US4255480A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Abrasion-resistant laminate
Assignee: Nevamar Corp
•
Filing: 1978-02-22
•
Granted: 1981-03-10
•
Expires: 1998-02-22
Abstract
Abstract An abrasion-resistant laminate is prepared by providing an ultra thin coating of mineral particles and micro crystalline cellulose on the surface of conventional printed paper, followed by impregnating the paper with a conventional laminating resin, and then using the print paper so obtained in a laminating process without the necessity of using an overlay sheet.
Inventors
- 👤 Herbert I. Scher
- 👤 Israel S. Ungar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 10:44
CPC Classifications
B; B32; B32B; B32B38/00; B32B38/08; B41; B41M; B41M7/00; B41M7/0036; D; D21; D21H; D21H27/00; D21H27/18; D21H27/22; D21H27/26; D21H27/28; B32B2260/00; B32B2260/04; B32B2260/046; B32B2305/00; B32B2305/30; B32B2307/00; B32B2307/50; B32B2307/554; B32B2317/00; B32B2317/12; B32B2451/00; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1043; Y10T156/1044; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/24521; Y10T428/24545; Y10T428/24554; Y10T428/24612; Y10T428/24802; Y10T428/24893; Y10T428/24909; Y10T428/249921; Y10T428/249953; Y10T428/249986; Y10T428/249994; Y10T428/25; Y10T428/256; Y10T428/257
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
224 words
A method of producing an abrasion resistant decorative laminate from at least one backing layer and a thermosetting resin impregnated decorative facing sheet, said laminate having enhanced abrasion resistance without an overlay layer, the method comprising: coating a decorative facing sheet with an ultra-thin wet layer of a mixture of (1) an abrasion resistant hard mineral of particle size 20-50 microns in quantity sufficient to provide an abrasion resistant layer without interfering with visibility and (2) binder material for said mineral which binder material has the properties of withstanding the subsequent laminating conditions, being compatible with said thermosetting resin, said binder being present in an amount sufficient to bind said abrasion resistant mineral to the surface of said decorative facing sheet, and the binder-mineral layer in the dry state being permeable to said thermosetting resin; drying said coated binder mineral mixture at a temperature sufficient to enhance the bonding of said abrasion resistant material by said binder material to said decorative facing sheet, to provide an ultra-thin dry porous layer of said binder-mineral mixture thereon; impregnating said coated facing sheet with said thermosetting resin; assembling said resin impregnated and coated facing sheet over said backing layer; and subjecting said assembly to heat and pressure sufficient to effect consolidation of said backing layer and said facing sheet to thereby provide said abrasion resistant decorative laminate.
Claim 2
Independent Claim
224 words
A method of producing an abrasion resistant decorative laminate from at least one backing layer and a thermosetting resin impregnated decorative facing sheet, said laminate having enhanced abrasion resistance without an overlay layer, the method comprising: coating a decorative facing sheet with an ultra-thin wet layer of a mixture of (1) an abrasion resistant hard mineral of particle size 20-50 microns in quantity sufficient to provide an abrasion resistant layer without interfering with visibility and (2) binder material for said mineral which binder material has the properties of withstanding the subsequent laminating conditions, being compatible with said thermosetting resin, said binder being present in an amount sufficient to bind said abrasion resistant mineral to the surface of said decorative facing sheet, and the binder-mineral layer in the dry state being permeable to said thermosetting resin; drying said coated binder mineral mixture at a temperature sufficient to enhance the bonding of said abrasion resistant material by said binder material to said decorative facing sheet, to provide an ultra-thin dry porous layer of said binder-mineral mixture thereon; impregnating said coated facing sheet with said thermosetting resin; assembling said resin impregnated and coated facing sheet over said backing layer; and subjecting said assembly to heat and pressure sufficient to effect consolidation of said backing layer and said facing sheet to thereby provide said abrasion resistant decorative laminate.
Claim 3
Dependent Claim
36 words
A method in accordance with claim 1, wherein said binder material is microcrystalline cellulose and said thermosetting resin is melamine-formaldehyde resin, and said drying is carried out at a temperature of at least about 140° F.
Claim 4
Dependent Claim
19 words
A method in accordance with claim 2 wherein said abrasion resistant mineral is alumina, silica or a mixture thereof.
