Method of making optical fibers utilizing thermophoretic deposition of glass precursor particulates
Assignee: AT&T Inc
•
Filing: 1979-10-01
•
Granted: 1981-04-21
•
Expires: 1999-10-01
Abstract
Abstract The deposition of glass precursor particulates, during optical fiber fabrication, is rendered more efficient by increasing the thermal forces which play a significant role in directing the particulate material to an appropriate substrate. Specific embodiments are addressed to various optical fiber fabrication processes, all of which involve the formation of glass particulate material and its subsequent deposition on an appropriate substrate.
Inventors
- 👤 William R. Sinclair
- 👤 Willy W. van Roosbroeck
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:08
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/018
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
65 words
A method of fabricating optical fibers comprising: a. forming glass precursor particulate material; b. depositing the glass precursor particulate material on an appropriate substrate to yield an optical fiber preform; and c. drawing the optical fiber preform into an optical fiber; the invention CHARACTERIZED IN THAT the particulate material is directed from regions of higher temperature to regions of lower temperature utilizing additional thermophoretic means.
Claim 2
Independent Claim
65 words
A method of fabricating optical fibers comprising: a. forming glass precursor particulate material; b. depositing the glass precursor particulate material on an appropriate substrate to yield an optical fiber preform; and c. drawing the optical fiber preform into an optical fiber; the invention CHARACTERIZED IN THAT the particulate material is directed from regions of higher temperature to regions of lower temperature utilizing additional thermophoretic means.
Claim 3
Dependent Claim
15 words
The method of claim 1 wherein the additional thermophoretic means comprises a temperature gradient means.
Claim 4
Dependent Claim
23 words
The method of claim 2 wherein the additional temperature gradient thermophoretic means does not result substantially in the formation of additional particulate material.
Claim 5
Dependent Claim
27 words
The method of claim 3 wherein the substrate is the inside surface of a heated tubular glass starting member, through which appropriate glass precursor vapors are flowed.
Claim 6
Dependent Claim
46 words
The method of claim 4 wherein the tubular starting member is heated using at least two external heat sources, the additional thermophoretic means comprising one of the heat sources which is placed downstream of the other, at a point at which there is substantially no deposition.
Claim 7
Dependent Claim
25 words
The method of claim 4 wherein the additional thermophoretic means comprises a heated rod situated within the tubular starting member and essentially coaxial with it.
Claim 8
Dependent Claim
36 words
The method of claim 6 wherein the additional thermophoretic means further comprises a gas stream which is flowed through the tubular starting member adjacent to the tubular wall so as to further cool the tubular wall.
Claim 9
Dependent Claim
51 words
The method of claim 4 wherein the heat source is external to the tube and extends substantially throughout the length of the tubular starting member, and wherein a rod is placed within the tubular starting member, coaxial with it, and heated to a temperature greater than that of the tube wall.
Claim 10
Dependent Claim
12 words
The method of claim 8 wherein the heat source is a flame.
Claim 11
Dependent Claim
41 words
The method of claim 3 wherein the substrate is a tubular glass starting member and wherein glass precursor particulate material is formed externally to the tube and subsequently introduced into the tube and deposited on the inside wall of the tube.
Claim 12
Dependent Claim
41 words
The method claim 10 wherein the tubular member is heated externally over substantially its entire length by an extended heat source having associated with it a limited region of decreased temperature and wherein deposition occurs over the region of decreased temperature.
Claim 13
Dependent Claim
20 words
The method of claim 11 wherein the region of decreased temperature is cooled by means of an external cooling source.
Claim 14
Dependent Claim
26 words
The method of claim 10 or 11 wherein the glass precursor material is formed externally to the tubular starting member by means of an hydrolysis burner.
Claim 15
Dependent Claim
12 words
The method of claim 13 wherein the heat source is a flame.
Claim 16
Dependent Claim
27 words
The method of claim 3 wherein the starting member is a glass rod, and wherein the glass particulate material is deposited on the outside of the rod.
Claim 17
Dependent Claim
22 words
The method of claim 15 wherein the additional thermophoretic means comprises a cooling means applied to the center region of the rod.
Claim 18
Dependent Claim
26 words
The method of claim 16 wherein the cooling means comprises a cooling material which is passed through a bore in the central region of the rod.
Claim 19
Dependent Claim
25 words
The method of claim 4 wherein the additional temperature gradient thermophoretic means comprises a cooling means applied to the tube downstream of the heated region.
Claim 20
Dependent Claim
13 words
The method of claim 4 wherein the cooling means comprises a gas stream.
Claim 21
Dependent Claim
38 words
The method of claim 4 wherein the precursor vapors are introduced into the tube by means of appropriate gas lines and wherein the additional temperature gradient thermophoretic means comprises a heating means applied to the said gas lines.
Claim 22
Dependent Claim
34 words
The method of claim 3 wherein the additional thermophoretic temperature gradient means are so selected as to result in the deposition of substantially all particles with an axial velocity less than a preselected value.
Claim 23
Independent Claim
75 words
A method of fabricating optical fibers comprising: a. forming glass precursor particulate material; b. depositing the glass precursor particulate material on an appropriate substrate to yield an optical fiber preform; and c. drawing the optical fiber preform into an optical fiber; the invention characterized in that the particulate material is directed from regions of higher temperature to regions of lower temperature utilizing additional thermophoretic means thereby directing the glass precursor particulate material to the substrate.
Claim 24
Independent Claim
75 words
A method of fabricating optical fibers comprising: a. forming glass precursor particulate material; b. depositing the glass precursor particulate material on an appropriate substrate to yield an optical fiber preform; and c. drawing the optical fiber preform into an optical fiber; the invention characterized in that the particulate material is directed from regions of higher temperature to regions of lower temperature utilizing additional thermophoretic means thereby directing the glass precursor particulate material to the substrate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-20 | 1984-10-20 | 1985-04-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-20 | 1988-10-20 | 1989-04-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-20 | 1992-10-20 | 1993-04-21 | $7700.00 | Window Closed / Lapsed |