Method for reticulating an adhesive to conform to a surface of an apertured workpiece
Assignee: Boeing Co
•
Filing: 1978-08-24
•
Granted: 1981-02-10
•
Expires: 1998-08-24
Abstract
Abstract A adhesive sheet or film placed in contact with a surface network formed by the edges of the cell walls of a honeycomb core panel is reticulated and conformed to the shape of the surface network to form a bead of adhesive on the surface network and the contiguous portions of the cell walls without depositing excess adhesive onto the interior cell walls. A method for reticulating the adhesive includes the steps of (a) contacting the surface network of a honeycomb core panel with a continuous film of adhesive material, (b) heating the film overlying at least a portion of the surface network to cause the heated portion of the adhesive film to adhere to the surface network and to reduce the cohesive strength of the heated portion of the adhesive film covering the honeycomb cells, and (c) thereafter injecting a pressurized gas through the cells of the honeycomb core toward the heated portion of the adhesive film, causing the heated portion of the film covering each of the honeycomb cells to distend outwardly away from the surface of the honeycomb core and to rupture. The surface tension of the heated adhesive film causes the ruptured portions of the film to contract toward the surface network leaving a bead of adhesive covering the surface network and the portion of the honeycomb cell walls contiguous to the surface network.
Inventors
- 👤 Paul H. Wilson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 18:40
CPC Classifications
B; B29; B29D; B29D24/00; B29D24/002; B29D24/005; B29C; B29C65/00; B29C65/48; B29C65/52; B29C66/00; B29C66/70; B29C66/72; B29C66/725; B29C66/7254; B29C66/90; B29C66/91; B29C66/912; B29C66/9121; B29C66/914; B29C66/9141; B29C66/91431; B29C66/9161; B29C66/91641; B29C66/91651; B29C66/91653; B29C66/96; B29C66/961; B31; B31D; B31D3/00; B31D3/02; B31D3/0292; C; C09; C09J; C09J5/00; B29C65/4805; B29C65/483; B29C65/526; B29C66/967; B29C66/9672; B29L; B29L2031/00; B29L2031/60; B29L2031/601; B29L2031/608; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1003; Y10T156/1052; Y10T156/1056; Y10T428/00; Y10T428/24; Y10T428/24149
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
205 words
A method for reticulating an adhesive on a discontinuous surface of a workpiece prior to adhering a second workpiece to said surface, said discontinuous surface including a plurality of orifices extending from said surface or said workpiece, said method comprising the steps of: (a) contacting said surface with a continuous film of adhesive so as to cover said surface and said orifices, said film of adhesive being characterized by a substantially uniform thickness, by a loss of cohesive strength upon heating, and by a tendency to contract when ruptured, (b) causing said film to adhere to at least a portion of said surface of said workpiece surrounding said orifices, (c) heating said film to a temperature lower than the melting temperature of said film to reduce the cohesive strength of said film, and, while maintaining the temperature of said film below the melting temperature of said film exerting a fluid pressure in said orifices to cause the portion of said film covering said orifices to distend outwardly away from said surface and to form bubbles, said fluid pressure being exerted until said bubbles rupture and said film contracts toward said surface to leave an adhesive bead on said surface adjacent the periphery of said orifices.
Claim 2
Independent Claim
205 words
A method for reticulating an adhesive on a discontinuous surface of a workpiece prior to adhering a second workpiece to said surface, said discontinuous surface including a plurality of orifices extending from said surface or said workpiece, said method comprising the steps of: (a) contacting said surface with a continuous film of adhesive so as to cover said surface and said orifices, said film of adhesive being characterized by a substantially uniform thickness, by a loss of cohesive strength upon heating, and by a tendency to contract when ruptured, (b) causing said film to adhere to at least a portion of said surface of said workpiece surrounding said orifices, (c) heating said film to a temperature lower than the melting temperature of said film to reduce the cohesive strength of said film, and, while maintaining the temperature of said film below the melting temperature of said film exerting a fluid pressure in said orifices to cause the portion of said film covering said orifices to distend outwardly away from said surface and to form bubbles, said fluid pressure being exerted until said bubbles rupture and said film contracts toward said surface to leave an adhesive bead on said surface adjacent the periphery of said orifices.
Claim 3
Dependent Claim
51 words
The method of claim 1 wherein said film comprises a thermosetting adhesive resin, and wherein said film is caused to adhere to said surface surrounding said apertures by heating said film to a temperature sufficiently high to cause said film to become tacky and adhere to said surface surrounding said orifices.
Claim 4
Dependent Claim
16 words
The method of claim 2 wherein said resin comprises an epoxy resin or a polyimide resin.
Claim 5
Dependent Claim
30 words
The method of claim 1 wherein said workpiece is a honeycomb core, said surface comprising the surface network formed by the edges of the cell walls of the honeycomb core.
Claim 6
Dependent Claim
94 words
The method of claim 1 wherein the portion of the surface of said workpiece being subjected to said fluid pressure exerting step and said heating step is supported in a substantially horizontal orientation, said film being heated to a temperature sufficient to cause said film covering said orifices to sag into said orifices, said fluid pressure being exerted by injecting a fluid stream into said orifice, said fluid stream being directed upwardly and outwardly from said surface of said workpiece so as to cause said film covering said apertures to distend outwardly and rupture.
