Fire retardant coating system utilizing polyurethane hydrogel
Assignee: WR Grace and Co
•
Filing: 1979-03-09
•
Granted: 1981-01-20
•
Expires: 1999-03-09
Abstract
Abstract A fire-retardant protective coating is produced by dissolving a water-soluble polyisocyanate prepolymer in either an aqueous slurry or solution of fire-retardant materials and/or intumescent materials. After mixing, the gel produced can be applied as a coating which is useful for protecting or holding together surfaces vulnerable to fire, heat, air or minor abrasion. After the water evaporates, the cross-linked polyurethane coating has a large solids content of the fire-retardant and/or intumescent materials uniformly dispersed throughout. Preferred prepolymers are liquid with a molecular weight greater than about 2,000 and are made of a random copolymer of ethylene oxide and other alkylene oxides with isocyanate capping.
Inventors
- 👤 Louis L. Wood
- 👤 Glenn E. Fulmer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 23:19
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/18; C09D5/185; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/48; C08G18/4833; C08G18/4837; C08K; C08K3/00; C08K3/01; C08K3/016; C08K5/00; C08K5/0008; C08K5/0066; C09D175/00; C09D175/04; C09D175/08; C08G2210/00; Y; Y10; Y10S; Y10S260/00; Y10S260/24
Claims Analysis
Total Claims: 40
Claim 1
Independent Claim
66 words
A fire-retardant, elastomeric cross-linked polyurethane gel composition comprising the reaction product of (a) a water-soluble prepolymer of a polyether polyol capped with polyisocyanates having a number average molecular weight of about at least 2,000, and (b) an aqueous fire-retardant or intumescent slurry, said prepolymer being present in the reaction mixture in an amount of about 1 to 100 parts by weight per 100 parts of water.
Claim 2
Dependent Claim
66 words
A fire-retardant, elastomeric cross-linked polyurethane gel composition comprising the reaction product of (a) a water-soluble prepolymer of a polyether polyol capped with polyisocyanates having a number average molecular weight of about at least 2,000, and (b) an aqueous fire-retardant or intumescent slurry, said prepolymer being present in the reaction mixture in an amount of about 1 to 100 parts by weight per 100 parts of water.
Claim 3
Dependent Claim
16 words
A gel composition according to claim 1, wherein the prepolymer is a liquid at room temperature.
Claim 4
Dependent Claim
45 words
A gel composition according to claim 1, wherein the polyether polyol is made of random ethylene oxide units and other alkylene oxide units with the ethylene oxide units comprising at least about 50 percent of the total number of ethylene oxide and alkylene oxide units.
Claim 5
Dependent Claim
29 words
A gel composition according to claim 3, wherein the ethylene oxide units comprise at least about 70 percent of the total number of ethylene oxide and alkylene oxide units.
Claim 6
Dependent Claim
24 words
A gel composition according to claims 3 or 4, wherein the polyether polyol is made of random ethylene oxide units and propylene oxide units.
Claim 7
Dependent Claim
32 words
A gel composition according to claim 1, wherein said prepolymer is present in the reaction mixture in an amount of about 1 to 20 parts by weight per 100 parts of water.
Claim 8
Dependent Claim
31 words
A gel composition according to claim 1, wherein the slurry contains a fire-retardant or intumescent material present in an amount of about 10 to 300 parts per 100 parts of water.
Claim 9
Dependent Claim
38 words
A gel composition according to claim 1, wherein said slurry contains a fire-retardant or intumescent material selected from the group consisting of alumina trihydrate, polyammonium phosphates, borates, wood pulp, halogen-containing materials, heavy metals, phosphorous compounds, and mixtures thereof.
Claim 10
Dependent Claim
24 words
A gel composition according to claim 1, wherein the slurry further comprises a surfactant selected from the group consisting of amphoteric and cationic surfactants.
Claim 11
Dependent Claim
17 words
A gel composition according to claim 1, wherein the slurry further comprises a non-ionic surfactant suspending agent.
Claim 12
Dependent Claim
16 words
A gel composition according to claim 1, wherein the slurry further comprises a fiber reinforcing agent.
