Abrasive composition for use in toothpaste
Assignee: JM Huber Corp
•
Filing: 1978-09-28
•
Granted: 1981-01-13
•
Expires: 1998-09-28
Abstract
Abstract The corrosion and staining of unlined aluminum tube surfaces by dentifrices such as toothpastes, particularly when the dentifrices contain therapeutic agents, is substantially prevented by incorporation into the dentifrice of a controlled amount of an alkaline earth metal ion such as calcium ion, in the range of 0.005-0.2 weight percent, and preferably in the range of 0.005-0.070 weight percent of the dentifrice. The alkaline earth metal may be provided from any water soluble alkaline earth metal salt or as a reaction product of the alkaline earth metal salt with an amorphous silica abrasive and/or thickener.
Inventors
- 👤 Satish K. Wason
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 15:25
CPC Classifications
A; A61; A61Q; A61Q11/00; A61K; A61K8/00; A61K8/18; A61K8/19; A61K8/20; A61K8/21; A61K8/25; C; C09; C09C; C09C1/00; C09C1/28; C09C1/30; C09C1/3045; C09C1/3054; A61K2800/00; A61K2800/40; A61K2800/52; A61K2800/526; C01; C01P; C01P2002/00; C01P2002/02; C01P2004/00; C01P2004/50; C01P2004/60; C01P2004/61; C01P2006/00; C01P2006/10; C01P2006/12; C01P2006/19
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
120 words
An abrasive composition useful for incorporation into a therapeutic toothpaste composition and which will provide abrasive characteristics for the toothpaste composition at RDA values of 200-400 and will prevent fluoride-caused corrosion and staining of an unlined aluminum tube containing said toothpaste composition, said abrasive composition consisting essentially of a dentifrice-grade silica polishing agent which has been treated with a sufficient amount of a food grade alkaline earth metal compound selected from the group consisting of the hydroxide, oxide, nitrate, chloride, acetate, or formate of calcium, magnesium, and strontium, and mixtures thereof, so as to have present therein from about 168-7000 ppm of the alkaline earth metal in said composition, said silica functioning as a carrier for the alkaline earth metal.
Claim 2
Dependent Claim
120 words
An abrasive composition useful for incorporation into a therapeutic toothpaste composition and which will provide abrasive characteristics for the toothpaste composition at RDA values of 200-400 and will prevent fluoride-caused corrosion and staining of an unlined aluminum tube containing said toothpaste composition, said abrasive composition consisting essentially of a dentifrice-grade silica polishing agent which has been treated with a sufficient amount of a food grade alkaline earth metal compound selected from the group consisting of the hydroxide, oxide, nitrate, chloride, acetate, or formate of calcium, magnesium, and strontium, and mixtures thereof, so as to have present therein from about 168-7000 ppm of the alkaline earth metal in said composition, said silica functioning as a carrier for the alkaline earth metal.
Claim 3
Dependent Claim
88 words
The abrasive composition of claim 1 wherein said silica is selected from the group consisting of amorphous precipitated silica, sodium aluminosilicates, silica xerogels and mixtures thereof; said abrasive composition being prepared, when amorphous precipitated silica is selected as the silica, by preparation of an amorphous silicon dioxide by precipitation through acidulation of an alkali metal silicate solution with a mineral acid in the presence of an alkali metal sulfate, isolating a wet cake of said precipitated product, and treating said wet cake with said alkaline earth metal compound.
Claim 4
Dependent Claim
42 words
The abrasive composition of claim 2 wherein said amorphous precipitated silica has the following properties: ______________________________________
Oil Absorption-Rub-Out Method (cc/100g)
= 80-120
BET Surface Area (m.sup.2 /g)
= 75-135
MSA Average Aggregate Size (microns)
= 1-10
Bulk Density (lbs./cu.ft.)
= 10-30
______________________________________
Claim 5
Dependent Claim
41 words
The abrasive composition of claim 2 wherein said sodium aluminosilicates have the following properties: ______________________________________
Oil Absorption-Rub-Out Method (cc/100g)
= 75-125
BET Surface Area (m.sup.2 /g)
= 50-300
MSA Average Aggregate Size (microns)
= 1-10
Bulk Density (lbs./cu.ft.)
= 12-35
______________________________________
Claim 6
Dependent Claim
19 words
The abrasive composition of claim 1 wherein the amount of alkaline earth metal present ranges from about 336-7000 ppm.
Claim 7
Dependent Claim
29 words
The abrasive composition of claim 1 wherein the water-soluble alkaline earth metal compound is selected from the group consisting of calcium hydroxide, calcium oxide, calcium nitrate and calcium chloride.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-13 | 1984-07-14 | 1985-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-13 | 1988-07-14 | 1989-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-13 | 1992-07-14 | 1993-01-13 | $7700.00 | Window Closed / Lapsed |