Process for producing powdery isotactic polyolefin

Claim 2

A process for producing a powdery isotactic polyolefin having high isotactic characteristic and a narrow size distribution which comprises forming a polymerization catalyst system including a solid catalytic component (A) formed by the preparatory process consisting essentially of reacting a Grignard reagent with a chain or cyclic hydropolysiloxane having the unit formula: ##EQU4## (R 1 represents an alkyl, aryl, aralkyl, alkoxy or aryloxy group; a is o, 1 or 2; b is 1, 2 or 3 and a+b≦3), to form a reaction product (a); reacting the reaction product (a) dissolved in an aromatic hydrocarbon solvent with at least one compound having the formula: R.sup.2.sub.n M.sup.(z) X.sub.z-n (R 2 represents a C 1 to C 12 hydrocarbon moiety; M represents Al or Si; z represents atomic value of 3 or 4; X represents a halogen atom; n is 0, 1 . . . (z-1)) in the presence of the aromatic hydrocarbon solvent at a temperature lower than 85° C. to form a particulate reaction product (b); and reacting the particulate reaction product (b) with at least one titanium halide in the presence of an organic carboxylic acid ester (c) added in the preparatory process after the formation of reaction product (a) to obtain the solid catalytic component (A) and adding an organoaluminum compound (B) and then, polymerizing a C 3 or C 4 olefin in the presence of a catalytic amount of the polymerization catalyst system including component (A) and compound (B).

Claim 3

A process according to claim 1, wherein said polymerization catalyst system is prepared by combining the solid catalyst component (A) with the organoaluminum compound (B) at a molar ratio of the organoaluminum compound (B) to Ti component in the solid catalytic component (A) of 2 to 15 in the absence of added organic acid ester other than that used as component (c) in the preparation of reaction product (A).

Claim 4

A process according to claim 1, wherein an organic carboxylic acid ester (C) is incorporated in the polymerization catalyst system for combination with components (A) and (B) at a molar ratio of a total of the organic acid ester (c) remaining in the solid catalytic component (A) and a newly added organic acid ester (C), to the organoaluminum compound (B) of 0.1 to 0.4 at a molar ratio of the organoaluminum compound (B) to Ti component in the solid catalytic component (A) of 10 to 80.

Claim 5

A process according to claim 1, 2 or 3 wherein the hydropolysiloxane is methyl hydropolysiloxane.

Claim 6

A process according to claim 1, 2 or 3 wherein the Grignard reagent is an organomagnesium compound obtained by reacting an organic halide with a magnesium metal or a magnesium alloy.

Claim 7

A process according to claim 1, 2 or 3 wherein the compound having the formula R.sup.2.sub.n M.sup.(z) X.sub.z-n is aluminum chloride or silicon tetrachloride.

Claim 8

A process according to claim 1, 2 or 3 wherein the organic hydrocarbon solvent is benzene, toluene or xylene.

Claim 9

A process according to claim 1, 2 or 3 wherein an amount of the compound having the formula R.sup.2.sub.n M.sup.(z) X.sub.z-n is in a range of 0.1 to 10 mole per 1 mole of Mg component in the reaction product (a).

Claim 10

A process according to claim 1, 2 or 3 wherein the titanium halide is titanium tetrachloride.

Claim 11

A process according to claim 1, 2 or 3 wherein the organic acid ester (c) is an aromatic monocarboxylic acid ester.

Claim 12

A process according to claim 1, 2 or 3 wherein the organoaluminum is trialkyl aluminum or dialkylaluminum halide.

Claim 13

A process according to claim 3 wherein the organic acid ester (C) is an aromatic monocarboxylic acid ester.

Claim 14

A process according to claim 1 wherein the solid catalytic component (A) is treated with titanium tetrachloride before combining it with the organoaluminum compound (B).

Claim 15

A process according to claim 1, 2 or 3 wherein said olefin is propylene to obtain isotactic polypropylene.

