Method for preparing aluminosilicates, their use as catalyst supports and catalysts, and method for producing catalysts therefrom
Assignee: BP PLC
•
Filing: 1978-12-11
•
Granted: 1980-12-30
•
Expires: 1998-12-11
Abstract
Abstract Aluminosilicates containing an organic nitrogen cation are prepared by mixing sources of silica, alumina and an alkali metal, water and either mono-ethanolamine or mono-propanolamine, or a derivative, or the precursors or a combination thereof and maintaining the mixture at a temperature in the range from 80° to 210° C. and a pressure in the range from 70 to 400 psig for over 4 hours. In a preferred embodiment the alkanolamines are prepared in situ` by reaction of the corresponding alkylene oxide with ammonia. Aluminosilicates so-prepared can be used without modification as catalysts and catalyst supports. Catalytic activity can be enhanced by, for example, reducing the sodium content or impregnating with a compound of one or more metals belonging to Groups 1B, 11B, 111A, 1VA, VA and V111 or reaction with a compound of one or more non-metals of Group 111A and VA of the Periodic Table.
Inventors
- 👤 William J. Ball
- 👤 Keith W. Palmer
- 👤 David G. Stewart
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 19:33
CPC Classifications
C; C01; C01B; C01B33/00; C01B33/20; C01B33/26; C01B33/28; C01B33/2807; C01B33/2876; B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/40; Y; Y02; Y02P; Y02P30/00; Y02P30/20; Y02P30/40; Y10; Y10S; Y10S423/00; Y10S423/22
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
106 words
A method for preparing a crystalline aluminosilicate which method comprises mixing a source of silica, a source of alumina, a source of alkali metal, water and at least one monoalkanolamine selected from the group consisting of mono-ethanolamine and mono-propanolamine, said source of silica to said source of alumina being in the range of from 10:1 to 150:1 based on the equivalent moles of silica and alumina in the respective sources, and maintaining the mixture at a temperature in the range of from about 80° to 210° C. and a pressure in the range from about 70 to 400 psig for a time greater than four hours.
Claim 2
Independent Claim
106 words
A method for preparing a crystalline aluminosilicate which method comprises mixing a source of silica, a source of alumina, a source of alkali metal, water and at least one monoalkanolamine selected from the group consisting of mono-ethanolamine and mono-propanolamine, said source of silica to said source of alumina being in the range of from 10:1 to 150:1 based on the equivalent moles of silica and alumina in the respective sources, and maintaining the mixture at a temperature in the range of from about 80° to 210° C. and a pressure in the range from about 70 to 400 psig for a time greater than four hours.
Claim 3
Independent Claim
95 words
A method for preparing an aluminosilicate which method comprises mixing a source of silica, a source of alumina, a source of alkali-metal, water and a monoalkanolamine selected from the group consisting of mono-ethanolamine and mono-propanolamine and monoalkanolamine formed in situ from an alkylene oxide selected from the group consisting of ethylene oxide, propylene oxide and combinations thereof and ammonia, and maintaining the mixture at a temperature in the range of from about 80° to 210° C. and a pressure in the range from about 70 to 400 psig for a time greater than four hours.
Claim 4
Independent Claim
95 words
A method for preparing an aluminosilicate which method comprises mixing a source of silica, a source of alumina, a source of alkali-metal, water and a monoalkanolamine selected from the group consisting of mono-ethanolamine and mono-propanolamine and monoalkanolamine formed in situ from an alkylene oxide selected from the group consisting of ethylene oxide, propylene oxide and combinations thereof and ammonia, and maintaining the mixture at a temperature in the range of from about 80° to 210° C. and a pressure in the range from about 70 to 400 psig for a time greater than four hours.
Claim 5
Independent Claim
53 words
A method according to either one of claims 1 and 2 wherein said source of silica is an aqueous colloidal dispersion of silica particles, said source of alumina is sodium aluminate prepared by dissolving alumina particles in excess sodium hydroxide solution and said alkali metal is sodium in the form of sodium hydroxide.
Claim 6
Independent Claim
28 words
A method according to either one of claims 1 and 2 wherein said mono-alkanolamine is mono-ethanolamine or the precursors thereof, said precursors consisting of ethylene oxide and ammonia.
Claim 7
Independent Claim
96 words
A method according to either one of claims 1 and 2 wherein, in said mixture, the ratio of said silica source to said alumina source is in the range 10:1 to 150:1 based on the equivalent moles of silica and alumina in the respective sources, said alkali metal source is present in an amount from 50 to 0.02 moles per mole equivalent of total silica and alumina in their respective sources and said alkanolamine is present in an amount from 50 to 0.02 moles per mole equivalent of total silica and alumina in their respective sources.
Claim 8
Dependent Claim
28 words
A method according to claim 15 wherein the molar ratio of said ammonia to said alkylene oxide in said mixture is in the range from 10:1 to 2:1.
Claim 9
Dependent Claim
45 words
A method as defined in claim 1 wherein the aluminosilicate obtained is impregnated with a compound of one or more metals selected from the group consisting of copper, silver, zinc, gallium, indium, thallium, lead, antimony, bismuth, iron, cobalt, nickel, ruthenium, rhodium, palladium, iridium, and platinum.
Claim 10
Dependent Claim
23 words
A method as defined in claim 1 wherein a boron compound is incorporated into the aluminosilicate obtained and the admixture is then heated.
Claim 11
Dependent Claim
23 words
A method as defined in claim 1 wherein a phosphorus compound is incorporated into the aluminosilicate obtained and the admixture is then heated.
References Cited (Backward Citations)
GB1161974A
Cited
DE1955095A1
Cited
US3702886A
Cited
GB1365318A
Cited
GB1471440A
Cited
US4089929A
Cited
DE2817577A1
Cited
DE2746844A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-30 | 1984-06-30 | 1984-12-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-30 | 1988-06-30 | 1988-12-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-30 | 1992-06-30 | 1992-12-30 | $7700.00 | Window Closed / Lapsed |