Glass fibers with reduced tendency to form gumming deposits and sizing composition
Assignee: PPG Industries Inc
•
Filing: 1979-09-13
•
Granted: 1981-03-31
•
Expires: 1999-09-13
Abstract
Abstract The sizing compositions and sized glass fibers formed therefrom are provided, wherein the sized glass fibers have a reduced tendency to form gumming deposits on fabrication machinery under relatively high humidity conditions, and wherein processibility of the sized glass fibers with the sizing composition is improved, and wherein the sized glass fiber strand package is improved. The sizing composition comprises in weight percent of the non-aqueous ingredients, about 50 to about 75 weight percent of a starch mixture having about 75 to about 95 percent by weight of the mixture comprised of an underivatized, high amylose starch component and about 5 to about 25 weight percent of the mixture comprised of an easily cookable low amylose starch component; and about 5 to about 35 percent of one or more waxes selected from the group consisting of animal waxes, vegetable waxes, mineral waxes, synthetic waxes, and petroleum waxes; and about 9 to about 77 percent by weight of a nonionic lubricant having fatty triglycerides; and about 10 to about 45 percent by weight of an alkyl imidazoline textile softener; and at least 0.1 parts per part of wax and per part of nonionic lubricant of a mixture of sorbitan monostearate and polyoxyethylene sorbitan monostearate wherein one emulsifier has an HLB as low as 4.5 and the other emulsifier has an HLB as high as 15 and wherein the ratio of the emulsifiers are sufficient to give an HLB for the emulsifying mixture between about 8 and about 12. The sizing composition may also contain wetting agents, coupling agents, cationic lubricants, bactericides and the like. The sized glass fibers have the dried residue of the sizing composition on the fibers in an amount of about 0.8 to about 1.5 weight percent based on the weight of the glass.
Inventors
- 👤 Dennis M. Fahey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 12:33
CPC Classifications
D; D03; D03D; D03D15/00; D03D15/20; D03D15/242; D03D15/267; C; C03; C03C; C03C25/00; C03C25/10; C03C25/24; C03C25/26; C03C25/32; C03C25/321; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2938; Y10T428/2964
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
259 words
An aqueous sizing composition for use with glass fibers to produce sized glass fibers with improved processibility and improved packaging structure for ease of handling and fabrication that has a reduced tendency to form gumming deposits on fabrication machinery under high relative humidity conditions comprising in weight percent based on the non-aqueous components of the sizing composition: (a) about 50 to about 75 percent of a starch mixture comprised of about 75 weight percent to about 95 weight percent of an underivatized, high amylose starch component and about 5 weight percent to about 25 weight percent of an easily cookable, low amylose starch component; (b) about 5 to about 35 percent by weight of a wax selected from the group consisting of animal waxes, vegetable waxes, mineral waxes, synthetic waxes and petroleum waxes; (c) about 9 to about 77 percent by weight of a nonionic lubricant having fatty triglycerides selected from the group consisting of hydrogenated cotton seed oil, hydrogenated corn oil, hydrogenated soybean oil and hydrogenated vegetable oil; (d) about 10 to about 45 percent by weight of an alkyl imidazoline textile softener; (e) at least 0.01 part per part of wax and per part of nonionic lubricant of a mixture of sorbitan monostearate emulsifying agent and polyoxyethylene sorbitan monostearate emulsifying agent wherein one emulsifier has an HLB as low as around 4.5 and the other emulsifying agent has a HLB as high as 15 and wherein the ratios of the emulsifiers are sufficient to give an HLB for the emulsifying mixture between about 8 and about 12.
Claim 2
Dependent Claim
259 words
An aqueous sizing composition for use with glass fibers to produce sized glass fibers with improved processibility and improved packaging structure for ease of handling and fabrication that has a reduced tendency to form gumming deposits on fabrication machinery under high relative humidity conditions comprising in weight percent based on the non-aqueous components of the sizing composition: (a) about 50 to about 75 percent of a starch mixture comprised of about 75 weight percent to about 95 weight percent of an underivatized, high amylose starch component and about 5 weight percent to about 25 weight percent of an easily cookable, low amylose starch component; (b) about 5 to about 35 percent by weight of a wax selected from the group consisting of animal waxes, vegetable waxes, mineral waxes, synthetic waxes and petroleum waxes; (c) about 9 to about 77 percent by weight of a nonionic lubricant having fatty triglycerides selected from the group consisting of hydrogenated cotton seed oil, hydrogenated corn oil, hydrogenated soybean oil and hydrogenated vegetable oil; (d) about 10 to about 45 percent by weight of an alkyl imidazoline textile softener; (e) at least 0.01 part per part of wax and per part of nonionic lubricant of a mixture of sorbitan monostearate emulsifying agent and polyoxyethylene sorbitan monostearate emulsifying agent wherein one emulsifier has an HLB as low as around 4.5 and the other emulsifying agent has a HLB as high as 15 and wherein the ratios of the emulsifiers are sufficient to give an HLB for the emulsifying mixture between about 8 and about 12.
Claim 3
Dependent Claim
20 words
The sizing composition of claim 1 that contains about 1.5 percent to 20 percent by weight of a coupling agent.
Claim 4
Dependent Claim
12 words
The sizing composition of claim 2 wherein the coupling agent is gamma-methacryloxypropyltrimethoxysilane.
