Method of ion implantation into a semiconductor substrate provided with an insulating film
Assignee: Fujitsu Ltd
•
Filing: 1979-10-26
•
Granted: 1981-03-24
•
Expires: 1999-10-26
Abstract
Abstract In the production of a semiconductor device, such as an IC including MOS transistors, impurity ions are implanted into the semiconductor substrate of the device provided with an insulating film. The insulating film is electrically charged by the impurity ions and may be destroyed due to an electric potential between the insulating film and the semiconductor substrate. A novel process provided by the invention prevents the destruction of the insulating film and shortens the ion implantation time, since the beam current of the impurity ions is successively increased until the required dosing amount is obtained.
Inventors
- 👤 Haruhisa Mori
- 👤 Motoo Nakano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 12:14
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/22; Y; Y10; Y10S; Y10S438/00; Y10S438/91
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
90 words
In the method of ion implantation into a semiconductor substrate through an insulating layer wherein, as a result of said implantation, a surface potential is developed on said insulating layer, the steps comprising: beginning said implantation at a maximum ion beam current at which the peak value of the surface potential of said insulating layer is below a destructive level, and; thereafter at least once increasing the ion beam current but at all times maintaining said current at a level such that the surface potential remains below said destructive level.
Claim 2
Dependent Claim
90 words
In the method of ion implantation into a semiconductor substrate through an insulating layer wherein, as a result of said implantation, a surface potential is developed on said insulating layer, the steps comprising: beginning said implantation at a maximum ion beam current at which the peak value of the surface potential of said insulating layer is below a destructive level, and; thereafter at least once increasing the ion beam current but at all times maintaining said current at a level such that the surface potential remains below said destructive level.
Claim 3
Dependent Claim
19 words
A method according to claim 1, said insulating film being adjacent to a gate electrode of an MOS transistor.
Claim 4
Dependent Claim
19 words
A method according to claim 1, said insulating film comprising a locally thin portion of a field insulation film.
Claim 5
Dependent Claim
17 words
A method according to claim 1, said insulating film comprising a photoresist layer having a window therein.
Claim 6
Dependent Claim
39 words
A method according to claim 1 comprising regulating said beam current to maintain the maximum surface electric potential of said insulating film at a valve from 80 to 90% of the value at which said insulating film breaks down.
Claim 7
Dependent Claim
23 words
A method according to claim 1 or 5 comprising forming said insulating film to have a thickness of from 60 to 1000 A.
Claim 8
Dependent Claim
43 words
A method according to claim 1 or 5 comprising forming said insulating film to have a thickness from 50 to 1000 A, and regulating the dosing amount of the ions into said semiconductor substrate from 10 15 to 10 16 ions/cm 2 .
Claim 9
Dependent Claim
57 words
A method according to claim 1 or 5 comprising forming said insulating layer to have a thickness from 50 to 1000 A, regulating the dosing amount of the ions into said substrate from 10 15 to 10 16 ions/cm 2 , and controlling the time period of the ion implantation to 200 seconds per substrate or less.
Claim 10
Dependent Claim
34 words
The method of claim 1 requiring no more than 200 seconds for implanting up to 10 16 ions/cm 2 into a portion of said substrate surface including said insulating layer and said gate electrode.
Claim 11
Independent Claim
69 words
A method of implanting ions into a semiconductor substrate through an insulating layer on a surface of said substrate, said method comprising beginning said implantation at a dose rate at which a destructive surface potential will not develop across said insulating layer and subsequently increasing said dose rate, while keeping the surface potential of said insulating layer at a value below the destructive surface potential of said insulating layer.
Claim 12
Independent Claim
69 words
A method of implanting ions into a semiconductor substrate through an insulating layer on a surface of said substrate, said method comprising beginning said implantation at a dose rate at which a destructive surface potential will not develop across said insulating layer and subsequently increasing said dose rate, while keeping the surface potential of said insulating layer at a value below the destructive surface potential of said insulating layer.
Claim 13
Dependent Claim
24 words
The method of claim 9 or 10 comprising forming said insulating film to have a thickness in the range from 50 to 1000 angstroms.
Claim 14
Dependent Claim
38 words
The method of claim 9 or 10, comprising implanting said ions over and around said insulating layer and said gate electrode to form source and drain regions of an MOS transistor on respective sides of said gate electrode.
References Cited (Backward Citations)
US3117022A
Cited
US3734769A
Cited
US4088799A
Cited
US4021675A
Cited
US4001049A
Cited
US4076558A
Cited
US4118630A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-23 | 1984-09-22 | 1985-03-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-23 | 1988-09-22 | 1989-03-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-23 | 1992-09-22 | 1993-03-24 | $7700.00 | Window Closed / Lapsed |