US4254007A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Electrical insulating composition
Assignee: General Electric Co
•
Filing: 1979-09-13
•
Granted: 1981-03-03
•
Expires: 1999-09-13
Abstract
Abstract An electrically insulating wire coating material comprised of the heat cured product of a mixture of polyvinylacetal and phenol-aldehyde resins, or a mixture of these resins with epoxy resins, and a catalyst from the special metal containing group of cyclic organic compounds known as chelates and which can be further defined as being a non-ionic inner complex salt. These materials give insulating coatings with improved flexibility and thermal aging properties.
Inventors
- 👤 Ralph G. Flowers
- 👤 William A. Fessler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 06:41
CPC Classifications
C; C09; C09D; C09D129/00; C09D129/14
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
64 words
An electrically insulating wire coating enamel consisting essentially of a mixture of polyvinylacetal resin and phenolic resin and including from 0.15 to 1.9 percent by weight of an inner complex salt which comprises a bidentate chelating agent having one acid and one coordinating group wherein the chelating agent includes a metal having a coordination number equal to twice the principle valence of the metal.
Claim 2
Dependent Claim
64 words
An electrically insulating wire coating enamel consisting essentially of a mixture of polyvinylacetal resin and phenolic resin and including from 0.15 to 1.9 percent by weight of an inner complex salt which comprises a bidentate chelating agent having one acid and one coordinating group wherein the chelating agent includes a metal having a coordination number equal to twice the principle valence of the metal.
Claim 3
Dependent Claim
23 words
The wire coating enamel of claim 1 wherein the inner complex of salt is selected from the group consisting of acetylacetonates and glycinates.
Claim 4
Dependent Claim
21 words
The wire coating enamel of claim 2 wherein the metal is selected from the group consisting of nickel, aluminum and zinc.
Claim 5
Dependent Claim
23 words
The wire coating enamel of claim 1 wherein the catalyst is selected from the group consisting of aluminum, nickel, titanium and zinc acetylacetonates.
Claim 6
Dependent Claim
13 words
The wire coating enamel of claim 1 wherein the catalyst comprises cooper glycinate.
Claim 7
Dependent Claim
13 words
The wire coating enamel of claim 1 wherein the catalyst comprises nickel dimethylglyoxime.
Claim 8
Dependent Claim
13 words
The wire coating enamel composition of claim 1 further including an epoxy resin.
Claim 9
Independent Claim
70 words
A method of preparing wire coating enamels comprising the steps of: dissolving a mixture of polyvinylacetal resin, phenolic resin in a solvent, with from 0.l5 percent to 1.9 percent of said resins of an inner complex salt which comprises a bidentate chelating agent having one acid and one coordinating group wherein the chelating agent includes a metal having a coordination number equal to twice the principle valence of the metal.
Claim 10
Independent Claim
70 words
A method of preparing wire coating enamels comprising the steps of: dissolving a mixture of polyvinylacetal resin, phenolic resin in a solvent, with from 0.l5 percent to 1.9 percent of said resins of an inner complex salt which comprises a bidentate chelating agent having one acid and one coordinating group wherein the chelating agent includes a metal having a coordination number equal to twice the principle valence of the metal.
Claim 11
Independent Claim
39 words
A method of preparing a wire coating enamel comprising the steps of: dissolving 452 parts polyvinylacetal resin 226 parts of phenolic resin, 18.9 parts hexamethoxymethylmelamine and 19.8 parts zinc acetylacetonate in a solvent mixture consisting of xylene and cresol.
Claim 12
Independent Claim
39 words
A method of preparing a wire coating enamel comprising the steps of: dissolving 452 parts polyvinylacetal resin 226 parts of phenolic resin, 18.9 parts hexamethoxymethylmelamine and 19.8 parts zinc acetylacetonate in a solvent mixture consisting of xylene and cresol.
Claim 13
Independent Claim
37 words
A method of preparing insulating wire coating enamels comprising the steps of dissolving 452 parts polyvinylacetal resin, 226 parts phenolic resin, 18.9 parts hexamethoxymethylmelamine and 19.3 parts nickel acetylacetonate in a solvent mixture of xylene and cresol.
Claim 14
Independent Claim
37 words
A method of preparing insulating wire coating enamels comprising the steps of dissolving 452 parts polyvinylacetal resin, 226 parts phenolic resin, 18.9 parts hexamethoxymethylmelamine and 19.3 parts nickel acetylacetonate in a solvent mixture of xylene and cresol.
Claim 15
Independent Claim
42 words
A method of preparing insulating wire coating enamels comprising the steps of: dissolving 4.7 parts polyvinylacetal resin, 3.1 parts phenolic resin, 2.0 parts epoxy resin and from 0.0l to 0.18 parts of metal acetylacetonate in a solvent mixture of xylene and cresol.
Claim 16
Independent Claim
42 words
A method of preparing insulating wire coating enamels comprising the steps of: dissolving 4.7 parts polyvinylacetal resin, 3.1 parts phenolic resin, 2.0 parts epoxy resin and from 0.0l to 0.18 parts of metal acetylacetonate in a solvent mixture of xylene and cresol.
Claim 17
Independent Claim
38 words
A method of preparing insulating wire coating enamels comprising the steps of: dissolving 4.7 parts polyvinylacetal resin, 3.1 parts phenolic resin, 2.0 parts epoxy resin and 0.08 parts titanium acetylacetonate in a solvent mixture of xylene and cresol.
Claim 18
Independent Claim
38 words
A method of preparing insulating wire coating enamels comprising the steps of: dissolving 4.7 parts polyvinylacetal resin, 3.1 parts phenolic resin, 2.0 parts epoxy resin and 0.08 parts titanium acetylacetonate in a solvent mixture of xylene and cresol.
Claim 19
Dependent Claim
17 words
The method of claim 11 wherein the xylene comprises 10 parts and the cresol comprises 30 parts.
References Cited (Backward Citations)
US2917416A
Cited
US2917483A
Cited
DE1065118B
Cited
US3141005A
Cited
US3471589A
Cited
US3442834A
Cited
US3617969A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-02 | 1984-09-01 | 1985-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-02 | 1988-09-01 | 1989-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-02 | 1992-09-01 | 1993-03-03 | $7700.00 | Window Closed / Lapsed |