Method of preparing porous, rigid ceramic separators for an electrochemical cell
Assignee: United States Department of Energy
•
Filing: 1979-03-30
•
Granted: 1981-01-13
•
Expires: 1999-03-30
Abstract
Abstract Porous, rigid separators for electrochemical cells are prepared by first calcining particles of ceramic material at temperatures above about 1200° C. for a sufficient period of time to reduce the sinterability of the particles. A ceramic powder that has not been calcined is blended with the original powder to control the porosity of the completed separator. The ceramic blend is then pressed into a sheet of the desired shape and sintered at a temperature somewhat lower than the calcination temperature. Separator sheets of about 1 to 2.5 mm thickness and 30 to 70% porosity can be prepared by this technique. Ceramics such as yttria, magnesium oxide and magnesium-aluminum oxide have advantageously been used to form separators by this method.
Inventors
- 👤 Gautam Bandyopadhyay
- 👤 Joseph T. Dusek
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 15:53
CPC Classifications
C; C04; C04B; C04B38/00; H; H01; H01M; H01M50/00; H01M50/40; H01M50/409; H01M50/431; H01M50/434; H01M50/489; H01M50/491; C04B2111/00; C04B2111/00474; C04B2111/00853; H01M2300/00; H01M2300/0017; H01M2300/0048; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
117 words
A metod of preparing a porous, rigid ceramic sheet for use as an interelectrode separator in an electrochemical cell comprising: calcining particulate ceramic material at a first temperature to agglomerate particles and reduce the ability of the ceramic material to sinter and densify into an integral mass; blending additional particulate ceramic material with said calcinced material, said additional material having smaller particle size and greater ability to sinter and densify into an integral mass than said agglomerated calcined material; pressing said blend of ceramic material to form a compacted sheet; and sintering said compacted sheet at a second temperature below said first temperature to form a rigid, porous separator for use between electrodes in an electrochemical cell.
Claim 2
Dependent Claim
117 words
A metod of preparing a porous, rigid ceramic sheet for use as an interelectrode separator in an electrochemical cell comprising: calcining particulate ceramic material at a first temperature to agglomerate particles and reduce the ability of the ceramic material to sinter and densify into an integral mass; blending additional particulate ceramic material with said calcinced material, said additional material having smaller particle size and greater ability to sinter and densify into an integral mass than said agglomerated calcined material; pressing said blend of ceramic material to form a compacted sheet; and sintering said compacted sheet at a second temperature below said first temperature to form a rigid, porous separator for use between electrodes in an electrochemical cell.
Claim 3
Dependent Claim
35 words
The method of claim 1 wherein said first temperature is about 30° to 100° C. higher than said second temperature and wherein both said first and second temperatures are between about 1200° and 1600° C.
Claim 4
Dependent Claim
43 words
The method of claim 1 wherein said ceramic material is selected from the group of metal oxides consisting of Y 2 O 3 , MgO, MgAl 2 O 4 , CaZrO 3 , LiaZrO 3 , LiAlO 2 and combinations of these oxides.
Claim 5
Dependent Claim
18 words
The method of claim 3 wherein said ceramic materials are selected from Y 2 O 3 and MgO.
Claim 6
Dependent Claim
25 words
The method of claim 1 wherein said particles of ceramic material have an average particle size of about 0.5 to 5 microns prior to calcination.
Claim 7
Dependent Claim
42 words
The method of claim 1 wherein said additional ceramic particles are of about 0.5 to 5 microns particle size and are blended into said calcined ceramic particles in amounts sufficient to provide about 5 to 10% by weight of the total mass.
Claim 8
Dependent Claim
20 words
The method of claim 1 wherein said calcining and sintering are performed at temperatures of about 1200° to 1600° C.
Claim 9
Dependent Claim
37 words
The method of claim 1 wherein said blend of ceramic material is pressed into a sheet of about 1 to 2.5 mm thickness and sintered to form a rigid porous sheet of about 30 to 70% porosity.
Claim 10
Dependent Claim
26 words
The method of claim 1 wherein said sintering of the compacted sheet is performed with a uniform load bearing upon the major surfaces of the sheet.
Claim 11
Dependent Claim
29 words
The method of claim 1 wherein said compacted sheet has rectangular major surfaces and is rounded at each corner to remove portions of high density gradient prior to sintering.
Claim 12
Independent Claim
128 words
A method of preparing a rigid ceramic sheet of 30-70% porosity for use as an interelectrode separator in an electrochemical cell comprising: providing particulate ceramic material having average particle size of 0.5 to 5 microns; calcining a major portion of said particulate ceramic material at a first temperature to agglomerate particles and reduce the ability of the ceramic material to sinter and densify into an integral mass; blending a remaining minor portion of said particulate ceramic material that was not subjected to said calcining step with said calcined agglomerated particles; pressing said blend of ceramic material to form a compacted sheet; and sintering said compacted sheet at a second temperature below said first temperature to form a rigid porous separator for use between electrodes in an electrochemical cell.
Claim 13
Independent Claim
128 words
A method of preparing a rigid ceramic sheet of 30-70% porosity for use as an interelectrode separator in an electrochemical cell comprising: providing particulate ceramic material having average particle size of 0.5 to 5 microns; calcining a major portion of said particulate ceramic material at a first temperature to agglomerate particles and reduce the ability of the ceramic material to sinter and densify into an integral mass; blending a remaining minor portion of said particulate ceramic material that was not subjected to said calcining step with said calcined agglomerated particles; pressing said blend of ceramic material to form a compacted sheet; and sintering said compacted sheet at a second temperature below said first temperature to form a rigid porous separator for use between electrodes in an electrochemical cell.
Claim 14
Dependent Claim
33 words
The method of claim 11 wherein said remaining minor portion of ceramic material is blended into said calcined ceramic particles in amounts sufficient to provide about 5-10% by weight of the total mass.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-13 | 1984-07-14 | 1985-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-13 | 1988-07-14 | 1989-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-13 | 1992-07-14 | 1993-01-13 | $7700.00 | Window Closed / Lapsed |