Carbonyl latent accelerators for curing epoxy resins
Assignee: Siemens Energy Inc
•
Filing: 1979-08-08
•
Granted: 1981-01-20
•
Expires: 1999-08-08
Abstract
Abstract A highly fluid, solventless, resinous, impregnating and coating composition, suitable as a high voltage insulation for electrical members, is made from an admixture containing: 100 parts of an epoxy resin, about 25 to 200 parts of an acid anhydride reactive with the epoxy resin, and about 0.002 to 1.00 part of a selected metal carbonyl, acting as a latent accelerator.
Inventors
- 👤 James D. B. Smith
- 👤 Robert N. Kauffman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 02:01
CPC Classifications
H; H02; H02K; H02K3/00; H02K3/30; C; C08; C08G; C08G59/00; C08G59/18; C08G59/68; C08G59/70; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/40; H01F; H01F27/00; H01F27/28; H01F27/32; H01F27/323; H01F27/327
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
59 words
A highly fluid, solventless, resinous epoxy composition comprising; (1) an epoxy resin, (2) an anhydride reactive with the epoxy resin and (3) from about 0.002 part to 1.00 part per 100 parts by weight of epoxy resin of a metal carbonyl selected from the group consisting of chromium hexacarbonyl, dicobalt octacarbonyl and mixtures thereof, acting as a latent catalyst.
Claim 2
Dependent Claim
59 words
A highly fluid, solventless, resinous epoxy composition comprising; (1) an epoxy resin, (2) an anhydride reactive with the epoxy resin and (3) from about 0.002 part to 1.00 part per 100 parts by weight of epoxy resin of a metal carbonyl selected from the group consisting of chromium hexacarbonyl, dicobalt octacarbonyl and mixtures thereof, acting as a latent catalyst.
Claim 3
Dependent Claim
151 words
A highly fluid, solventless, resinous epoxy composition comprising by weight: (A) 100 parts by weight of a resin comprising: (1) a first epoxy resin consisting of a diglycidyl ether of an aliphatic diol; and (2) a second epoxy resin selected from the group consisting of bisphenol A epoxy resins, bisphenol F epoxy resins, novolac epoxy resins, glycidyl ester epoxy resins, hydantoin epoxy resins, cycloaliphatic epoxy resins and mixtures thereof, wherein the weight ratio of diglycidyl ether of an aliphatic diol; second epoxy resin is from about 1.0:0.0 to about 1.0:4.0, (B) about 25 parts to 200 parts by weight of an organic carboxylic acid anhydride, and (C) about 0.002 part to 1.00 part of a metal carbonyl selected from the group consisting of chromium hexacarbonyl, dicobalt octacarbonyl and mixtures thereof, acting as a latent catalyst, wherein the resinous composition has an initial viscosity of below about 350 cps. at 25° C.
Claim 4
Dependent Claim
151 words
A highly fluid, solventless, resinous epoxy composition comprising by weight: (A) 100 parts by weight of a resin comprising: (1) a first epoxy resin consisting of a diglycidyl ether of an aliphatic diol; and (2) a second epoxy resin selected from the group consisting of bisphenol A epoxy resins, bisphenol F epoxy resins, novolac epoxy resins, glycidyl ester epoxy resins, hydantoin epoxy resins, cycloaliphatic epoxy resins and mixtures thereof, wherein the weight ratio of diglycidyl ether of an aliphatic diol; second epoxy resin is from about 1.0:0.0 to about 1.0:4.0, (B) about 25 parts to 200 parts by weight of an organic carboxylic acid anhydride, and (C) about 0.002 part to 1.00 part of a metal carbonyl selected from the group consisting of chromium hexacarbonyl, dicobalt octacarbonyl and mixtures thereof, acting as a latent catalyst, wherein the resinous composition has an initial viscosity of below about 350 cps. at 25° C.
Claim 5
Dependent Claim
20 words
The composition of claim 2, wherein the resin has an epoxy equivalent weight of from about 100 to about 500.
Claim 6
Dependent Claim
23 words
The composition of claim 2, wherein the composition has a storage lifetime of at least 150 days under 1,000 cps. at 25° C.
Claim 7
Dependent Claim
12 words
The composition of claim 2, wherein the metal carbonyl is chromium hexacarbonyl.
Claim 8
Dependent Claim
48 words
The composition of claim 2, wherein the diglycidyl ether of an aliphatic diol has a viscosity of between about 5 cps. to about 60 cps. at 25° C. and the second epoxy resin has a viscosity of between about 250 cps. to about 20,000 cps. at 25° C.
Claim 9
Dependent Claim
44 words
The composition of claim 2, wherein the diglycidyl ether of an aliphatic diol is selected from the group consisting of diglycidyl ethers of neopentyl glycol, diglycidyl ethers of 1,4 butane diol, diglycidyl ethers of ethylene glycol, diglycidyl ethers of polyether glycols and mixtures thereof.
Claim 10
Dependent Claim
21 words
The composition of claim 2, also containing up to 300 parts of monoethylenically unsaturated vinyl monomer per 100 parts epoxy resin.
Claim 11
Dependent Claim
31 words
The composition of claim 2, wherein the composition also contains up to about 100 parts of filler particles, of average particle sizes of from about 10 microns to about 300 microns.
Claim 12
Dependent Claim
25 words
An insulated electrical member and a cured body of resinous insulation applied to the member, the insulation comprising the cured resinous composition of claim 1.
References Cited (Backward Citations)
US3709861A
Cited
US4137275A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-20 | 1984-07-21 | 1985-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-20 | 1988-07-21 | 1989-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-20 | 1992-07-21 | 1993-01-20 | $7700.00 | Window Closed / Lapsed |