Claim 5
Dependent Claim
64 words
A method in accordance with claim 3 wherein said binder-mineral mixture comprises 5-10 parts by weight of microcrystalline cellulose for about 20-120 parts by weight of alumina, along with sufficient water to facilitate the coating operation, and wherein said coating is carried out at such a rate as to provide an ultra-thin coating, after drying, of thickness from 0.02 to about 0.3 mils thick.
Claim 6
Dependent Claim
31 words
A method in accordance with claim 4 wheren said finder-mineral mixture further comprises about 0.5% to about 2% by weight of an amino silane based on the weight of the alumina.
Claim 7
Dependent Claim
21 words
A method in accordance with claim 3 wherein said mixture binder-mineral mixture further contains a small quantity of non-ionic wetting agent.
Claim 8
Dependent Claim
19 words
A method in accordance with claim 3 wherein said drying is carried out at a temperature of 240°-270° F.
Claim 9
Dependent Claim
38 words
A method in accordance with claim 1 wherein said composition further comprises a silane compatible with said thermosetting resin, said silane being present in an amount sufficient to chemically bond said abrasion resistant mineral to said thermosetting resin.
Claim 10
Dependent Claim
55 words
A method of producing an abrasion resistant, high-pressure decorative laminate in accordance with claim 1 wherein said backing comprises a plurality of phenolic resin impregnated kraft paper sheets, and said thermosetting resin comprises melamine-formaldehyde resin, the heat and pressure to which said assembly is subjected to effect consolidation being about 230°-340° F. and 800-1600 p.s.i.
Claim 11
Dependent Claim
9 words
A product obtained by the process of claim 9.
Claim 12
Dependent Claim
67 words
A method in accordance with claim 9 wherein said binder material comprises predominantly is microcrystalline cellulose and said abrasion resistant mineral is alumina, said mixture comprising about 5-10 parts by weight of said microcrystalline cellulose for about 20-120 parts by weight of said alumina, and wherein said binder-mineral mixture is applied so as to provide a dry, ultrathin layer of about 0.02 to about 0.3 mils thick.
Claim 13
Dependent Claim
30 words
A method in accordance with claim 10 wherein said binder-mineral mixture further comprises 0.5 to about 2% by weight, based on the weight of said alumina, of an amino silane.
Claim 14
Dependent Claim
31 words
A method of producing an abrasion resistant low-pressure decorative laminate in accordance with claim 1, wherein said thermosetting resin is selected from the group consisting of melamine-formaldehyde resin and polyester resin.
Claim 15
Dependent Claim
118 words
A method in accordance with claim 13 wherein said backing layer comprises a wood particle panel, said thermosetting resin is melamine-formaldehyde resin, said laminating is carried out at a temperature of about 325°-350° F. and a pressure of about 175-225 p.s.i., and wherein said abrasion resistant material is alumina, silica or a mixture thereof, and said binder material comprises predominently is microcrystalline cellulose, said microcrystalline cellulose being present in an amount of about 5 to about 10 parts by weight per about about 20-120 parts by weight of said mineral, said mixture being applied to provide a dried coating of 0.02 to 0.2 mils thickness, said drying being carried out at a temperature of at least 180° F.
Claim 16
Dependent Claim
26 words
A process in accordance with claim 14 wherein said composition further comprises 0.5-2% by weight of an amino silane based on the weight of said alumina.
Claim 17
Dependent Claim
9 words
A product obtained by the process of claim 13.
Claim 18
Dependent Claim
19 words
A method in accordance with claim 1 wherein said binder material comprises a mixture of microcrystalline cellulose and carboxymethylcellulose.
References Cited (Backward Citations)
CA836522A
Cited
US2060824A
Cited
US2732325A
Cited
US2739081A
Cited
US3223579A
Cited
US3067077A
Cited
US3346443A
Cited
US3373071A
Cited
US3373070A
Cited
US3525664A
Cited
US3669727A
Cited
US3798111A
Cited
US3814647A
Cited
US3968291A
Cited
US3928706A
Cited
US4024842A
Cited
US3975572A
Cited
US4006271A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-09 | 1984-09-08 | 1985-03-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-09 | 1988-09-08 | 1989-03-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-09 | 1992-09-08 | 1993-03-10 | $7700.00 | Window Closed / Lapsed |