Claim 13
Dependent Claim
17 words
A gel composition according to claim 1, wherein the polyisocyanate capping the polyether polyol is toluene diisocyanate.
Claim 14
Dependent Claim
17 words
A gel composition according to claim 1, wherein the prepolymer has less than about 1.0 meq. NCO/g.
Claim 15
Dependent Claim
20 words
A gel composition according to claim 1, wherein the prepolymer has a number average molecular weight of at least 3,000.
Claim 16
Dependent Claim
28 words
A gel composition according to claim 1, wherein the slurry contains alumina trihydrate in an amount of about 20 to about 300 parts per 100 parts of water.
Claim 17
Dependent Claim
117 words
A gel composition according to claim 1, wherein (a) the polyether polyol is a liquid made of random ethylene oxide units and propylene oxide units with the ethylene oxide units comprising at least about 70 percent of the total number of ethylene oxide and propylene units, (b) the prepolymer is present in the reaction mixture in an amount of about 1 to 20 parts by weight per 100 parts of water, and (c) the slurry contains a fire-retardant or intumescent, material in an amount of about 10 to 300 parts per 100 parts of water selected from the group consisting of alumina trihydrate, polyammonium phosphates, borates, wood pulp, halogen-containing materials, heavy metals, phosphorous compounds, and mixtures thereof.
Claim 18
Independent Claim
61 words
A method of producing a fire-retardant, elastomeric cross-linked polyurethane gel by reacting together. (a) a water-soluble prepolymer of a polyether polyol capped with polyisocyanates having a number average molecular weight of about at least 2,000, and (b) an aqueous fire-retardant slurry, said prepolymer being present in the reaction in an amount of 1--100 parts by weight per 100 parts of water.
Claim 19
Independent Claim
61 words
A method of producing a fire-retardant, elastomeric cross-linked polyurethane gel by reacting together. (a) a water-soluble prepolymer of a polyether polyol capped with polyisocyanates having a number average molecular weight of about at least 2,000, and (b) an aqueous fire-retardant slurry, said prepolymer being present in the reaction in an amount of 1--100 parts by weight per 100 parts of water.
Claim 20
Dependent Claim
59 words
A method according to claim 17, wherein the polyether polyol is made of random ethylene oxide and propylene oxide units, with at least 70 percent of the total units being ethylene oxide and wherein the prepolymer is a liquid which is present in the reaction mixture in an amount of 1 to 20 parts per 100 parts of water.
Claim 21
Independent Claim
72 words
A method of protecting flammable surfaces comprising applying to the surface of coating of a cross-linked polyurethane gel forming composition formed by reacting together. (a) a water-soluble prepolymer of a polyether polyol capped with polyisocyanates having a number average molecular weight of about at least 2,000, and (b) an aqueous fire-retardant slurry, said prepolymer being present in the reaction in an amount of 1--100 parts by weight per 100 parts of water.
Claim 22
Independent Claim
72 words
A method of protecting flammable surfaces comprising applying to the surface of coating of a cross-linked polyurethane gel forming composition formed by reacting together. (a) a water-soluble prepolymer of a polyether polyol capped with polyisocyanates having a number average molecular weight of about at least 2,000, and (b) an aqueous fire-retardant slurry, said prepolymer being present in the reaction in an amount of 1--100 parts by weight per 100 parts of water.
Claim 23
Dependent Claim
59 words
A method according to claim 19, wherein the polyether polyol is made of random ethylene oxide and propylene oxide units with at least 70 percent of the total units being ethylene oxide and wherein the prepolymer is a liquid which is present in the reaction mixture in an amount of 1 to 20 parts per 100 parts of water.
Claim 24
Dependent Claim
94 words
In a fire-retardant, elastomeric cross-linked polyurethane gel composition comprising the reaction product of (a) a water-soluble prepolymer of a polyether polyol capped with polyisocyanates having a number average molecular weight of about at least 2,000, and (b) water, said prepolymer being present in the reaction mixture in an amount of about 1 to 100 parts by weight per 100 parts of water, the improvement which comprises a combination of a fire-retardant or intumescent material present in an amount of about 10 to 300 parts per 100 parts of the water in the reaction mixture.
