited
US3874887A
Cited
US3933514A
Cited
US4066463A
Cited
US4030939A
Cited
US4138268A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-20 | 1984-10-20 | 1985-04-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-20 | 1988-10-20 | 1989-04-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-20 | 1992-10-20 | 1993-04-21 | $7700.00 | Window Closed / Lapsed |