Electrolytic process for producing potassium hydroxide
Assignee: Olin Corp
•
Filing: 1979-06-01
•
Granted: 1981-03-03
•
Expires: 1999-06-01
Abstract
Abstract Current efficiency in an electrolytic membrane cell for the production of concentrated potassium hydroxide is considerably increased by employing in the electrolytic membrane cell a membrane selected from a group consisting of an amine modified perfluorosulfonic acid membrane such as a primary amine, diamine, or polyamine modified perfluorosulfonic acid membrane, and a laminated perfluorosulfonic acid acid membrane, and a laminated perfluorosulfonic acid membrane comprised of at least two unmodified perfluorosulfonic acid membranes of different thickness and different equivalent weight.
Inventors
- 👤 Richard W. Lynch
- 👤 Garland E. Hilliard
- 👤 Ronald L. Dotson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 23:50
CPC Classifications
C; C25; C25B; C25B1/00; C25B1/01; C25B1/34; C25B1/46; C08; C08J; C08J5/00; C08J5/20; C08J5/22; C08J5/2206; C08J5/2275; C08J5/2281; C08J5/2287; C08J5/2293; C08J2327/00; C08J2327/02; C08J2327/12; C08J2327/18
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
129 words
In a process for the preparation of potassium hydroxide, chlorine and hydrogen in an electrolytic cell by electrolysis of potassium chloride brine, said cell having an anolyte chamber containing an anode and a catholyte chamber containing a cathode and wherein said anolyte chamber is separated from said catholyte chamber by a cationic permselective membrane, the improvement which comprises employing as said membrane a membrane selected from the group consisting of: (i) an amine substituted perfluorosulfonic acid membrane, and (ii) a single film laminate membrane comprised of at least two perfluorosulfonic acid membranes, and wherein the potassium hydroxide concentration in said catholyte chamber is in the range from about 300 to about 500 grams KOH per liter and wherein said membrane is laminated to a fabric of polytetrafluoroethylene and rayon.
Claim 2
Dependent Claim
129 words
In a process for the preparation of potassium hydroxide, chlorine and hydrogen in an electrolytic cell by electrolysis of potassium chloride brine, said cell having an anolyte chamber containing an anode and a catholyte chamber containing a cathode and wherein said anolyte chamber is separated from said catholyte chamber by a cationic permselective membrane, the improvement which comprises employing as said membrane a membrane selected from the group consisting of: (i) an amine substituted perfluorosulfonic acid membrane, and (ii) a single film laminate membrane comprised of at least two perfluorosulfonic acid membranes, and wherein the potassium hydroxide concentration in said catholyte chamber is in the range from about 300 to about 500 grams KOH per liter and wherein said membrane is laminated to a fabric of polytetrafluoroethylene and rayon.
Claim 3
Dependent Claim
16 words
The process of claim 1, wherein said amine substituted membrane is a primary amine substituted membrane.
Claim 4
Dependent Claim
15 words
The process of claim 1, wherein said amine substituted membrane is a diamine substituted membrane.
Claim 5
Dependent Claim
15 words
The process of claim 1, wherein said amine substituted membrane is a polyamine substituted membrane.
Claim 6
Dependent Claim
35 words
The process of claims 3 or 4 wherein said diamine and said polyamine is comprised of at least two amino groups with one primary amino group and the second amino group either primary or secondary.
Claim 7
Dependent Claim
36 words
The process of claim 5, wherein said amine substituted membrane is prepared by reacting said amine with a precursor sulfonyl fluoride polymer wherein pendant sulfonyl fluoride groups react to form N-monosubstituted sulfonamido groups or salts thereof.
Claim 8
Dependent Claim
24 words
The process of claim 6, wherein the thickness of said amine substituted membrane is in the range from about 4 to about 10 mils.
Claim 9
Dependent Claim
24 words
The process of claim 7 wherein the thickness of said amine substituted polymer is in the range from about 5 to about 9 mils.
Claim 10
Dependent Claim
29 words
The process of claim 8 wherein said amine is reacted with said precursor sulfonyl fluoride polymer to a depth in the range from about 0.5 to about 7 mils.
Claim 11
Dependent Claim
29 words
The process of claim 9 wherein said amine is reacted with said precursor sulfonyl fluoride polymer to a depth in the range from about 1 to about 2 mils.
Claim 12
Dependent Claim
11 words
The process of claim 10 wherein said diamine is ethylene diamine.
Claim 13
Dependent Claim
23 words
The process of claim 1, wherein said laminate of perfluorosulfonic acid membranes is comprised of at least two unmodified homogeneous perfluorosulfonic acid films.
