Manufacturing process of vermicular graphic cast-irons through double modification
Assignee: Institutul de Cercetare Stiintifica Inginerie Tehnologica SI Proiectare Mine pe Lignit SA
•
Filing: 1979-09-12
•
Granted: 1981-01-20
•
Expires: 1999-09-12
Abstract
Abstract A two-stage method of making vermicular graphite cast iron in which a first alloy is introduced into the ladle into which the iron is cast and then the vermicular graphite level is measured. A second alloy of a compacting or anticompacting nature is then added to ensure a final vermicular graphite level of at least 85% of the total graphite.
Inventors
- 👤 Doru M. Stefanescu
- 👤 Lucian Dinescu
- 👤 Stefan Craciun
- 👤 Ioan Cristea
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:50
CPC Classifications
C; C21; C21C; C21C1/00; C21C1/10; C21C1/105
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
249 words
A process for the preparation of vermicular graphite-containing cast-iron having a minimum graphite content of at least 85% vermicular graphite which comprises the steps of: (a) forming a melt of cast-iron at a temperature of about 1350° to 1520° C. and having sulfur content ranging between 0.01 and 0.04%; (b) contacting the melt of castiron formed during step (a) with a modifying alloy comprising Fe, Si, Mg, Ti, Al and Ce to form a modified melt; (c) subsequent to step (b) taking a sample of the melt and subjecting the sample to differential thermal analysis to obtain a differentiated cooling curve and determine the content of the graphite present therein that is vermicular, the content of the graphite present therein that is nodular and the content of the graphite present therein that is flaked; (d) when a nodular graphite content is so high that the vermicular graphite content is less than 85%, treating the melt analyzed in step (c) with a sufficient amount of an anticompacting modifier containing silicon, titanium and iron to adjust the content of vermicular graphite to at least 85% of the total graphite present and when the graphite content in flaked form is so high that the vermicular graphite content is less than 85%, treating the melt analyzed in step (c) with a sufficient amount of a compacting modifier to adjust the content of the vermicular graphite to at least 85% of the total graphite present; and (e) pouring the castiron subsequent to step (d).
Claim 2
Dependent Claim
249 words
A process for the preparation of vermicular graphite-containing cast-iron having a minimum graphite content of at least 85% vermicular graphite which comprises the steps of: (a) forming a melt of cast-iron at a temperature of about 1350° to 1520° C. and having sulfur content ranging between 0.01 and 0.04%; (b) contacting the melt of castiron formed during step (a) with a modifying alloy comprising Fe, Si, Mg, Ti, Al and Ce to form a modified melt; (c) subsequent to step (b) taking a sample of the melt and subjecting the sample to differential thermal analysis to obtain a differentiated cooling curve and determine the content of the graphite present therein that is vermicular, the content of the graphite present therein that is nodular and the content of the graphite present therein that is flaked; (d) when a nodular graphite content is so high that the vermicular graphite content is less than 85%, treating the melt analyzed in step (c) with a sufficient amount of an anticompacting modifier containing silicon, titanium and iron to adjust the content of vermicular graphite to at least 85% of the total graphite present and when the graphite content in flaked form is so high that the vermicular graphite content is less than 85%, treating the melt analyzed in step (c) with a sufficient amount of a compacting modifier to adjust the content of the vermicular graphite to at least 85% of the total graphite present; and (e) pouring the castiron subsequent to step (d).
Claim 3
Dependent Claim
33 words
The process defined in claim 1, step (b), wherein the modifying alloy consists by weight essentially of 51.8% Si; 2.69% Al; 2.03% Ca; 4.64% Mg; 4.97% Ti; 0.3% Mischmetall and the balance Fe.
Claim 4
Dependent Claim
22 words
The process defined in claim 2, step (d), wherein the anticompacting modifier comprises by weight 48.4% Si; 0.8% Ca and 8% Ti.
Claim 5
Dependent Claim
29 words
The process defined in claim 2, step (d), wherein the anticompacting modifier consists by weight essentially of 1 to 15% Ti; 40 to 90% Si and the balance Fe.
Claim 6
Dependent Claim
24 words
The process defined in claim 2, step (d), wherein the anticompacting modifier is added in an amount by weight of 0.25% of the melt.
Claim 7
Dependent Claim
33 words
The process defined in claim 2, step (d), wherein the compacting modifier consists by weight essentially of 0.5 to 2% Mg; 0.5 to 2% Ce; 40 to 90% Si and the balance iron.
Claim 8
Dependent Claim
24 words
The process defined in claim 2, step (d), wherein the compacting modifier is added in an amount by weight of 0.25% of the melt.
Claim 9
Dependent Claim
34 words
The process defined in claim 2, step (b), wherein the modifying alloy is added to the melt of castiron so that the amount of modifying alloy added is about 0.1% of the cast-iron melt.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-20 | 1984-07-21 | 1985-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-20 | 1988-07-21 | 1989-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-20 | 1992-07-21 | 1993-01-20 | $7700.00 | Window Closed / Lapsed |