Process of making nodular iron and after-treating alloy utilized therein

Claim 2

In a process for the production of cast nodular iron in which molten iron is first contacted with a graphite-spheroidizing agent in an amount sufficient to yield from about 0.03 to about 0.075 weight percent graphite-spheroidizing agent in the cast nodular iron, the improvement which comprises after-treating the contacted melt with an after-treating agent compatible with said contacted melt and containing from about 0.8 to about 1.8 percent by weight of magnesium whereby said first contacting can be performed with a reduced amount of graphite-spheroidizing agent sufficient to yield from about 0.02 to about 0.055 percent of the graphite-spheroidizing agent in the nodular iron without substantially detrimentally affecting the metallurgical properties of said nodular iron.

Claim 3

The improved process of claim 1 wherein said graphite-spheroidizing agent includes magnesium.

Claim 4

The improved process of claim 1 wherein said first contacting is performed with a reduced amount of graphite-spheroidizing agent sufficient to yield from about 0.03 to about 0.045 percent of the graphite-spheroidizing agent in the nodular iron.

Claim 5

The improved process of claim 1 wherein said melt is contacted with from about 0.25 to about 1.5 percent of the melt of said after-treating agent.

Claim 6

The improved process of claim 1 wherein said after-treating agent contains from about 1 to about 1.6 weight percent magnesium.

Claim 7

The improved process of claim 5 wherein said melt is contacted with from about 0.4 to about 0.8 weight percent of the melt of said after-treating agent.

Claim 8

The improved process of claim 6 wherein said reduced amount of graphite-spheroidizing agent is sufficient to yield an amount of graphite-spheroidizing agent in the nodular iron of from about 0.033 to about 0.042 weight percent.

Claim 9

In a process for the production of cast nodular iron in which molten iron is first contacted with a magnesium- or rare earth-containing graphite-spheroidizing agent, the improvement which comprises after-treating the contacted melt with from about 0.25 to about 1.5 percent of the melt of an after-treating agent compatible with said contacted melt and containing from about 0.8 to about 1.8 percent by weight of magnesium whereby said first contacting can be performed with a reduced amount of graphite-spheroidizing agent without substantially detrimentally affecting the metallurgical properties of said nodular iron.

Claim 10

In a process for the production of cast nodular iron in which molten iron is first contacted with a magnesium- or rare earth-containing graphite-spheroidizing agent, the improvement which comprises after-treating the contacted melt with from about 0.25 to about 1.5 percent of the melt of an after-treating agent compatible with said contacted melt and containing from about 0.8 to about 1.8 percent by weight of magnesium whereby said first contacting can be performed with a reduced amount of graphite-spheroidizing agent without substantially detrimentally affecting the metallurgical properties of said nodular iron.

Claim 11

The improved process of claim 8 wherein said after-treating agent contains from about 1 to about 1.6 weight percent magnesium and said melt is contacted with from about 0.4 to about 0.8 weight percent of the melt of said after-treating agent.

Claim 12

A process for the production of cast nodular iron which comprises contacting molten iron with a graphite-spheroidizing agent in an amount sufficient to yield from about 0.02 to about 0.055 percent of the graphite-spheroidizing agent in the nodular iron and then after-treating the melt within about 15 minutes prior to casting with an after-treating agent compatible with said contacted melt and containing from about 0.8 to about 1.8 percent by weight of magnesium

Claim 13

A process for the production of cast nodular iron which comprises contacting molten iron with a graphite-spheroidizing agent in an amount sufficient to yield from about 0.02 to about 0.055 percent of the graphite-spheroidizing agent in the nodular iron and then after-treating the melt within about 15 minutes prior to casting with an after-treating agent compatible with said contacted melt and containing from about 0.8 to about 1.8 percent by weight of magnesium

Claim 14

whereby a nodular iron is produced as if the said graphite-spheroidizing agent had been utilized in an amount sufficient to yield from about 0.03 to about 0.075 weight percent graphite-spheroidizing agent in the cast nodular iron without substantially detrimentally affecting the metallurgical properties of said nodular iron.

Claim 15

whereby a nodular iron is produced as if the said graphite-spheroidizing agent had been utilized in an amount sufficient to yield from about 0.03 to about 0.075 weight percent graphite-spheroidizing agent in the cast nodular iron without substantially detrimentally affecting the metallurgical properties of said nodular iron.

