Powder-metallurgy steel article with high vanadium-carbide content
Assignee: Crucible Materials Corp
•
Filing: 1978-09-20
•
Granted: 1981-02-10
•
Expires: 1998-09-20
Abstract
Abstract A powder metallurgy tool steel article for use in applications requiring high wear resistance having a carbide content of 10 to 18 volume percent of substantially all MC-type vanadium carbides, which carbides are substantially spherical and uniformly dispersed; the carbon content of the article is balanced relative to the carbide formers vanadium, chromium and molybdenum to provide an amount of carbon in the matrix of the article sufficient to permit the article to be heat treated to a hardness of at least 56 R c .
Inventors
- 👤 Walter T. Haswell
- 👤 August Kasak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:34
CPC Classifications
B; B22; B22F; B22F5/00; C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0278; C22C33/0285; C22C33/0292
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
133 words
A powder metallurgy articles formed from compacted prealloyed powder of an alloy consisting essentially of, in weight percent, manganese 0.2 to 1.5, silicon 2 max., chromium 1.5 to 6, molybdenum 0.50 to 6, sulfur 0.30 max., vanadium 6 to 11, carbon 1.6 to 2.8, balance iron and incidential elements and impurities characteristic of steelmaking practice, said article having a dispersion of substantially all MC-ype vanadium carbides within the range of about 10 to 18 percent by volume, whereby said article is characterized by improved wear resistance with toughness and workability at acceptable levels, said carbides being substantially spherical and uniformly distributed, said carbon being balanced with the chromium, molybdenum and vanadium to provide sufficient carbon to permit said article to be heat treated to a hardness of at least 56 R c .
Claim 2
Dependent Claim
133 words
A powder metallurgy articles formed from compacted prealloyed powder of an alloy consisting essentially of, in weight percent, manganese 0.2 to 1.5, silicon 2 max., chromium 1.5 to 6, molybdenum 0.50 to 6, sulfur 0.30 max., vanadium 6 to 11, carbon 1.6 to 2.8, balance iron and incidential elements and impurities characteristic of steelmaking practice, said article having a dispersion of substantially all MC-ype vanadium carbides within the range of about 10 to 18 percent by volume, whereby said article is characterized by improved wear resistance with toughness and workability at acceptable levels, said carbides being substantially spherical and uniformly distributed, said carbon being balanced with the chromium, molybdenum and vanadium to provide sufficient carbon to permit said article to be heat treated to a hardness of at least 56 R c .
Claim 3
Dependent Claim
101 words
The powder metallurgy article of claim 1 wherein the powder metallurgy article is formed of prealloyed powder of an alloy consisting essentially of, in weight percent, manganese 0.4 to 0.6, silicon 1 max., chromium 5 to 5.5, molybdenum 1.15 to 1.4, sulfur 0.09 max., vanadium 9.25 to 10.25, carbon 2.40 to 2.50, balance iron and incidental elements and impurities characteristic of steelmaking practice, said article having a dispersion of substantially all MC-type vanadium carbides within the range of about 15 to 17 percent by volume whereby said article is characterized by improved wear resistance with toughness and workability at acceptable levels.
Claim 4
Dependent Claim
101 words
The powder metallurgy article of claim 1 wherein the powder metallurgy article is formed of prealloyed powder of an alloy consisting essentially of, in weight percent, manganese 0.2 to 1, silicon 2 max., chromium 4.5 to 5.5, molybdenum 0.80 to 1.7, sulfur 0.14 max., vanadium 8 to 10.5, carbon 2.2 to 2.6, balance iron and incidential elements and impurities characteristic of steelmaking practice, said article having a dispersion of substantially all MC-type vanadium carbides within the range of about 13.3 to 17.2 percent by volume whereby said article is characterized by improved wear resistance with toughness and workability at acceptable levels.
References Cited (Backward Citations)
US3150444A
Cited
US3591349A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-02-10 | 1984-08-11 | 1985-02-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-02-10 | 1988-08-11 | 1989-02-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-02-10 | 1992-08-11 | 1993-02-10 | $7700.00 | Window Closed / Lapsed |