Urea/formaldehyde adhesives
Assignee: Patentes y Novedades SA
•
Filing: 1979-04-04
•
Granted: 1981-01-20
•
Expires: 1999-04-04
Abstract
Abstract The invention relates to a process for the production of urea/formaldehyde adhesives and to the adhesives thus obtained. According to the invention, an inorganic salt is mixed with a source of formaldehyde, the resulting mixture is heated and reacted with urea to initiate polymerization in an acid medium, the polymerization reaction is stopped when the mixture has reached the required viscosity, the mixture is cooled, urea is added to the mixture during cooling and the adhesive is obtained after cooling. The adhesives obtained may be used in the production of agglomerated or laminated panels of wood.
Inventors
- 👤 Ramon Bruguera
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:10
CPC Classifications
C; C09; C09J; C09J161/00; C09J161/20; C09J161/22; C09J161/24; C08; C08G; C08G12/00; C08G12/02; C08G12/04; C08G12/10; C08G12/12; C08K; C08K3/00; C08K3/18; C08K3/24; C08L; C08L97/00; C08L97/02; C08L61/00; C08L61/20; C08L61/22; C08L61/24
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
78 words
A process for the production of a urea/formaldehyde adhesive comprising the step of mixing an inorganic salt with a formaldehyde source, heating the resulting mixture and reacting the resulting mixture with urea to initiate polymerisation in an acid medium at a pH between 5 and 6.5, the polymerisation reaction being stopped by rendering the mixture alkaline when the mixture has reached a required viscosity and urea being added to the mixture during cooling to give adhesive after cooling.
Claim 2
Dependent Claim
78 words
A process for the production of a urea/formaldehyde adhesive comprising the step of mixing an inorganic salt with a formaldehyde source, heating the resulting mixture and reacting the resulting mixture with urea to initiate polymerisation in an acid medium at a pH between 5 and 6.5, the polymerisation reaction being stopped by rendering the mixture alkaline when the mixture has reached a required viscosity and urea being added to the mixture during cooling to give adhesive after cooling.
Claim 3
Dependent Claim
30 words
The process according to claim 1 wherein the formaldehyde source is selected from the group consisting of aqueous solutions of formaldehyde, more or less polymerised formaldehydes, paraformaldehyde and urea/formaldehyde pre-condensates.
Claim 4
Dependent Claim
25 words
The process according to claim 1 wherein the formaldehyde source is an aqueous solution of formaldehyde and two additions of urea are made during heating.
Claim 5
Dependent Claim
89 words
The process according to claim 3 wherein the aqueous formaldehyde solution is a 37% by weight, solution and the first addition of urea is made when the temperature of the mixture is about 50° C. in such a quantity that the resulting molar ratio of formaldehyde to urea is about 2.65:1 and the second addition of urea is made when the temperature of the mixture is about 100° C. in such a quantity that the resulting molar ratio of formaldehyde to urea is from about 2.0:1 to about 2.65:1.
Claim 6
Dependent Claim
23 words
The process according to claim 1 wherein the formaldehyde source is a urea/formaldehyde pre-condensate and one addition of urea is made during heating.
Claim 7
Dependent Claim
66 words
The process according to claim 5 wherein the urea/formaldehyde pre-condensate has a molar ratio of formaldehyde to urea of from about 4:1 to about 6:1 and the addition of urea is made when the temperature of the mixture is from about 60° to about 65° C. in such a quantity that the resulting molar ratio of formaldehyde to urea is from about 2.0:1 to about 2.65:1
Claim 8
Dependent Claim
28 words
The process according to claim 1 wherein the inorganic salt is selected from the group consisting of alkali metal or alkaline earth metal halides or alkali metal sulphates.
Claim 9
Dependent Claim
32 words
The process according to claim 7 wherein the inorganic salt is added in such a quantity that the resulting molar ratio of salt to formaldehyde is from about 0.015:1 to about 0.35:1.
Claim 10
Dependent Claim
23 words
The process according to claim 1 wherein the polymerisation reaction is stopped when the temperature is from about 80° to about 100° C.
Claim 11
Dependent Claim
45 words
The process according to claim 1 wherein the addition of urea during cooling is made when the temperature is from about 60° to 80° C. in such a quantity that the resulting molar ratio of formaldehyde to urea is from about 1.45:1 to about 2:1.
Claim 12
Dependent Claim
19 words
The process according to claim 1 wherein, after the urea has been added during cooling, the mixture is distilled.
Claim 13
Dependent Claim
39 words
The process according to claim 1 wherein the mixture is cooled to a temperature of from about 20° to about 35° C. and is adjusted to a pH of about 8.0 to about 8.5 before the adhesive is obtained.
References Cited (Backward Citations)
US2175475A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-20 | 1984-07-21 | 1985-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-20 | 1988-07-21 | 1989-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-20 | 1992-07-21 | 1993-01-20 | $7700.00 | Window Closed / Lapsed |