Claim 25
Dependent Claim
94 words
In a fire-retardant, elastomeric cross-linked polyurethane gel composition comprising the reaction product of (a) a water-soluble prepolymer of a polyether polyol capped with polyisocyanates having a number average molecular weight of about at least 2,000, and (b) water, said prepolymer being present in the reaction mixture in an amount of about 1 to 100 parts by weight per 100 parts of water, the improvement which comprises a combination of a fire-retardant or intumescent material present in an amount of about 10 to 300 parts per 100 parts of the water in the reaction mixture.
Claim 26
Dependent Claim
16 words
A gel composition according to claim 21, wherein the prepolymer is a liquid at room temperature.
Claim 27
Dependent Claim
45 words
A gel composition according to claim 21, wherein the polyether polyol is made of random ethylene oxide units and other alkylene oxide units with the ethylene oxide units comprising at least about 50 percent of the total number of ethylene oxide and alkylene oxide units.
Claim 28
Dependent Claim
29 words
A gel composition according to claim 21, wherein the ethylene oxide units comprise at least about 70 percent of the total number of ethylene oxide and alkylene oxide units.
Claim 29
Dependent Claim
24 words
A gel composition according to claims 23 or 24, wherein the polyether polyol is made of random ethylene oxide units and propylene oxide units.
Claim 30
Dependent Claim
32 words
A gel composition according to claim 21, wherein said prepolymer is present in the reaction mixture in an amount of about 1 to 20 parts by weight per 100 parts of water.
Claim 31
Dependent Claim
37 words
A gel composition according to claim 21, wherein said fire-retardant or intumescent material is selected from the group consisting of alumina trihydrate, polyammonium phosphates, borates, wood pulp, halogen-containing materials, heavy metals and phosphorous compounds, and mixtures thereof.
Claim 32
Dependent Claim
24 words
A gel composition according to claim 21, wherein the slurry further comprises a surfactant selected from the group consisting of amphoteric and cationic surfactants.
Claim 33
Dependent Claim
17 words
A gel composition according to claim 21, wherein the slurry further comprises a non-ionic surfactant suspending agent.
Claim 34
Dependent Claim
16 words
A gel composition according to claim 21, wherein the slurry further comprises a fiber reinforcing agent.
Claim 35
Dependent Claim
17 words
A gel composition according to claim 21, wherein the polyisocyanate capping the polyether polyol is toluene diisocyanate.
Claim 36
Dependent Claim
17 words
A gel composition according to claim 21, wherein the prepolymer has less than about 1.0 meq. NCO/g.
Claim 37
Dependent Claim
20 words
A gel composition according to claim 21, wherein the prepolymer has a number average molecular weight of at least 3,000.
Claim 38
Dependent Claim
28 words
A gel composition according to claim 21, wherein the slurry contains alumina trihydrate in an amount of about 20 to about 300 parts per 100 parts of water.
Claim 39
Dependent Claim
117 words
A gel composition according to claim 21, wherein (a) the polyether polyol is a liquid made of random ethylene oxide units and propylene oxide units with the ethylene oxide units comprising at least about 70 percent of the total number of ethylene oxide and propylene units, (b) the prepolymer is present in the reaction mixture in an amount of about 1 to 20 parts by weight per 100 parts of water, and (c) the slurry contains a fire-retardant or intumescent material in an amount of about 10 to 300 parts per 100 parts of water selected from the group consisting of alumina trihydrate, polyammonium phosphates, borates, wood pulp, halogen-containing materials, heavy metals, phosphorous compounds, and mixtures thereof.
Claim 40
Dependent Claim
25 words
A gel composition according to claims 8, 16, 27 or 35, wherein said borates comprise sugar borate derivative, starch borate derivative, or cellulose borate derivative.
References Cited (Backward Citations)
US2948691A
Cited
US3719050A
Cited
US4118354A
Cited
US3897372A
Cited
GB1478000A
Cited
US4066578A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-20 | 1984-07-21 | 1985-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-20 | 1988-07-21 | 1989-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-20 | 1992-07-21 | 1993-01-20 | $7700.00 | Window Closed / Lapsed |