Fire-retardant putty-like compositions
Assignee: Dainichi Nippon Cables Ltd
•
Filing: 1979-07-17
•
Granted: 1981-03-10
•
Expires: 1999-07-17
Abstract
Abstract A composition for filling the spaces in bores penetrating walls and floors of buildings and having electric wires and cables extending therethrough or for filling the clearances at the joints of interior finishing materials of buildings. The composition comprises (a) 100 parts by weight of a curable polychloroprene in a liquid state at room temperature, (b) about 200 to about 700 parts by weight of a hydrated metallic oxide, and (c) about 20 to about 100 parts by weight of a heat-resistant fibrous material. The components (b) and (c) are contained in a combined amount of at least about 250 parts by weight per 100 parts by weight of the component (a). The composition will not soften, sag or drip in molten drops even when subjected to the high-temperature conditions of a fire, and gives a tough residual product retaining the original shape when burned and ashed, effectively preventing the spread of fire and assuring outstanding smoketightness.
Inventors
- 👤 Tamotsu Kaide
- 👤 Toshikazu Gozen
- 👤 Jinichi Taniguchi
- 👤 Yutaka Ohta
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 10:59
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/34; C08; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; Y; Y10; Y10S; Y10S260/00; Y10S260/24
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
85 words
A fire-retardant putty-like composition comprising (a) 100 parts by weight of a curable polychloroprene in a liquid state at room temperature, (b) about 200 to about 700 parts by weight of a hydrated metallic oxide, and (c) about 20 to about 100 parts by weight of a heat-resistant fibrous material, the composition containing the hydrated metallic oxide (b) and the heat-resistant fibrous material (c) in a combined amount of at least about 250 parts by weight per 100 parts by weight of the polychloroprene (a).
Claim 2
Dependent Claim
85 words
A fire-retardant putty-like composition comprising (a) 100 parts by weight of a curable polychloroprene in a liquid state at room temperature, (b) about 200 to about 700 parts by weight of a hydrated metallic oxide, and (c) about 20 to about 100 parts by weight of a heat-resistant fibrous material, the composition containing the hydrated metallic oxide (b) and the heat-resistant fibrous material (c) in a combined amount of at least about 250 parts by weight per 100 parts by weight of the polychloroprene (a).
Claim 3
Dependent Claim
17 words
A composition as defined in claim 1 wherein the hydrated metallic oxide (b) is a hydrated alumina.
Claim 4
Dependent Claim
17 words
A composition as defined in claim 1 wherein the hydrated metallic oxide (b) is a hydrated magnesia.
Claim 5
Dependent Claim
57 words
A composition as defined in claim 2 wherein the hydrated alumina comprises a portion about 10 to about 100 μm in mean particle size and another portion less than about 10 μm in mean particle size in an amount of about 10 to about 500 parts by weight per 100 parts by weight of the former portion.
Claim 6
Dependent Claim
62 words
A composition as defined in any one of claims 1 to 4 further comprising at least one material less than about 10 μm in mean particle size and selected from the group consisting of clay, zinc borate, bentonite, talc, diatomaceous earth, calcium carbonate, mica and mixtures thereof in an amount of up to about 80% by weight based on the component (b).
Claim 7
Dependent Claim
36 words
A composition as defined in any one of claims 1 to 4 wherein the heat-resistant fibrous material (c) comprises at least one fiber selected from the group consisting of glass fiber asbestos fiber and mixtures thereof.
Claim 8
Dependent Claim
40 words
A composition as defined in claim 6 wherein the heat-resistant fibrous material (c) comprises glass fiber and asbestos fiber in an amount of about 10 to about 300 parts by weight per 100 parts by weight of the glass fiber.
Claim 9
Dependent Claim
45 words
A composition as defined in any one of claims 1 to 4 wherein the liquid polychloroprene (a) has a viscosity of about 5,000 to about 500,000 at room temperature and an alkylxanthate end group in which the alkyl has 2 to about 10 carbon atoms.
Claim 10
Dependent Claim
60 words
A composition as defined in any one of claims 1 to 4 wherein the liquid polychloroprene (a) has a viscosity of about 5,000 to about 500,000 at room temperature and comprises a mixture of a polychloroprene having an alkylxanthate end group in which the alkyl has 2 to about 10 carbon atoms and a polychloroprene having a hydroxyl end group.
Claim 11
Dependent Claim
56 words
A composition as defined in any one of claims 1 to 4 wherein the liquid polychloroprene (a) has a viscosity of about 5,000 to about 500,000 at room temperature and a hydroxyl end group and contains about 0.5 to about 20 parts by weight of a curing agent per 100 parts by weight of the polychloroprene.
