Polyurethane derived from both an aliphatic dicarboxylic acid and an aromatic dicarboxylic acid and fuel container made therefrom
Assignee: Engineered Fabrics Corp
•
Filing: 1979-08-17
•
Granted: 1981-01-27
•
Expires: 1999-08-17
Abstract
Abstract A polyester urethane fuel cell having at least one layer of a reaction product of an organic polyisocyanate and a mixed polyester and a curative. In the preferred embodiment the fuel cell has a barrier layer composed of a polyester urethane formed from reacting bis(4-cyclohexyl isocyanate) with 10 to 90 mol percent of polyhexamethylene ortho phthalate and 90 to 10 mol percent of a polycaprolactane and curative. The mixed polyesters are either a blend or co-condensation product of a monomeric polyol of less than 5 carbon atoms with an aromatic dicarboxylic acid and an aliphatic dicarboxylic acid.
Inventors
- 👤 Daniel A. Chung
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:44
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/72; C08G18/74; C08G18/75; C08G18/758; C08G18/08; C08G18/10; C08G18/12; C08G18/28; C08G18/40; C08G18/42; C08G18/4202; C08G18/4205; C08G18/4208; C08G18/4211; C08G18/4216; C08G18/4219; C08G2390/00; C08G2390/40
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
80 words
A polyurethane comprising the reaction product of an aliphatic or alicyclic polyisocyanate with a mixed polyester selected from the class consisting of (1) a copolyester having the structure obtained by condensation of a polyol of less than 900 molecular weight with an aliphatic dicarboxylic acid and an aromatic dicarboxylic acid and (2) a blend of an aliphatic polyester and an aromatic polyester and cured with a curative containing at least two groups selected from the class of amine and hydroxyl.
Claim 2
Dependent Claim
80 words
A polyurethane comprising the reaction product of an aliphatic or alicyclic polyisocyanate with a mixed polyester selected from the class consisting of (1) a copolyester having the structure obtained by condensation of a polyol of less than 900 molecular weight with an aliphatic dicarboxylic acid and an aromatic dicarboxylic acid and (2) a blend of an aliphatic polyester and an aromatic polyester and cured with a curative containing at least two groups selected from the class of amine and hydroxyl.
Claim 3
Dependent Claim
19 words
The polyurethane of claim 1 where the polyol condensed with the dicarboxylic acid contains at least 6 carbon atoms.
Claim 4
Dependent Claim
17 words
The polyurethane of claim 2 wherein the aliphatic dicarboxylic acid contains from 6 to 9 carbon atoms.
Claim 5
Dependent Claim
18 words
The polyurethane of claim 2 wherein the dicarboxylic acids are composed of a mixture of isophthalic and azelaic.
Claim 6
Dependent Claim
16 words
The polyurethane of claim 1 wherein the polyester contains 1 to 10 mol percent of trifunctionality.
Claim 7
Dependent Claim
92 words
A polyester urethane fuel cell having at least one layer of an elastomer composed of reaction product of an aliphatic or an alicyclic polyisocyanate with mixed polyesters having structures obtained by condensation of a monomeric polyol of less 400 molecular weight with a blend of 10 to 90 mol percent of an aromatic dicarboxylic acid and 90 to 10 mol percent of an aliphatic dicarboxylic acid of 6 to 9 carbon atoms to give at least 3 mol percent free NCO and then curing with a curative containing hydroxyl or amino groups.
Claim 8
Dependent Claim
92 words
A polyester urethane fuel cell having at least one layer of an elastomer composed of reaction product of an aliphatic or an alicyclic polyisocyanate with mixed polyesters having structures obtained by condensation of a monomeric polyol of less 400 molecular weight with a blend of 10 to 90 mol percent of an aromatic dicarboxylic acid and 90 to 10 mol percent of an aliphatic dicarboxylic acid of 6 to 9 carbon atoms to give at least 3 mol percent free NCO and then curing with a curative containing hydroxyl or amino groups.
Claim 9
Dependent Claim
50 words
The fuel cell of claim 6 having a fuel barrier layer composed of a polyester urethane obtained by reacting methylene bis(4-cyclohexylisocyanate) with 10 to 90 mol percent of polyhexamethylene ortho phthalate and 90 to 10 mol percent of polycaprolactone to form a prepolymer and curing the prepolymer with a diamine.
Claim 10
Dependent Claim
12 words
The fuel cell of claim 6 wherein the diamine is meta-phenylene diamine.
Claim 11
Dependent Claim
14 words
The fuel cell of claim 6 wherein the elastomer contains a fabric reinforcing material.
References Cited (Backward Citations)
US2880192A
Cited
US3998871A
Cited
US3738860A
Cited
US3804810A
Cited
US3951919A
Cited
US3929732A
Cited
US4102868A
Cited
US4158649A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-27 | 1984-07-28 | 1985-01-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-27 | 1988-07-28 | 1989-01-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-27 | 1992-07-28 | 1993-01-27 | $7700.00 | Window Closed / Lapsed |