Method of preparing a novel cement particularly suitable as a refractory cement
Assignee: Imerys Aluminates SA
•
Filing: 1980-01-04
•
Granted: 1981-03-31
•
Expires: 2000-01-04
Abstract
Abstract A refractory cement with outstanding mechanical properties contains 10 to 30 parts by weight of C 4 A 3 S clinker and 70 to 90 parts by weight of an aluminous clinker including 30 to 75% CA. This cement may be prepared by either grinding said clinkers to a specified fineness and then mixing the same, or by grinding said clinkers simultaneously and jointly to said specified fineness. The novel double clinker cement allows concrete with considerably improved refractory and mechanical properties to be prepared, as compared to the corresponding products known up to now.
Inventors
- 👤 Alain Mathieu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 02:40
CPC Classifications
C; C04; C04B; C04B7/00; C04B7/32; C04B7/323
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
53 words
A comminuted double clinker refractory cement comprising 10 to 30 parts by weight of a first clinker having the formula (CaO) 4 (A1 2 O 3 ) 3 (SO 3 ) and 70 to 90 parts by weight of a second clinker containing 30 to 75% of (CaO) (Al 2 O 3 ).
Claim 2
Dependent Claim
53 words
A comminuted double clinker refractory cement comprising 10 to 30 parts by weight of a first clinker having the formula (CaO) 4 (A1 2 O 3 ) 3 (SO 3 ) and 70 to 90 parts by weight of a second clinker containing 30 to 75% of (CaO) (Al 2 O 3 ).
Claim 3
Dependent Claim
85 words
A cement according to claim 1, wherein said (CaO) 4 (Al 2 O 3 ) 3 (SO 3 ) clinker is a clinker obtained by mixing raw materials sufficient to provide CaO, Al 2 O 3 and SO 3 , in such amounts that after sintering at a temperature higher than 1400° C. a product having the following composition is obtained: ______________________________________
. CaO = 35-37%
. Al.sub.2 O.sub.3
= 48-54%
. SO.sub.3 = 9-14%
. Fe.sub.2 O.sub.3
= 0-4%
. SiO.sub.2 = 0-2%.
______________________________________
Claim 4
Dependent Claim
36 words
The cement of claim 1, wherein said (CaO) 4 (Al 2 O 3 ) 3 (SO 3 ) clinker has a granulometric particle size corresponding to a specific surface of 5000 to 8000 cm 2 /g.
Claim 5
Dependent Claim
28 words
The cement of claim 1, wherein said double clinker cement is prepared by mixing previously ground constituents, the fineness of said cement corresponding to 3000-6000 cm 2 /g.
Claim 6
Dependent Claim
27 words
The cement of claim 1, wherein said double clinker cement is prepared by simultaneously and jointly grinding said clinkers to a fineness of 3500-5000 cm 2 /g.
Claim 7
Dependent Claim
20 words
The cement of claim 1, wherein said first clinker and said second clinker are mixed in a ratio of 20/80.
Claim 8
Dependent Claim
50 words
The cement of claim 1, wherein said first clinker is admixed with a second clinker containing 70% by weight (CaO)(Al 2 O 3 ), the ratio of the respective amount by weight of (CaO) 4 (Al 2 O 3 ) 3 (SO 3 ) and said second clinker being 10/90.
References Cited (Backward Citations)
US3510326A
Cited
US3857714A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-30 | 1984-09-29 | 1985-03-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-30 | 1988-09-29 | 1989-03-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-30 | 1992-09-29 | 1993-03-31 | $7700.00 | Window Closed / Lapsed |