US4246057A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Heat transfer surface and method for producing such surface
Assignee: Bank of Nova Scotia
•
Filing: 1977-12-27
•
Granted: 1981-01-20
•
Expires: 1997-12-27
Abstract
Abstract The invention relates to improving the heat transfer properties in boiling liquids of tubes and other surfaces by applying a very porous reticulated organic foam layer in contact with the tube surface, and then plating a thin metal coating on the foam substrate. Preferably, the tube is copper and the plating consists of a first electrolessly applied layer of copper and a second electroplated layer. The foam is preferably in the form of a thin tape which is spirally wound about the tube. Pyrolization of the foam after plating improves the heat transfer performance of the tube.
Inventors
- 👤 Kenneth R. Janowski
- 👤 Ming S. Shum
- 👤 Steven A. Bradley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 08:24
CPC Classifications
F; F28; F28F; F28F13/00; F28F13/18; F28F13/185; F28F13/187; B; B22; B22F; B22F3/00; B22F3/10; B22F3/11; B22F3/1121; B22F3/1137; B23; B23P; B23P15/00; B23P15/26; B29; B29C; B29C63/00; B29C63/02; B29C63/04; B29C63/08; B29C63/10; C; C25; C25D; C25D7/00; F16; F16L; F16L9/00; F16L9/14; B22F2998/00; B22F2998/10; B29K; B29K2105/00; B29K2105/04; B29K2705/00; B29K2705/08; B29K2705/10; B29L; B29L2009/00; B29L2009/003; Y; Y10; Y10S; Y10S138/00; Y10S138/09; Y10T; Y10T29/00; Y10T29/49; Y10T29/4935; Y10T29/49377; Y10T29/49826; Y10T29/49885; Y10T29/49886; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249987; Y10T428/24999
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
143 words
A method of providing a metal heat transfer tube with a porous nucleate boiling surface comprising the steps of applying a layer of reticulated open cell organic foam material to the external surface of the metal tube and then plating the exposed surfaces of the reticulated foam material with a metal so as to form a reticulated metal surface which overlies the surface of the metal tube and is firmly adhered thereto, said tube being heated after it is plated to pyrolyze the organic foam material and cause the reticulated metal surface which had been plated around the organic foam material to become a hollow metal skeleton capable of trapping vapor when the tube is placed in a liquid boiling medium and releasing some of said vapor through a multiplicity of openings or pores in said skeleton which comprise vapor phase nucleation sites.
Claim 2
Independent Claim
143 words
A method of providing a metal heat transfer tube with a porous nucleate boiling surface comprising the steps of applying a layer of reticulated open cell organic foam material to the external surface of the metal tube and then plating the exposed surfaces of the reticulated foam material with a metal so as to form a reticulated metal surface which overlies the surface of the metal tube and is firmly adhered thereto, said tube being heated after it is plated to pyrolyze the organic foam material and cause the reticulated metal surface which had been plated around the organic foam material to become a hollow metal skeleton capable of trapping vapor when the tube is placed in a liquid boiling medium and releasing some of said vapor through a multiplicity of openings or pores in said skeleton which comprise vapor phase nucleation sites.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein said plating step includes an initial electroless deposit of metal followed by an electro-deposit deposit of metal.
Claim 4
Dependent Claim
25 words
The method of claim 1 wherein said layer of foam material is applied by spirally wrapping a strip of said foam material about said tube.
Claim 5
Dependent Claim
29 words
The method of claim 1 wherein said plating is made sufficiently thin that portions of it will be fractured by gases developed during pyrolyzation to produce pore openings therein.
Claim 6
Dependent Claim
19 words
The method of claim 1 wherein said heating takes place at a temperature of less than about 900° F.
Claim 7
Dependent Claim
19 words
The method of claim 1 wherein said foam material has a pore size of about 100 pores per inch.
References Cited (Backward Citations)
US3778336A
Cited
GB1199404A
Cited
US3549505A
Cited
GB1238183A
Cited
GB1242864A
Cited
US3679552A
Cited
US3968786A
Cited
US4026747A
Cited
US4093755A
Cited
US4077853A
Cited
US4136428A
Cited
US4136427A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-20 | 1984-07-21 | 1985-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-20 | 1988-07-21 | 1989-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-20 | 1992-07-21 | 1993-01-20 | $7700.00 | Window Closed / Lapsed |