High surface area catalysts
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1978-10-30
•
Granted: 1981-01-13
•
Expires: 1998-10-30
Abstract
Abstract High surface area metal-containing catalysts are prepared by dispersing a thermally decomposable metal compound in a hydrocarbon oil having a Conradson carbon content of up to about 50 weight percent, the thermally decomposable metal compound being added in an amount sufficient to obtain a specified ratio of atoms of Conradson carbon of the oil chargestock to atoms of metal constituent of the thermally decomposable compound, heating the compound in the presence of a gas comprising either hydrogen or hydrogen sulfide or hydrogen and hydrogen sulfide to form a solid high surface area catalyst within the oil, and recovering the resulting high surface area catalyst. The metal constituent of the thermally decomposable metal compound may be a metal of Groups II, III, IV, V, VIB, VIIB, VIII or mixtures thereof. The high surface area solids are suitable as catalysts, catalyst supports or catalyst components for use in hydrocarbon treating processes and in chemical processes.
Inventors
- 👤 Clyde L. Aldridge
- 👤 Roby Bearden, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 21:36
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/08; B01J37/082; B01J37/086; C; C10; C10G; C10G11/00; C10G11/02; C10G35/00; C10G35/04; C10G35/06; C10G49/00; C10G49/02; Y; Y10; Y10S; Y10S208/00; Y10S208/951
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
159 words
A high surface area catalyst prepared by the steps which comprise: (a) dispersing in hydrocarbon oil chargestock having a Conradson carbon content up to about 50 weight percent, a thermally decomposable metal compound in an amount sufficient to provide a ratio of atoms of oil chargestock Conradson carbon to atoms of metal constituent of said thermally decomposable metal compound of less than about 750 to 1, said metal constituent being selected from the group consisting of Group II, Group III, Group IV, Group V, Group VIB, Group VIIB, and Group VIII of the Periodic Table of Elements and mixtures thereof; (b) heating said thermally decomposable metal compound within said chargestock at an elevated temperature in the presence of a gas selected from the group consisting of hydrogen-containing gas, a hydrogen sulfide-containing gas, and a gas comprising hydrogen and hydrogen sulfide to produce a solid high surface area catalyst within said chargestock, and (c) recovering said high surface area catalyst.
Claim 2
Dependent Claim
159 words
A high surface area catalyst prepared by the steps which comprise: (a) dispersing in hydrocarbon oil chargestock having a Conradson carbon content up to about 50 weight percent, a thermally decomposable metal compound in an amount sufficient to provide a ratio of atoms of oil chargestock Conradson carbon to atoms of metal constituent of said thermally decomposable metal compound of less than about 750 to 1, said metal constituent being selected from the group consisting of Group II, Group III, Group IV, Group V, Group VIB, Group VIIB, and Group VIII of the Periodic Table of Elements and mixtures thereof; (b) heating said thermally decomposable metal compound within said chargestock at an elevated temperature in the presence of a gas selected from the group consisting of hydrogen-containing gas, a hydrogen sulfide-containing gas, and a gas comprising hydrogen and hydrogen sulfide to produce a solid high surface area catalyst within said chargestock, and (c) recovering said high surface area catalyst.
Claim 3
Dependent Claim
32 words
The catalyst of claim 1 wherein said thermally decomposable metal compound is selected from the group consisting of inorganic metal compounds, salts of organic acids, organometallic compounds and salts of organic amines.
Claim 4
Dependent Claim
31 words
The catalyst of claim 1 wherein said thermally decomposable metal compound is selected from the group consisting of salts of acyclic aliphatic carboxylic acids and salts of alicyclic aliphatic carboxylic acids.
Claim 5
Dependent Claim
18 words
The catalyst of claim 1 wherein said thermally decomposable metal compound is a salt of a naphthenic acid.
Claim 6
Dependent Claim
33 words
The catalyst of claim 1 wherein the metal constituent of said thermally decomposable metal compound is selected from the group consisting of molybdenum, tungsten, chromium, vanadium, cobalt, titanium, iron, nickel and mixtures thereof.
Claim 7
Dependent Claim
14 words
The catalyst of claim 1 wherein said thermally decomposable metal compound is molybdenum naphthenate.
