Process for forming an anodized film over the surface of aluminum substrates
Assignee: Individual
•
Filing: 1979-04-25
•
Granted: 1981-02-24
•
Expires: 1999-04-25
Abstract
Abstract Anodized films having an aesthetic value are formed over the surface of aluminum or aluminum alloy substrates by anodizing the substrate in an electrolyte solution containing 50-60% of sulfuric acid and oxalic acid or nickel sulfate, at a bath temperature of 18° to 30° C. and a current density of 1 to 10 A/dm 2 . The oxide film formed by this method has a porcelain-like texture or feel or the appearance of a meshwork thereof or a grainy texture resembling wood, leather or sand, depending upon the nature of the base or substrate metal and the anodizing conditions employed.
Inventors
- 👤 Setsuo Tomita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 19:27
CPC Classifications
C; C25; C25D; C25D11/00; C25D11/02; C25D11/04; C25D11/14
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
69 words
A method for forming an anodized film of aesthetic value over the surface of an aluminum or aluminum alloy substrate which comprises anodizing said aluminum or aluminum alloy substrate in an aqueouselectrolyte solution consisting essentially of 50-60% of sulfuric acid; 1-3% of nickel sulfate additive; and water, at a bath temperature of from 18° to 30° C. and a current density of from 1 to 10 A/dm 2 .
Claim 2
Independent Claim
69 words
A method for forming an anodized film of aesthetic value over the surface of an aluminum or aluminum alloy substrate which comprises anodizing said aluminum or aluminum alloy substrate in an aqueouselectrolyte solution consisting essentially of 50-60% of sulfuric acid; 1-3% of nickel sulfate additive; and water, at a bath temperature of from 18° to 30° C. and a current density of from 1 to 10 A/dm 2 .
Claim 3
Dependent Claim
24 words
A method as claimed in claim 1, wherein the anodizing is performed at a current density of from 3 to 5 A/dm 2 .
Claim 4
Dependent Claim
19 words
A method as claimed in claim 1, wherein the anodizing is performed at a temperature of about 25° C.
Claim 5
Dependent Claim
24 words
A method as claimed in claim 1, wherein the anodizing is performed until the thickness of the film formed is in excess of 20μ.
Claim 6
Dependent Claim
21 words
An aluminum or aluminum alloy substrate having an oxide film over the surface thereof prepared by the method of claim 1.
References Cited (Backward Citations)
GB409679A
Cited
US2963409A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-02-24 | 1984-08-25 | 1985-02-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-02-24 | 1988-08-25 | 1989-02-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-02-24 | 1992-08-25 | 1993-02-24 | $7700.00 | Window Closed / Lapsed |