Claim 16

The process of claim 10 wherein said graphite-spheroidizing agent includes magnesium.

Claim 17

The process of claim 10 wherein said molten iron is contacted with a graphite-spheroidizing agent in an amount sufficient to yield to from about 0.03 to about 0.045 weight percent of the graphite-spheroidizing agent in the nodular iron.

Claim 18

The process of claim 10 wherein said contacted melt is after-treated with from about 0.025 to about 1.5 weight percent of the melt of said after-treating agent.

Claim 19

The process of claim 10 wherein said after-treating agent contains from about 1 to about 1.6 weight percent magnesium.

Claim 20

The process of claim 14 wherein said after-treating agent further contains from about 45 to about 83 weight percent silicon and from about 0.1 to about 4 weight percent calcium.

Claim 21

A process for the production of cast nodular iron which comprises contacting molten iron with a graphite-spheroidizing agent in an amount sufficient to yield from about 0.03 to about 0.045 percent of the graphite-spheroidizing agent in the nodular iron and then after-treating the melt within about 15 minutes prior to casting with an after-treating agent compatible with said contacted melt and containing from about 1.0 to about 1.6 percent by weight of magnesium, balance essentially silicon or a ferrosilicon alloy, whereby a nodular iron is produced as if the said graphite-spheroidizing agent had been utilized in an amount sufficient to yield from about 0.03 to about 0.075 weight percent graphite-spheroidizing agent in the cast nodular iron without substantially detrimentally affecting the metallurgical properties of said nodular iron and the magnesium recovery in the after-treatment is at least about 85 percent.

Claim 22

A process for the production of cast nodular iron which comprises contacting molten iron with a graphite-spheroidizing agent in an amount sufficient to yield from about 0.03 to about 0.045 percent of the graphite-spheroidizing agent in the nodular iron and then after-treating the melt within about 15 minutes prior to casting with an after-treating agent compatible with said contacted melt and containing from about 1.0 to about 1.6 percent by weight of magnesium, balance essentially silicon or a ferrosilicon alloy, whereby a nodular iron is produced as if the said graphite-spheroidizing agent had been utilized in an amount sufficient to yield from about 0.03 to about 0.075 weight percent graphite-spheroidizing agent in the cast nodular iron without substantially detrimentally affecting the metallurgical properties of said nodular iron and the magnesium recovery in the after-treatment is at least about 85 percent.

Claim 23

The process of claim 10 wherein said graphite-spheroidizing agent includes magnesium.

Claim 24

The process of claim 10 wherein said contacted melt is after-treated with from about 0.25 to about 1.5 weight percent of the melt of said after-treating agent and said after-treating agent is ferrosilicon alloy containing said magnesium.

Claim 25

In a process for the production of cast nodular iron in which molten iron is first contacted with a graphite-spheroidizing agent, the improvement which comprises after-treating the contacted melt with an after-treating agent compatible with said contacted melt and containing from about 0.8 to about 1.8 weight percent of magnesium whereby said first contacting can be performed with a reduced amount of graphite-spheroidizing agent without substantially detrimentally affecting the metallurgical properties of said nodular iron.

Claim 26

In a process for the production of cast nodular iron in which molten iron is first contacted with a graphite-spheroidizing agent, the improvement which comprises after-treating the contacted melt with an after-treating agent compatible with said contacted melt and containing from about 0.8 to about 1.8 weight percent of magnesium whereby said first contacting can be performed with a reduced amount of graphite-spheroidizing agent without substantially detrimentally affecting the metallurgical properties of said nodular iron.

Claim 27

In the process of claim 19 wherein said after-treating agent contains from about 1 to about 1.6 weight percent magnesium.

Claim 28

In the process of claim 20 wherein the after-treating agent further contains from about 45 to about 83 weight percent silicon and from about 0.1 to about 4 weight percent calcium.

Claim 29

In the process of claim 19 wherein said after-treating agent is added in an amount of from about 0.25 to about 1.25 weight percent of the melt and the reduction in amount of graphite-spheroidizing agent utilized is from about 20 to about 25 percent.

Claim 30

In the process of claim 19 wherein the said contacted melt is after-treated with the after-treating within about 15 minutes of casting of the melt.