Abstract In a process wherein an organic coating is formed on a metallic surface by immersing the surface in an acidic aqueous coating composition containing dispersed particles of an organic coating-forming material from which the particles are deposited on the metallic surface forming an organic coating which increases in thickness the longer the surface is immersed in the composition and wherein the temperature of the coating composition tends to rise with the result that the quality of coatings formed therefrom is affected adversely, particularly when coating worked or roughened metal surfaces, the improvement comprising maintaining the temperature of the coating composition at a temperature within the range over which the rate of change in the rate of film build is substantially constant thereby improving the quality of the coating formed by the deposition of coating-forming particles, including reducing or preventing the tendency of the composition to form coatings which contain pinholes and/or craters.
In an autodepositing coating process wherein an acidic aqueous solution having coating forming organic resin particles dispersed therein is applied to a worked or roughened ferrous metal surface by immersing said surface in a coating bath containing said solution to produce on the surface a coating which increases in thickness during the time the surface is immersed in the solution, the rate at which the coating increases in thickness being greater at high temperatures, and wherein the coating is fused to form a film having surface defects including pinholes and craters; the improvement comprising carrying out the coating process by maintaining the temperature between about 65° F. and about 75° F. by cooling the coating composition by means of a heat exchanger immersed in the bath or surrounding the bath only at times when the temperature has a tendency to rise thereby to eliminate pinholes and craters in the fused coating.
Claim 2
Dependent Claim
151 words
In an autodepositing coating process wherein an acidic aqueous solution having coating forming organic resin particles dispersed therein is applied to a worked or roughened ferrous metal surface by immersing said surface in a coating bath containing said solution to produce on the surface a coating which increases in thickness during the time the surface is immersed in the solution, the rate at which the coating increases in thickness being greater at high temperatures, and wherein the coating is fused to form a film having surface defects including pinholes and craters; the improvement comprising carrying out the coating process by maintaining the temperature between about 65° F. and about 75° F. by cooling the coating composition by means of a heat exchanger immersed in the bath or surrounding the bath only at times when the temperature has a tendency to rise thereby to eliminate pinholes and craters in the fused coating.
Claim 3
Dependent Claim
22 words
The coating process of claim 1 wherein the coating composition comprises ferric fluoride, hydrofluoric acid, a pigment and a styrene butadiene latex.
Claim 4
Dependent Claim
71 words
The coating process of claim 1 wherein the coating composition contains the equivalent of about 0.5 to about 3.5 g/l of ferric iron, about 0.2 to about 5.0 g/l of hydrofluoric acid, about 5.0 g/l of a carbon black pigment dispersion and about 50 to about 100 g/l of resin particles added as a latex containing particles of resin prepared by copolymerizing butadiene, styrene, a vinyl halide and an acrylic acid.