Method of producing low voltage field emission cathode structure
Assignee: Georgia Tech Research Institute
•
Filing: 1979-06-14
•
Granted: 1981-03-03
•
Expires: 1999-06-14
Abstract
Abstract A method of making a low voltage field device utilizing a preferentially etched unidirectionally solidified composite as the substrate. In the process, the composite is etched so that the electrically conducting rod-like or fiber phase protrudes above the matrix phase. The tip of the exposed fiber phase may be processed further to provide a rounded or needle-like geometry. Next, a layer of insulating material is deposited in a direction approximately parallel to the axes of the fibers to cause the formation of cone-like deposits of insulating material on the fiber tips which shadow the deposit on the matrix around the fibers and produce conical holes in the layer of insulating material about the fibers. Then, an electrically conductive film is deposited in approximately the same direction to produce on the insulating layer a cellular grid having openings corresponding in number and distribution to the fiber sites. Lastly, the cones of insulating material are removed from the fibers.
Inventors
- 👤 Joe K. Cochran, Jr.
- 👤 Jae-Do Lee
- 👤 Alan T. Chapman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 17:45
CPC Classifications
H; H01; H01J; H01J9/00; H01J9/02; H01J9/022; H01J9/025
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
148 words
A method of making a low voltage field emission device comprising the steps of: providing an oxide-metal composite which consists of a plurality of metallic fibers unidirectionally aligned in an oxide matrix; etching the oxide matrix to a desired depth to expose the fibers; forming a needle-like tip on the fibers; depositing in a direction approximately parallel to the axes of the fibers a layer of insulating material on the oxide matrix to cause the formation of inverse truncated cones of insulating material on the fibers and holes in the layer of insulating material about the fibers; depositing in a direction approximately parallel to the axes of the fibers a metal film on the insulating layer and the insulating cones to produce a cellular grid whose openings correspond in number and distribution to the sites of the fibers; and removing the cones of insulating material from the fibers.
Claim 2
Independent Claim
148 words
A method of making a low voltage field emission device comprising the steps of: providing an oxide-metal composite which consists of a plurality of metallic fibers unidirectionally aligned in an oxide matrix; etching the oxide matrix to a desired depth to expose the fibers; forming a needle-like tip on the fibers; depositing in a direction approximately parallel to the axes of the fibers a layer of insulating material on the oxide matrix to cause the formation of inverse truncated cones of insulating material on the fibers and holes in the layer of insulating material about the fibers; depositing in a direction approximately parallel to the axes of the fibers a metal film on the insulating layer and the insulating cones to produce a cellular grid whose openings correspond in number and distribution to the sites of the fibers; and removing the cones of insulating material from the fibers.
Claim 3
Dependent Claim
40 words
The method of making a low voltage field emission device recited in claim 1 wherein the providing step includes: providing an oxide-metal composite which consists of a plurality of single crystal W metallic fibers undirectionally aligned in an oxide matrix.
Claim 4
Dependent Claim
40 words
The method of making a low voltage field emission device recited in claim 1 wherein the providing step includes: providing an oxide-metal composite which consists of a plurality of single crystal Mo metallic fibers unidirectionally aligned in an oxide matrix.
Claim 5
Dependent Claim
38 words
The method of making a low voltage field emission device recited in claim 1 wherein the providing step includes: providing an oxide-metal composite which consists of a plurality of metallic fibers unidirectionally aligned in an UO 2 matrix.
Claim 6
Dependent Claim
39 words
The method of making a low voltage field emission device recited in claim 1 wherein the providing step includes: providing a unidirectionally solidified insitu composite which consists of a plurality of electrically conducting fibers unidirectionally aligned in a matrix.
Claim 7
Dependent Claim
70 words
The method of making a low voltage field emission device recited in claim 1 wherein the insulating material depositing step includes: depositing in a direction approximately parallel to the axes of emitters exposed above a matrix a layer of electrically insulating material to cause the formation of inverse truncated cones of insulating material on the emitters and holes about the emitters in the layer of insulating material on the matrix.
Claim 8
Dependent Claim
73 words
The method of making a low voltage field emission device recited in claim 1 wherein the insulating material depositing step includes: depositing in a direction approximately parallel to the axes of the fibers a layer of Al 2 O 3 or SiO 2 insulating material on the matrix to cause the formation of inverse truncated cones of insulating material on the fibers and holes in the layer of insulating material about the fibers.
Claim 9
Dependent Claim
58 words
The method of making a low voltage field emission device recited in claim 1 wherein the metal film depositing step includes: depositing in a direction parallel to the axes of the fibers a Mo metal film on the insulating layer to produce a cellular grid whose openings correspond in number and distribution to the sites of the fibers.
Claim 10
Dependent Claim
39 words
The method of making a low voltage field emission device recited in claim 1 wherein the removing step includes the step of: ultrasonically vibrating the oxide-metal composite to remove the vapor deposited cones of insulating material from the fibers.
Claim 11
Dependent Claim
33 words
The method of making a low voltage field emission device recited in claim 1 wherein the step of forming includes the step of: ion milling the fibers to form a needle-like tip thereon.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-02 | 1984-09-01 | 1985-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-02 | 1988-09-01 | 1989-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-02 | 1992-09-01 | 1993-03-03 | $7700.00 | Window Closed / Lapsed |