Method of making sintered metal-diamond aggregates
Assignee: Individual
•
Filing: 1978-09-12
•
Granted: 1981-01-20
•
Expires: 1998-09-12
Abstract
Abstract A method of making aggregated diamond abrasive particles comprising forming a mixture of diamond abrasive particles and a powdered metal, heating the mixture to sinter the metal followed by cooling to produce a mass and crushing the mass to obtain the aggregated particles, characterized in that the particles are selected from Types A, B and C, as hereinafter defined, and mixtures thereof: Particles of Type A have the following characteristics: 1. A Friatest Index of about 70 to 90 for those particles of size 74 to 88 microns. 2. Medium metal content. 3. Predominantly translucent color with the occasional transparent white, grey and yellow particle. 4. Predominantly blocky shape tending towards elongate particles. 5. Predominantly rough and undulating surface. Particles of Type B have the following characteristics: 1. Weak, having a Friatest Index of about 65 to 88 for those particles of size 74 to 88 microns. 2. A high metal content. 3. Predominantly dark in color. 4. A blocky and irregular shape. 5. Rough with surface irregularities, re-entrant angles and etch pits. Particles of Type C have the following characteristics: 1. Medium strength, having a Friatest Index in the range about 100 to 121, for those particles of size 74 to 88 microns. 2. Low metal content. 3. Predominantly yellow in color. 4. An angular to blocky shape with sharp edges. 5. A predominantly smooth surface. The particles so produced are particularly useful in the grinding, particularly dry grinding, of carbides, nitrides and abrasive compacts.
Inventors
- 👤 Cornelius Phaal
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 20:32
CPC Classifications
C; C22; C22C; C22C26/00; B; B24; B24D; B24D3/00; B24D3/02; B24D3/20; B24D3/28; B24D3/285; C04; C04B; C04B35/00; C04B35/515; C04B35/52; C09; C09K; C09K3/00; C09K3/14; C09K3/1409; C09K3/1418; C09K3/1436
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
182 words
A method of making aggregated diamond abrasive particles comprising forming a mixture of diamond abrasive particles and a powdered metal, heating the mixture to sinter the metal followed by cooling to produce a mass and crushing the mass to obtain the aggregated particles, characterised in that the particles comprise particles of size 74 to 88 microns and the particles are selected from Types A, B and C, as hereinafter defined, and mixtures thereof: Particles of Type A have the following characteristics: 1. A Friatest Index of about 70 to 90, for those particles of size 74 to 88 microns; 2. A metal content of about 1.0 to 1.5 percent by weight; 3. Predominantly translucent colour with the occasional transparent white, grey and yellow particle; 4. Predominantly blocky shape tending towards elongate particles; 5. Predominantly rough and undulating surface; Particles of Type B have the following characteristics: 1. Weak, having a Friatest Index of about 65 to 88, for those particles of size 74 to 88 microns; 2. A metal content of greater than 2 percent by weight; 3. Predominantly dark in colour;
Claim 2
Independent Claim
182 words
A method of making aggregated diamond abrasive particles comprising forming a mixture of diamond abrasive particles and a powdered metal, heating the mixture to sinter the metal followed by cooling to produce a mass and crushing the mass to obtain the aggregated particles, characterised in that the particles comprise particles of size 74 to 88 microns and the particles are selected from Types A, B and C, as hereinafter defined, and mixtures thereof: Particles of Type A have the following characteristics: 1. A Friatest Index of about 70 to 90, for those particles of size 74 to 88 microns; 2. A metal content of about 1.0 to 1.5 percent by weight; 3. Predominantly translucent colour with the occasional transparent white, grey and yellow particle; 4. Predominantly blocky shape tending towards elongate particles; 5. Predominantly rough and undulating surface; Particles of Type B have the following characteristics: 1. Weak, having a Friatest Index of about 65 to 88, for those particles of size 74 to 88 microns; 2. A metal content of greater than 2 percent by weight; 3. Predominantly dark in colour;
Claim 3
Dependent Claim
76 words
A blocky and irregular shape; 5. Rough with surface irregularities, re-entrant angles and etch pits; Particles of Type C have the following characteristics: 1. Medium strength, having a Friatest Index in the range about 100 to 121 for those particles of size 74 to 88 microns; 2. A metal content of less than 0.8 percent by weight; 3. Predominantly yellow in colour; 4. An angular to blocky shape with sharp edges; 5. A predominantly smooth surface.
Claim 4
Dependent Claim
76 words
A blocky and irregular shape; 5. Rough with surface irregularities, re-entrant angles and etch pits; Particles of Type C have the following characteristics: 1. Medium strength, having a Friatest Index in the range about 100 to 121 for those particles of size 74 to 88 microns; 2. A metal content of less than 0.8 percent by weight; 3. Predominantly yellow in colour; 4. An angular to blocky shape with sharp edges; 5. A predominantly smooth surface.