Claim 7
Independent Claim
221 words
A method for forming an adhesive bead on the surface of a workpiece surrounding an aperture in the surface of said workpiece and on the walls of the aperture contiguous to the surface of the workpiece, said adhesive bead being formed prior to adhering a second workpiece to said surface, said method comprising the steps of: (a) placing a self-supporting film of adhesive on said workpiece so as to cover said aperture and contact the surface of said workpiece surrounding said aperture, said film being characterized by a tendency to lose cohesive strength when heated, by a substantially uniform thickness, and by a tendency to contract when ruptured, (b) causing said film to at least partially adhere to said surface surrounding said aperture, (c) heating said film to a temperature lower than the melting temperature of said film to reduce the cohesive strength of said film, and while maintaining the temperature of said film below the melting temperature of said film injecting a fluid into said aperture in a direction so as to cause the portion of said film covering said aperture to distend outwardly from the surface of said workpiece and form a bubble, said fluid being injected until said bubble ruptures and said film contracts toward the periphery of said aperture to leave an adhesive bead surrounding said aperture.
Claim 8
Independent Claim
221 words
A method for forming an adhesive bead on the surface of a workpiece surrounding an aperture in the surface of said workpiece and on the walls of the aperture contiguous to the surface of the workpiece, said adhesive bead being formed prior to adhering a second workpiece to said surface, said method comprising the steps of: (a) placing a self-supporting film of adhesive on said workpiece so as to cover said aperture and contact the surface of said workpiece surrounding said aperture, said film being characterized by a tendency to lose cohesive strength when heated, by a substantially uniform thickness, and by a tendency to contract when ruptured, (b) causing said film to at least partially adhere to said surface surrounding said aperture, (c) heating said film to a temperature lower than the melting temperature of said film to reduce the cohesive strength of said film, and while maintaining the temperature of said film below the melting temperature of said film injecting a fluid into said aperture in a direction so as to cause the portion of said film covering said aperture to distend outwardly from the surface of said workpiece and form a bubble, said fluid being injected until said bubble ruptures and said film contracts toward the periphery of said aperture to leave an adhesive bead surrounding said aperture.
Claim 9
Dependent Claim
45 words
The method of claim 6 wherein said workpiece contains a plurality of apertures and wherein said film of adhesive is placed on said workpiece so as to cover said plurality of apertures and to contact the surface of said workpiece surrounding said plurality of apertures.
Claim 10
Dependent Claim
16 words
The method of claim 6 wherein said resin comprises an epoxy resin or a polyimide resin.
Claim 11
Dependent Claim
30 words
The method of claim 5 wherein said workpiece is a honeycomb core, said surface comprising the surface network formed by the edges of the cell walls of the honeycomb core.
Claim 12
Independent Claim
224 words
A method for reticulating an adhesive film to conform to the surface network formed by the edge surfaces of the cell walls of a honeycomb core comprising: (a) overlaying said surface network with a continuous adhesive film, said film being characterized by a tendency to lose its cohesive strength when heated, by a substantially uniform thickness, and by a tendency to contract when ruptured, (b) heating said adhesive film to a temperature lower than the melting temperature of said film over at least a portion of said surface network to cause said adhesive film to adhere to said surface network and to reduce the cohesive strength of said adhesive film, and (c) prior to placing a second workpiece on said surface for adherence thereto and after heating said adhesive film, injecting a fluid through the cells of said honeycomb core, while maintaining the temperature of said film below the melting temperature of said film, so as to cause the heated portion of said adhesive film covering said cells to distend outwardly away from said surface network to form bubbles over said cells, said fluid being injected until said bubbles rupture and said adhesive film contracts toward said surface network to leave a bead of adhesive covering said surface network and only the portion of the walls of said cells continguous to said surface network.
Claim 13
Independent Claim
224 words
A method for reticulating an adhesive film to conform to the surface network formed by the edge surfaces of the cell walls of a honeycomb core comprising: (a) overlaying said surface network with a continuous adhesive film, said film being characterized by a tendency to lose its cohesive strength when heated, by a substantially uniform thickness, and by a tendency to contract when ruptured, (b) heating said adhesive film to a temperature lower than the melting temperature of said film over at least a portion of said surface network to cause said adhesive film to adhere to said surface network and to reduce the cohesive strength of said adhesive film, and (c) prior to placing a second workpiece on said surface for adherence thereto and after heating said adhesive film, injecting a fluid through the cells of said honeycomb core, while maintaining the temperature of said film below the melting temperature of said film, so as to cause the heated portion of said adhesive film covering said cells to distend outwardly away from said surface network to form bubbles over said cells, said fluid being injected until said bubbles rupture and said adhesive film contracts toward said surface network to leave a bead of adhesive covering said surface network and only the portion of the walls of said cells continguous to said surface network.
Claim 14
Dependent Claim
17 words
The method of claim 10 wherein said adhesive film comprises an epoxy resin or a polyimide resin.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-02-10 | 1984-08-11 | 1985-02-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-02-10 | 1988-08-11 | 1989-02-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-02-10 | 1992-08-11 | 1993-02-10 | $7700.00 | Window Closed / Lapsed |