Process for rendering polyester hollow bodies gastight
Assignee: Rhone Poulenc Industries SA
•
Filing: 1979-02-08
•
Granted: 1981-03-03
•
Expires: 1999-02-08
Abstract
Abstract The invention pertains to a process for producing bioriented polyester hollow bodies characterized by good gas and flavor tightness, wherein one wall of a preform is coated with an aqueous composition consisting of at least two incompatible polymers, one of which is a water soluble polyvinyl alcohol and the other, a polymer latex with low water sensitivity; the coating is dried and the preform is bidrawn-blown.
Inventors
- 👤 Gilbert Roullet
- 👤 Pierre Legrand
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 21:47
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/02; B05D7/22; B29; B29C; B29C49/00; B29C49/22; B29B; B29B11/00; B29B11/06; B29B11/08; B29B11/10; B29B11/12; B29B11/14; B29C49/42; B29C49/78; B29C49/786; B29C2049/7864; B29C2049/78645; B29C2949/00; B29C2949/07; B29C2949/0715; B29C2949/081; B29C2949/0811; B29C2949/0819; B29C2949/082; B29C2949/0829; B29C2949/20; B29C2949/22; B29C2949/24; B29C2949/30; B29C2949/3016; B29C2949/302; B29C2949/3024; B29C2949/3026; B29C2949/3032; B29C2949/3041; B29C2949/3056; B29C2949/3064; B29C2949/3066; B29C2949/3074; B29C2949/308; B29C49/071; B29K; B29K2009/00; B29K2009/06; B29K2027/00; B29K2027/08; B29K2029/00; B29K2029/04; B29K2105/00; B29K2105/0005; B29K2105/0008; B29K2105/0038; B29K2105/0044; B29K2105/0047; B29K2105/005; B29K2105/06; B29K2105/16; B29K2105/25; B29K2105/253; B29K2105/258; B29K2667/00; B29L; B29L2031/00; B29L2031/712; B29L2031/7158; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1379; Y10T428/31504; Y10T428/31786; Y10T428/31797; Y10T428/31855; Y10T428/31931; Y10T428/31935; Y10T428/31938
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
140 words
In a process for producing bioriented polyester composite hollow bodies which includes the steps of making a preform, transferring the preform into a mold, bidrawing-blowing the preform under biorientation conditions to produce a hollow body, followed by cooling and removing the hollow body from the mold, the improvement comprising coating at least one wall of the preform with an aqueous composition composed of at least two imcompatible polymers, one of which is a polyvinyl alcohol in solution in water, and the other or others of which is a latex of relatively water insensitive polymers, in which the weight ratio of polyvinyl alcohol/latex polymer is between 0.4 and 3, to provide a two-phase system in which the polyvinyl alcohol solution forms a continuous phase and the water insensitive polymer is in the dispersed phase, drying the coating, followed by said bidrawing-blowing.
Claim 2
Dependent Claim
140 words
In a process for producing bioriented polyester composite hollow bodies which includes the steps of making a preform, transferring the preform into a mold, bidrawing-blowing the preform under biorientation conditions to produce a hollow body, followed by cooling and removing the hollow body from the mold, the improvement comprising coating at least one wall of the preform with an aqueous composition composed of at least two imcompatible polymers, one of which is a polyvinyl alcohol in solution in water, and the other or others of which is a latex of relatively water insensitive polymers, in which the weight ratio of polyvinyl alcohol/latex polymer is between 0.4 and 3, to provide a two-phase system in which the polyvinyl alcohol solution forms a continuous phase and the water insensitive polymer is in the dispersed phase, drying the coating, followed by said bidrawing-blowing.
Claim 3
Dependent Claim
34 words
Process as claimed in claim 1, in which the viscosity of the polyvinyl alcohol is less than 20 cp (in solution at 4% in water) and the ester index is between 2 and 150.
Claim 4
Dependent Claim
44 words
Process as claimed in claim 1, in which the polymer latex is selected from the group consisting of styrene-butadiene, styrene-acrylate base latexes, unsaturated carboxylic acid aryl or alkyl ester base latexes, unsaturated nitrile base latexes, vinyl halogenide base latexes and vinyl acetate base latexes.
Claim 5
Dependent Claim
17 words
Process as claimed in claim 1, in which the polymer latex is a vinylidene chloride copolymer latex.
Claim 6
Dependent Claim
15 words
Process as claimed in claim 1, in which the coating composition includes a cross-linking agent.
Claim 7
Dependent Claim
54 words
Process as claimed in claim 1, in which the coating composition is composed of a 5-25% by weight polyvinyl alcohol aqueous solution and at least one relatively water insensitive polymer latex having a dry material content comprised between 40 and 60%, and in which the polyvinyl alcohol/latex polymer ratio is between 0.4 and 3.
Claim 8
Dependent Claim
22 words
Process as claimed in claim 1, in which the weight of dry coating on the preform is between 10 and 100 g/m2.
Claim 9
Dependent Claim
15 words
Process as claimed in claim 1, in which several coats are applied on the preform.
Claim 10
Dependent Claim
33 words
Process as claimed in claim 1, in which the coating or coatings is dried up to a residual moisture content between 0.5 and 5%, and post-drying the hollow body after it is blown.
Claim 11
Dependent Claim
32 words
Process as claimed in claim 9, which includes the step of heat treatment of the coating after bidrawing and blowing of the hollow body at a temperature between 80° and 200° C.
Claim 12
Dependent Claim
35 words
Process as claimed in claim 10, in which the heat treatment is carried out first at a temperature between 150° and 200° and then at a temperature which promotes the crystallization of the latex polymer.
Claim 13
Dependent Claim
41 words
Bioriented polyester composite hollow bodies, produced by the process of claim 1, having a coating with a two-phase structure formed of a bioriented continuous phase composed of a moisture insensitive polymer and a laminar, bioriented discontinuous phase composed of polyvinyl alcohol.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-02 | 1984-09-01 | 1985-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-02 | 1988-09-01 | 1989-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-02 | 1992-09-01 | 1993-03-03 | $7700.00 | Window Closed / Lapsed |