Claim 5
Dependent Claim
48 words
A method according to claim 1 characterised in that the particles are a mixture of type A particles and particles of at least one type selected from the group consisting of type B and C, type A particles constituting at least 40 percent by weight of the mixture.
Claim 6
Dependent Claim
20 words
A method according to claim 2 wherein the particles of type A constitute 40-80 percent by weight of the mixture.
Claim 7
Dependent Claim
32 words
A method according to claim 2 wherein the mixture contains particles of type A, type B and type C, the particles of types B and C being present in substantially equal proportions.
Claim 8
Dependent Claim
34 words
A method according to claim 1 wherein the particles are a mixture consisting of 50 percent type A particles, and 25 percent of each of types B and C, all percentages being by weight.
Claim 9
Dependent Claim
26 words
A method according to claim 1 wherein the diamond abrasive particles which are used in the starting mixture have a size smaller than about 125 microns.
Claim 10
Dependent Claim
18 words
A method according to claim 1 wherein the aggregated particles have a size in the range 149-250 microns.
Claim 11
Dependent Claim
18 words
A method according to claim 4 wherein the aggregated particles have a size in the range 149-250 microns.
Claim 12
Dependent Claim
18 words
A method according to claim 1 wherein the aggregated particles have a size in the range 177-250 microns.
Claim 13
Dependent Claim
18 words
A method according to claim 4 wherein the aggregated particles have a size in the range 177-250 microns.
Claim 14
Dependent Claim
28 words
A method according to claim 1 wherein the metal is selected from silver, copper, tin, nickel, cobalt and iron and alloys containing one or more of these metals.
Claim 15
Dependent Claim
18 words
A method according to claim 11 wherein the metal or alloy has a melting point below 1200° C.
Claim 16
Dependent Claim
18 words
A method according to claim 11 wherein the metal or alloy has a melting point below 1000° C.
Claim 17
Dependent Claim
16 words
A method according to claim 1 wherein the metal powder consists of a powdered copper/silver alloy.
Claim 18
Dependent Claim
16 words
A method according to claim 8 wherein the metal powder consists of a powdered copper/silver alloy.
Claim 19
Dependent Claim
19 words
A method according to claim 1 wherein the powdered metal consists of a mixture of copper and silver powders.
Claim 20
Dependent Claim
19 words
A method according to claim 8 wherein the powdered metal consists of a mixture of copper and silver powders.
Claim 21
Dependent Claim
22 words
A method according to claim 1 wherein the mixture of diamond abrasive particles and metal powder also contains a diamond wetting agent.
Claim 22
Dependent Claim
22 words
A method according to claim 8 wherein the mixture of diamond abrasive particles and metal powder also contains a diamond wetting agent.
Claim 23
Dependent Claim
20 words
A method according to claim 18 wherein the diamond wetting agent is selected from titanium, zirconium, vanadium, chromium and silicon.
Claim 24
Dependent Claim
25 words
A method according to claim 18 wherein the diamond wetting agent is present in an amount of 5-15 percent by weight of the metal powders.
Claim 25
Dependent Claim
30 words
A method according to claim 1 wherein the amount of metal powder in the starting mixture is such as to produce aggregated particles containing 40-60 percent by weight of metal.
Claim 26
Dependent Claim
31 words
A method according to claim 1 wherein the amount of metal powder used in the starting mixture is such as to produce aggregated particles containing 55 percent by weight of metal.
Claim 27
Dependent Claim
20 words
A method according to claim 1 wherein sintering takes place at a temperature in the range 700° to 1200° C.
Claim 28
Dependent Claim
21 words
A method according to claim 24 wherein the sintering takes place at a temperature in the range 900° to 950° C.
Claim 29
Dependent Claim
18 words
A method according to claim 1 wherein sintering takes place for a period of 10 to 20 minutes.
Claim 30
Dependent Claim
18 words
A method according to claim 1 wherein the sintering and cooling takes place in a substantially non-oxidising atmosphere.
Claim 31
Dependent Claim
25 words
A method according to claim 27 wherein the non-oxidising atmosphere is selected from a non-oxidising gas and a vacuum of 10 -4 Torr or better.
Claim 32
Dependent Claim
14 words
A method according to claim 1 wherein the crushing is effected by shear crushing.
Claim 33
Dependent Claim
19 words
Aggregated diamond abrasive particles when produced by a method according to (any one of the preceding claims) claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-20 | 1984-07-21 | 1985-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-20 | 1988-07-21 | 1989-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-20 | 1992-07-21 | 1993-01-20 | $7700.00 | Window Closed / Lapsed |