Claim 5
Dependent Claim
72 words
The sizing composition of claim 1 that has from about 4 to about 52 percent by weight of a salt of a polyamino functional polyamide resin wherein said polyamino functional polyamide resin salt is formed from the condensation reaction product of a polycarboxylic acid or carboxylic acid and a polyamine wherein said polyamine has greater than two amine groups per molecule and wherein said carboxylic acid has 1 to 5 carbon atoms.
Claim 6
Dependent Claim
21 words
The sizing composition of claim 1 wherein the wax, nonionic lubricant, emulsifying agents, are present in the form of an emulsion.
Claim 7
Dependent Claim
16 words
The sizing composition of claim 5 wherein a textile softening agent is present in the emulsion.
Claim 8
Dependent Claim
40 words
The sizing composition of claim 1 wherein the starch in the underivatized, high amylose content starch fraction is an underivatized corn starch having an amylose content of about 50 to 60 percent by weight with the remaining starch being amylopectin.
Claim 9
Dependent Claim
46 words
The sizing composition of claim 1 wherein the starch of the low amylose containing starch component is selected from potato starch or a hybrid or slightly cross-linked corn starch having an amylose content from 25 to 27 percent by weight with the remaining starch being amylopectin.
Claim 10
Dependent Claim
52 words
The sizing composition of claim 1 wherein the sorbitan monostearate has an HLB of 4.7 and the polyoxyethylene sorbitan monostearate is a polyoxyethylene (20) sorbitan monostearate having an HLB of 14.9, and the mixture of both are present in an amount in the range of about 1.5 to about 3 weight percent.
Claim 11
Dependent Claim
23 words
The sizing composition of claim 1 wherein a wetting agent is present in an amount of about 0.1 to about 3 weight percent.
Claim 12
Dependent Claim
12 words
The sizing composition of claim 9 wherein the wetting agent is octylphenoxypoly-(ethyleneoxy)ethanol.
Claim 13
Dependent Claim
21 words
The sizing composition of claim 1 wherein a bactericide is present in an amount sufficient to retard molding and bacterial growth.
Claim 14
Dependent Claim
12 words
The sizing composition of claim 11 wherein the bactericide is organo-tin bactericide.
Claim 15
Dependent Claim
23 words
The sizing composition of claim 1 wherein polyethyleneglycol is present in an amount sufficient to provide a plasticizing effect for the sizing composition.
Claim 16
Dependent Claim
30 words
The sizing composition of claim 1 being present as a dried residue on glass fibers in an amount of 0.80 percent to about 2.5 percent by weight of the glass.
Claim 17
Independent Claim
220 words
The method of preparing a sizing composition for treating glass fibers to produce sized glass fibers with improved processibility of formation of the glass fibers and an improved sized glass fiber strand package wherein the sized glass fibers have a reduced tendency to form gumming deposits on fabrication machinery under high relative humidity conditions, comprising: (a) cooking a starch mixture comprised of 75 to 95 weight percent of an underivatized high amylose starch component and 5 to 25 percent by weight of an easily cookable low amylose starch component at a temperature and pressure conditions to cause partial cooking to the extent that the starch forms a suspension with water; (b) adding to the partially cooked starch an emulsion formed by adding sorbitan monostearate and polyoxyethylene sorbitan monostearate, one stearate having an HLB of around 4.5 and the other stearate having an HLB of around 15, and a wax selected from the group consisting of animal wax, vegetable wax, synthetic wax, mineral wax and petroleum wax and a nonionic lubricant having fatty triglycerides selected from the group consisting of hydrogenated vegetable oils and an alkyl imidazoline textile softener, and water at a temperature in the range of about 150° to about 170° F.; and (c) adding other ingredients including coupling agent, wetting agent, cationic lubricant, bactericide, either simultaneously or sequentially.
Claim 18
Independent Claim
220 words
The method of preparing a sizing composition for treating glass fibers to produce sized glass fibers with improved processibility of formation of the glass fibers and an improved sized glass fiber strand package wherein the sized glass fibers have a reduced tendency to form gumming deposits on fabrication machinery under high relative humidity conditions, comprising: (a) cooking a starch mixture comprised of 75 to 95 weight percent of an underivatized high amylose starch component and 5 to 25 percent by weight of an easily cookable low amylose starch component at a temperature and pressure conditions to cause partial cooking to the extent that the starch forms a suspension with water; (b) adding to the partially cooked starch an emulsion formed by adding sorbitan monostearate and polyoxyethylene sorbitan monostearate, one stearate having an HLB of around 4.5 and the other stearate having an HLB of around 15, and a wax selected from the group consisting of animal wax, vegetable wax, synthetic wax, mineral wax and petroleum wax and a nonionic lubricant having fatty triglycerides selected from the group consisting of hydrogenated vegetable oils and an alkyl imidazoline textile softener, and water at a temperature in the range of about 150° to about 170° F.; and (c) adding other ingredients including coupling agent, wetting agent, cationic lubricant, bactericide, either simultaneously or sequentially.
References Cited (Backward Citations)
US3227192A
Cited
US3615311A
Cited
US3664855A
Cited
US3928666A
Cited
US3869308A
Cited
US4066106A
Cited
US4197349A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-30 | 1984-09-29 | 1985-03-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-30 | 1988-09-29 | 1989-03-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-30 | 1992-09-29 | 1993-03-31 | $7700.00 | Window Closed / Lapsed |