Production of metal carbides in pure form

Claim 1

A method for the formation in substantially pure solid form of a metal carbide of a metal selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, uranium, tungsten, manganese, iron and mixtures thereof, which comprises: forming a blend of finely divided carbon and a finely divided ore or concentrate thereof, said ore or concentrate thereof containing said metal in oxide, carbonate and/or hydroxide form and gangue constituents comprising at least one oxide selected from the group consisting of silica, alumina, magnesia and lime, said carbon being present in said blend in an amount at least sufficient to convert all said metal in oxide, carbonate and/or hydroxide form in said ore or concentrate thereof to a corresponding metal carbide, heating said blend in a reaction zone to a temperature at least sufficient to initiate and sustain a single step solid state reducing and carburization reaction between said carbon and said metal in oxide, carbonate and/or hydroxide form to convert substantially all said metal in oxide, carbonate and/or hydroxide form to a corresponding solid metal carbide in accordance with the schematic equation: MeO+2C→MeC+CO wherein MeO is the metal in oxide, carbonate and/or hydroxide form and MeC is the metal carbide, while removing carbon monoxide evolved in said solid state reaction from said reaction zone, the temperature of said heating in said solid state reaction being insufficiently high to result in significant reduction of said gangue constituents, whereby said gangue constituents are left substantially unaffected by said solid state reaction, and, after completion of said solid state reaction, physically separating said solid metal carbide in substantially pure form from said unaffected solid gangue constituents.

Claim 2

A method for the formation in substantially pure solid form of a metal carbide of a metal selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, uranium, tungsten, manganese, iron and mixtures thereof, which comprises: forming a blend of finely divided carbon and a finely divided ore or concentrate thereof, said ore or concentrate thereof containing said metal in oxide, carbonate and/or hydroxide form and gangue constituents comprising at least one oxide selected from the group consisting of silica, alumina, magnesia and lime, said carbon being present in said blend in an amount at least sufficient to convert all said metal in oxide, carbonate and/or hydroxide form in said ore or concentrate thereof to a corresponding metal carbide, heating said blend in a reaction zone to a temperature at least sufficient to initiate and sustain a single step solid state reducing and carburization reaction between said carbon and said metal in oxide, carbonate and/or hydroxide form to convert substantially all said metal in oxide, carbonate and/or hydroxide form to a corresponding solid metal carbide in accordance with the schematic equation: MeO+2C→MeC+CO wherein MeO is the metal in oxide, carbonate and/or hydroxide form and MeC is the metal carbide, while removing carbon monoxide evolved in said solid state reaction from said reaction zone, the temperature of said heating in said solid state reaction being insufficiently high to result in significant reduction of said gangue constituents, whereby said gangue constituents are left substantially unaffected by said solid state reaction, and, after completion of said solid state reaction, physically separating said solid metal carbide in substantially pure form from said unaffected solid gangue constituents.