Claim 16

A process for producing a powdery isotactic polyolefin having high isotactic characteristic and a narrow size distribution which comprises forming a polymerization catalyst system including a solid catalyst component (A) formed by the preparatory process consisting essentially of reacting (i) a Grignard reagent with (ii) a liquid chain or cyclic hydropolysiloxane having the unit formula: ##EQU5## (R 1 represents an alkyl, aryl, aralkyl, alkoxy or aryloxy group; a is 0, 1 or 2; b is 1, 2 or 3 and a+b≦3), in a ratio of 0.05 to 1 mols of (i) expressed as Mg in the Grignard reagent to 1 mol of (ii) expressed as Si to form a reaction product (a); reacting the reaction product (a) dissolved in an aromatic hydrocarbon solvent with at least one compound having the formula: R.sup.2.sub.n M.sup.(z) X.sub.z-n (R 2 represents a C 1 to C 12 hydrocarbon moiety; M represents Al or Si; z represents atomic value of 3 or 4; X represents a halogen atom; n is 0, 1 . . . (z-1)) at a molar ratio of 0.1 to 10:1 of the said compound to Mg in the reaction product (a) in the presence of the aromatic hydrocarbon solvent at a temperature in the range of 20° C. to 85° C. to form a particulate reaction product (b); and reacting the particulate reaction product (b) at 50° to 150° C. with at least one titanium halide in the presence of an aromatic organic carboxylic acid ester (c) added in the preparatory process after formation of the reaction product (a), at a molar ratio of 0.5 to 5 of (c) to 1 mol of Mg in the reaction product (b) and 0.1 to 150 mole of titanium halide per 1 mol of Mg in the reaction product (b), to obtain the solid catalytic component (A) containing 0.5 to 10 wt.% of Ti and a molar ratio of organic ester (c) to Ti of 0.6 to 4.0:1 and adding an organoaluminum compound (B) and then, polymerizing a C 3 or C 4 olefin in the presence of a catalytic amount of the polymerization catalyst system including component (A) and compound (B).

Claim 17

A process for producing a powdery isotactic polyolefin having high isotactic characteristic and a narrow size distribution which comprises forming a polymerization catalyst system including a solid catalyst component (A) formed by the preparatory process consisting essentially of reacting (i) a Grignard reagent with (ii) a liquid chain or cyclic hydropolysiloxane having the unit formula: ##EQU5## (R 1 represents an alkyl, aryl, aralkyl, alkoxy or aryloxy group; a is 0, 1 or 2; b is 1, 2 or 3 and a+b≦3), in a ratio of 0.05 to 1 mols of (i) expressed as Mg in the Grignard reagent to 1 mol of (ii) expressed as Si to form a reaction product (a); reacting the reaction product (a) dissolved in an aromatic hydrocarbon solvent with at least one compound having the formula: R.sup.2.sub.n M.sup.(z) X.sub.z-n (R 2 represents a C 1 to C 12 hydrocarbon moiety; M represents Al or Si; z represents atomic value of 3 or 4; X represents a halogen atom; n is 0, 1 . . . (z-1)) at a molar ratio of 0.1 to 10:1 of the said compound to Mg in the reaction product (a) in the presence of the aromatic hydrocarbon solvent at a temperature in the range of 20° C. to 85° C. to form a particulate reaction product (b); and reacting the particulate reaction product (b) at 50° to 150° C. with at least one titanium halide in the presence of an aromatic organic carboxylic acid ester (c) added in the preparatory process after formation of the reaction product (a), at a molar ratio of 0.5 to 5 of (c) to 1 mol of Mg in the reaction product (b) and 0.1 to 150 mole of titanium halide per 1 mol of Mg in the reaction product (b), to obtain the solid catalytic component (A) containing 0.5 to 10 wt.% of Ti and a molar ratio of organic ester (c) to Ti of 0.6 to 4.0:1 and adding an organoaluminum compound (B) and then, polymerizing a C 3 or C 4 olefin in the presence of a catalytic amount of the polymerization catalyst system including component (A) and compound (B).

Claim 18

The process of claim 14 wherein the Grignard reagent is butyl magnesium chloride, the hydropolysiloxane is a methylhydropolysiloxane, the aromatic hydrocarbon solvent is benzene, toluene, or xylene, the compound R 2 n M.sup.(z) X z-n is aluminum chloride or silicon tetrachloride, the titanium halide is titanium tetrachloride, and the organic carboxylic acid ester (c) is an aromatic monocarboxylic acid ester selected from methyl benzoate, ethyl benzoate, methyl toluate, ethyl toluate, methyl anisate and ethyl anisate.