Claim 12
Dependent Claim
34 words
A composition as defined in any one of claims 1 to 4 further comprising up to about 100 parts by weight of a flame retardant per 100 parts by weight of the component (a).
Claim 13
Dependent Claim
33 words
A composition as defined in any one of claims 1 to 4 further comprising up to about 50 parts by weight of a plasticizer per 100 parts by weight of the component (a).
Claim 14
Dependent Claim
40 words
A composition as defined in any one of claims 1 to 4 further comprising up to about 30 parts by weight of a silane coupling agent or a titanate coupling agent per 100 parts by weight of the component (a).
Claim 15
Dependent Claim
38 words
A composition as defined in any one of claims 1 to 4 which has a cone penetration value (mm/150 g, 5 sec, at 20° C.) of about 2 to about 40 as determined according to JIS A 5752-1966.
Claim 16
Dependent Claim
31 words
A composition as defined in claim 5 wherein the heat-resistant fibrous material (c) comprises at least one fiber selected from the group consisting of glass fiber, asbestos fiber, and mixtures thereof.
Claim 17
Dependent Claim
40 words
A composition as defined in claim 15 wherein the heat-resistant fibrous material (c) comprises glass fiber and asbestos fiber in an amount of about 10 to about 300 parts by weight per 100 parts by weight of the glass fiber.
Claim 18
Dependent Claim
40 words
A composition as defined in claim 5 wherein the liquid polychloroprene (a) has a viscosity of about 5,000 to about 500,000 at room temperature and an alkylxanthate end group in which the alkyl has 2 to about 10 carbon atoms.
Claim 19
Dependent Claim
40 words
A composition as defined in claim 6 wherein the liquid polychloroprene (a) has a viscosity of about 5,000 to about 500,000 at room temperature and an alkylxanthate end group in which the alkyl has 2 to about 10 carbon atoms.
Claim 20
Dependent Claim
40 words
A composition as defined in claim 7 wherein the liquid polychloroprene (a) has a viscosity of about 5,000 to about 500,000 at room temperature and an alkylxanthate end group in which the alkyl has 2 to about 10 carbon atoms.
Claim 21
Dependent Claim
55 words
A composition as defined in claim 5 wherein the liquid polychloroprene (a) has a viscosity of about 5,000 to about 500,000 at room temperature and comprises a mixture of a polychloroprene having an alkylxanthate end group in which the alkyl has 2 to about 10 carbon atoms and a polychloroprene having a hydroxyl end group.
Claim 22
Dependent Claim
55 words
A composition as defined in claim 6 wherein the liquid polychloroprene (a) has a viscosity of about 5,000 to about 500,000 at room temperature and comprises a mixture of a polychloroprene having an alkylxanthate end group in which the alkyl has 2 to about 10 carbon atoms and a polychloroprene having a hydroxyl end group.
Claim 23
Dependent Claim
55 words
A composition as defined in claim 7 wherein the liquid polychloroprene (a) has a viscosity of about 5,000 to about 500,000 at room temperature and comprises a mixture of a polychloroprene having an alkylxanthate end group in which the alkyl has 2 to about 10 carbon atoms and a polychloroprene having a hydroxyl end group.
Claim 24
Dependent Claim
51 words
A composition as defined in claim 5 wherein the liquid polychloroprene (a) has a viscosity of about 5,000 to about 500,000 at room temperature and a hydroxyl end group and contains about 0.5 to about 20 parts by weight of a curing agent per 100 parts by weight of the polychloroprene.
Claim 25
Dependent Claim
51 words
A composition as defined in claim 6 wherein the liquid polychloroprene (a) has a viscosity of about 5,000 to about 500,000 at room temperature and a hydroxyl end group and contains about 0.5 to about 20 parts by weight of a curing agent per 100 parts by weight of the polychloroprene.
Claim 26
Dependent Claim
51 words
A composition as defined in claim 7 wherein the liquid polychloroprene (a) has a viscosity of about 5,000 to about 500,000 at room temperature and a hydroxyl end group and contains about 0.5 to about 20 parts by weight of a curing agent per 100 parts by weight of the polychloroprene.
References Cited (Backward Citations)
US3843592A
Cited
US4138537A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-09 | 1984-09-08 | 1985-03-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-09 | 1988-09-08 | 1989-03-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-09 | 1992-09-08 | 1993-03-10 | $7700.00 | Window Closed / Lapsed |