Claim 14
Dependent Claim
63 words
The process of claim 12, wherein said laminated perfluorosulfonic acid membranes are comprised of a first membrane having a thickness in the range from about 1 to about 2 mils, of about 1500 equivalent weight perfluorosulfonic acid resin, and the second membrane has a thickness in the range from about 4 to about 5 mils of about 1100 equivalent weight perfluorosulfonic acid resin.
Claim 15
Dependent Claim
52 words
The process of claim 13, wherein said laminate of perfluorosulfonic acid membrane is comprised of a first membrane having a thickness of about 2 mils of about 1500 equivalent weight perfluorosulfonic acid resin and the second membrane has a thickness of about 4 mils of about 1100 equivalent weight perfluorosulfonic acid resin.
Claim 16
Dependent Claim
52 words
The process of claim 13, wherein said laminate of perfluorosulfonic acid membrane is comprised of a first membrane having a thickness of about 1 mil of about 1500 equivalent weight perfluorosulfonic acid resin and the second membrane has a thickness of about 5 mils of about 1100 equivalent weight perfluorosulfonic acid resin.
Claim 17
Dependent Claim
52 words
The process of claim 13, wherein said laminate of perfluorosulfonic acid membrane is comprised of a first membrane having a thickness of about 1.5 mils of about 1500 equivalent weight perfluorosulfonic acid resin and the second membrane has a thickness of about 5 mils of about 1100 equivalent weight perfluorosulfonic acid resin.
Claim 18
Dependent Claim
33 words
The process of claim 1, wherein said membrane is a diamine substituted membrane chemically modified on one side by amine to a depth in the range from about 0.5 to about 7 mils.
Claim 19
Dependent Claim
53 words
The process of claim 17, wherein said membrane is a diamine substituted membrane comprised of a homogeneous film about 7 mils thick, of about 1150 equivalent weight perfluorosulfonic acid resin which has been chemically modified on one side by ethylene diamine converting a depth of about 1.5 mils of the polymer to perfluorosulfonamide.
Claim 20
Dependent Claim
57 words
The process of claim 18, wherein said fabric is characterized by having a basic weave pattern, a thread count of about 6×6 polytetrafluoroethylene, 24×24 rayon per centimeter, a denier of about 200 polytetrafluoroethylene and 50 rayon, a fabric thickness of about 4.6 mils and an open area (Optical) of about 70 percent by volume after rayon removed.
Claim 21
Dependent Claim
55 words
The process of claim 18, wherein said diamine substituted membrane is a perfluorosulfonic acid polymer comprised of a homogeneous film about 7 mils thick, of about 1200 equivalent weight perfluorosulfonic acid resin which has been chemically modified on one side by ethylene diamine converting a depth of about 1.5 mils of the polymer to perfluorosulfonamide.
Claim 22
Dependent Claim
55 words
The process of claim 18, wherein said diamine substituted membrane is a perfluorosulfonic acid polymer comprised of a homogeneous film about 7 mils thick, of about 1150 equivalent weight perfluorosulfonic acid resin which has been chemically modified on one side by ethylene diamine converting a depth of about 1.2 mils of the polymer to perfluorosulfonamide.
Claim 23
Dependent Claim
105 words
In a process for the preparation of potassium hydroxide, chlorine and hydrogen in an electrolytic cell by electrolysis of potassium chloride brine, said cell having an anolyte chamber containing an anode and a catholyte chamber containing a cathode and wherein said anolyte chamber is separated from said catholyte chamber by a cationic permselective membrane, the improvement which comprises employing as said membrane a perfluorosulfonic acid membrane modified on one side with an amine and having the unmodified side laminated to a fabric of polytetrafluoroethylene and rayon wherein the concentration of potassium hydroxide is in the range from about 300 to about 500 grams per liter.
Claim 24
Dependent Claim
105 words
In a process for the preparation of potassium hydroxide, chlorine and hydrogen in an electrolytic cell by electrolysis of potassium chloride brine, said cell having an anolyte chamber containing an anode and a catholyte chamber containing a cathode and wherein said anolyte chamber is separated from said catholyte chamber by a cationic permselective membrane, the improvement which comprises employing as said membrane a perfluorosulfonic acid membrane modified on one side with an amine and having the unmodified side laminated to a fabric of polytetrafluoroethylene and rayon wherein the concentration of potassium hydroxide is in the range from about 300 to about 500 grams per liter.
Claim 25
Dependent Claim
19 words
The process of claim 22, wherein said depth is in the range from about 1 to about 2 mils.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-02 | 1984-09-01 | 1985-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-02 | 1988-09-01 | 1989-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-02 | 1992-09-01 | 1993-03-03 | $7700.00 | Window Closed / Lapsed |