Method for the continuous production of a co-extruded heat-shrinkable composite foamed resin sheet
Assignee: Graham Packaging Plastic Products Inc
•
Filing: 1979-03-26
•
Granted: 1981-01-13
•
Expires: 1999-03-26
Abstract
Abstract This invention relates to the treatment of plastic sheet material and especially co-extruded sheet of orientable plastic material which is comprised of film and foam layers which are continuously stretched in a longitudinal direction. The stretching is effected between a pair of rolls which are maintained at different temperatures and rotated at different rates of rotation to effect a cold stretching of the film-foam laminate to improve its shrink capability and lower its shrink temperature upon usage in various packaging applications. A preferred material is polyethylene which is co-extruded into a laminate of film and foam layers and which exhibits improved shrinkage characteristics when employed in the form of tubular sleeves for container labels or bands.
Inventors
- 👤 James E. Heider
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 15:31
CPC Classifications
B; B29; B29C; B29C55/00; B29C55/02; B29C55/023; B32; B32B; B32B27/00; B32B27/06; B32B27/065; B29C55/18; B29C61/00; B29C61/06; B29C61/0608; B29C61/0616; B32B27/32; B32B38/00; B32B38/0012; B32B5/00; B32B5/18; B29C48/00; B29C48/001; B29C48/0018; B29C48/03; B29C48/07; B29C48/08; B29C48/16; B29C48/18; B29C48/21; B29K; B29K2023/00; B29K2023/04; B29K2023/06; B29K2105/00; B29K2105/04; B29L; B29L2023/00; B29L2023/001; B32B2038/0028; B32B2266/00; B32B2266/02; B32B2266/0214; B32B2266/025; B32B2305/00; B32B2305/02; B32B2305/022; B32B2307/00; B32B2307/40; B32B2307/406; B32B2307/50; B32B2307/514; B32B2307/70; B32B2307/732; B32B2307/734; B32B2307/736; B32B2309/00; B32B2309/08; B32B2309/10; B32B2309/105; B32B2323/00; B32B2323/04
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
136 words
The method of continuously producing a heat-shrinkable oriented film and foam thermoplastic polyolefin sheet material comprising the steps of co-extruding a layer of film and a layer of foam of said thermoplastic polyolefin material in tubular form, initially stretching the said co-extruded sheet of film and foam thermoplastic material in both longitudinal and transverse directions immediately following its co-extrusion, as a first step; and secondarily stretching the said co-extruded sheet longitudinally by feeding said sheet between the closely spaced peripheral surfaces of a pair of rolls rotating at different peripheral surface speeds, as a subsequent second step; said second step being effected with the temperature of said sheet below the melt point temperature of the polyolefin material, said sheet being lengthened in the range of 50% to 70% of its initially-stretched length by such secondary stretching.
Claim 2
Independent Claim
136 words
The method of continuously producing a heat-shrinkable oriented film and foam thermoplastic polyolefin sheet material comprising the steps of co-extruding a layer of film and a layer of foam of said thermoplastic polyolefin material in tubular form, initially stretching the said co-extruded sheet of film and foam thermoplastic material in both longitudinal and transverse directions immediately following its co-extrusion, as a first step; and secondarily stretching the said co-extruded sheet longitudinally by feeding said sheet between the closely spaced peripheral surfaces of a pair of rolls rotating at different peripheral surface speeds, as a subsequent second step; said second step being effected with the temperature of said sheet below the melt point temperature of the polyolefin material, said sheet being lengthened in the range of 50% to 70% of its initially-stretched length by such secondary stretching.
Claim 3
Dependent Claim
30 words
The method in accordance with claim 1, wherein the adjacent surfaces of said pair of rolls are spaced apart tangentially by a gap ranging from about 15 to 20 mils.
Claim 4
Dependent Claim
34 words
The method in accordance with claim 1, wherein one of said rolls is maintained at a temperature ranging from about 140° F. to 150° F. and the other roll is maintained at ambient temperature.
Claim 5
Dependent Claim
43 words
The method in accordance with claim 1, wherein said co-extruded film and foam sheet is secondarily stretched to reduce its thickness from about 12 mils to about 6 mils to lower the shrink temperature of the material and provide greater total shrink capability.
Claim 6
Dependent Claim
32 words
The method in accordance with claim 1, wherein said pair of rolls have similar cylindrical contours and are operated at different rates of rotation having a ratio of about 2 to 1.
Claim 7
Dependent Claim
36 words
The method in accordance with claim 1, wherein said co-extruded film and foam sheet is mechanically stressed by said secondary stretching operation to provide greater contraction upon heat shrinkage of said sheet around a rigid article.
Claim 8
Dependent Claim
30 words
The method in accordance with claim 1, wherein said co-extruded film and foam sheet is comprised of polyethylene, the film surface having high gloss and smoothness to facilitate its decoration.
References Cited (Backward Citations)
US2778057A
Cited
GB954069A
Cited
US3076232A
Cited
US3558764A
Cited
US3536797A
Cited
US3855376A
Cited
US4038446A
Cited
US4071597A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-13 | 1984-07-14 | 1985-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-13 | 1988-07-14 | 1989-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-13 | 1992-07-14 | 1993-01-13 | $7700.00 | Window Closed / Lapsed |