Claim 8
Dependent Claim
14 words
The catalyst of claim 1 wherein said thermally decomposable metal compound is phosphomolybdic acid.
Claim 9
Dependent Claim
15 words
The catalyst of claim 1 wherein said gas of step (b) is a hydrogen-containing gas.
Claim 10
Dependent Claim
16 words
The catalyst of claim 1 wherein said gas of step (b) is a hydrogen sulfide-containing gas.
Claim 11
Dependent Claim
19 words
The catalyst of claim 1 wherein said gas of step (b) is a gas comprising hydrogen and hydrogen sulfide.
Claim 12
Dependent Claim
22 words
The catalyst of claim 1 wherein said gas of step (b) comprises from about 1 to about 90 mole percent hydrogen sulfide.
Claim 13
Dependent Claim
22 words
The catalyst of claim 1 wherein said gas of step (b) comprises from about 2 to about 50 mole percent hydrogen sulfide.
Claim 14
Dependent Claim
26 words
The catalyst of claim 1 wherein said gas of step (b) is present in an amount sufficient to provide a pressure of at least 50 psig.
Claim 15
Dependent Claim
21 words
The catalyst of claim 1 wherein said elevated temperature of step (b) ranges from about 199° C. to about 571° C.
Claim 16
Dependent Claim
21 words
The catalyst of claim 1 wherein said elevated temperature of step (b) ranges from about 260° C. to about 482° C.
Claim 17
Dependent Claim
21 words
The catalyst of claim 1 wherein said elevated temperature of step (b) ranges from about 316° C. to about 449° C.
Claim 18
Dependent Claim
23 words
The catalyst of claim 1 wherein said heating of step (b) is conducted at a total pressure ranging up to about 5000 psig.
Claim 19
Dependent Claim
23 words
The catalyst of claim 1 wherein said atomic ratio of Conradson carbon to said metal constituent is less than about 600 to 1.
Claim 20
Dependent Claim
23 words
The catalyst of claim 1 wherein said atomic ratio of Conradson carbon to said metal constituent is less than about 100 to 1.
Claim 21
Dependent Claim
26 words
The catalyst of claim 1 wherein said atomic ratio of Conradson carbon to metal constituent ranges from about 2 to 1 to about 600 to 1.
Claim 22
Dependent Claim
20 words
The catalyst of claim 1 wherein said hydrocarbon oil chargestock has an atmospheric pressure boiling point above about 221° C.
Claim 23
Dependent Claim
20 words
The catalyst of claim 1 wherein said hydrocarbon oil chargestock has an atmospheric pressure boiling point above about 260° C.
Claim 24
Dependent Claim
18 words
The catalyst of claim 1 wherein said added thermally decomposable metal compound comprises a mixture of metal compounds.
Claim 25
Dependent Claim
22 words
The catalyst of claim 23 wherein said mixture of added thermally decomposable metal compounds comprises a molybdenum compound and a cobalt compound.
Claim 26
Dependent Claim
26 words
The catalyst of claim 1 wherein at least one additional catalytic metal component for hydrocarbon treating processes is composited with said recovered high surface area catalyst.
Claim 27
Dependent Claim
21 words
The catalyst of claim 25 wherein said additional catalytic metal component is composited with said high surface area catalyst by impregnation.
Claim 28
Dependent Claim
33 words
The catalyst of claim 25 wherein said additional metal component is composited with said high surface area catalyst by depositing the additional catalytic component or precursor thereof on said high surface area catalyst.
Claim 29
Dependent Claim
23 words
The high surface area catalyst of claim 1 wherein said catalyst has a surface area of at least about 50 m 2 /g.
Claim 30
Dependent Claim
41 words
The high surface area catalyst of claim 1 wherein said metal constituent of said thermally decomposable compound is present in said catalyst in an amount of at least 10 weight percent, calculated as the elemental metal, based on the total catalyst.
References Cited (Backward Citations)
US1876270A
Cited
US2091831A
Cited
US3131142A
Cited
US3161585A
Cited
US3331769A
Cited
US3657111A
Cited
US4125455A
Cited
US4032435A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-13 | 1984-07-14 | 1985-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-13 | 1988-07-14 | 1989-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-13 | 1992-07-14 | 1993-01-13 | $7700.00 | Window Closed / Lapsed |