Abstract A method of producing a cross-linked polyvinyl alcohol structure, such as a battery separator membrane or electrode envelope. An aqueous solution of a film-forming polyvinyl alcohol is admixed with an aldehyde cross-linking agent at basic pH to inhibit cross-linking. The cross-linking agent, preferably a dialdehyde such as glutaraldehyde, is used in an amount of from about 1/2 to about 20% of the theoretical amount required to cross-link all of the hydroxyl groups of the polymer. The aqueous admixture is formed into a desired physical shape, such as by casting a sheet of the solution. The sheet is then dried to form a self-supporting film. Cross-linking is then effected by immersing the film in aqueous acid solution. The resultant product has excellent properties for use as a battery separator, including a low electrical resistivity, the value of which is principally determined by the amount of cross-linking which is easily and closely controlled by the amount of cross-linking agent added to the polymer.
An alkaline battery having a cross linked polyvinyl alcohol separator made by providing an aqueous admixture of a film-forming polyvinyl alcohol resin and an aldehyde cross-linking agent capable of cross-linking the polyvinyl alcohol resin, said aldehyde being a dialdehyde having the formula ##STR3## wherein R is a divalent organic radical having from 1 to 12 carbon atoms, said aldehyde being present in an amount required to react with from 0.5 to 20% of all the hydroxyl groups of the polyvinyl alcohol resin, said aqueous admixture having a basic pH to inhibit a cross-linking reaction between the aldehyde and the resin; forming said aqueous admixture into a sheet drying the shaped admixture to form a self-supporting polymeric sheet containing said cross-linking agent; and contacting said polymeric sheet with an aqueous acid catalyst solution to effect the cross-linking reaction between said resin and said aldehyde to produce a cross-linked polyvinyl alcohol separator.
Claim 2
Dependent Claim
150 words
An alkaline battery having a cross linked polyvinyl alcohol separator made by providing an aqueous admixture of a film-forming polyvinyl alcohol resin and an aldehyde cross-linking agent capable of cross-linking the polyvinyl alcohol resin, said aldehyde being a dialdehyde having the formula ##STR3## wherein R is a divalent organic radical having from 1 to 12 carbon atoms, said aldehyde being present in an amount required to react with from 0.5 to 20% of all the hydroxyl groups of the polyvinyl alcohol resin, said aqueous admixture having a basic pH to inhibit a cross-linking reaction between the aldehyde and the resin; forming said aqueous admixture into a sheet drying the shaped admixture to form a self-supporting polymeric sheet containing said cross-linking agent; and contacting said polymeric sheet with an aqueous acid catalyst solution to effect the cross-linking reaction between said resin and said aldehyde to produce a cross-linked polyvinyl alcohol separator.
Claim 3
Dependent Claim
28 words
A battery according to claim 1 wherein said polyvinyl alcohol has a number average molecular weight of from 10,000 to 200,000 and is provided in an aqueous solution.
Claim 4
Dependent Claim
14 words
A battery according to claim 1 wherein R is a divalent aliphatic hydrocarbon radical.
Claim 5
Dependent Claim
11 words
A battery according to claim 3 wherein said dialdehyde is glutaraldehyde.
Claim 6
Dependent Claim
22 words
A battery according to claim 3 wherein said dialdehyde has the formula ##STR4## wherein x and y are each 0 or 2.
Claim 7
Dependent Claim
13 words
A battery according to claim 5 wherein x and y are each 0.
Claim 8
Dependent Claim
36 words
A battery according to claim 1 wherein two of the sheets are superposed and joined at their edges to form an envelope bag for an electrode of an alkaline battery prior to effecting said cross-linking reaction.