Abstract Lubricants and processing aids for synthetic fibers, particularly polyester and nylon fibers, are disclosed comprising compounds having the structural formulas: ##STR1## in which R is an aliphatic group generally having about 3 to about 22 carbon atoms; A is a mixture of residues from ethylene oxide and at least one other lower alkylene oxide, preferably a heteric mixture of oxyethylene and oxypropylene residues in the respective ratio by weight of 20:80 to 90:10; and n has a value to produce a molecular weight of about 300 to about 3000. Where liquid products are desired which contain the higher numbered carbon chain residues, low viscosity compounds can be obtained by oxyalkylating a glycerol-1,3-dialkylether with a mixture of ethylene oxide and 1,2-propylene oxide in the respective ratio as set forth above. Thus it is possible by properly balancing the carbon chain length of the R groups in the lubricant compounds of the invention with the oxyalkylene chain length to obtain products varying between water insoluble and water soluble. The oxyalkylated fiber lubricants of the invention have the properties of viscous liquids, solids or pastes at ambient temperature.
The process of preparing a fiber lubricating compound having the structural formula: ##STR4## wherein R is an alkyl radical having about 3 to about 22 carbon atoms; A is a mixture of the residues of ethylene oxide and another lower alkylene oxide; n has a value to produce a molecular weight of about 300 to about 3000; and said compound is the oxyalkylation product of a glycerol-1,3-dialkylether comprising a. reacting a fatty alcohol having 3 to about 22 carbon atoms with epihalohydrin catalyzed with a Lewis acid catalyst followed by treatment with a base to form an alkoxyglycidyl ether, b. reacting said alkoxyglycidyl ether with an excess of a fatty alcohol having 3 to about 22 carbon atoms, wherein said alcohol can be the same or different than said alcohol in part (a), in the presence of a Lewis acid catalyst, c. recovering the gycerol-1,3-dialkylether intermediate produced, and d. alkoxylating said intermediate with ethylene oxide and another alkylene oxide under alkaline catalysis at a temperature of about 110° to 135° C.
Claim 2
Dependent Claim
171 words
The process of preparing a fiber lubricating compound having the structural formula: ##STR4## wherein R is an alkyl radical having about 3 to about 22 carbon atoms; A is a mixture of the residues of ethylene oxide and another lower alkylene oxide; n has a value to produce a molecular weight of about 300 to about 3000; and said compound is the oxyalkylation product of a glycerol-1,3-dialkylether comprising a. reacting a fatty alcohol having 3 to about 22 carbon atoms with epihalohydrin catalyzed with a Lewis acid catalyst followed by treatment with a base to form an alkoxyglycidyl ether, b. reacting said alkoxyglycidyl ether with an excess of a fatty alcohol having 3 to about 22 carbon atoms, wherein said alcohol can be the same or different than said alcohol in part (a), in the presence of a Lewis acid catalyst, c. recovering the gycerol-1,3-dialkylether intermediate produced, and d. alkoxylating said intermediate with ethylene oxide and another alkylene oxide under alkaline catalysis at a temperature of about 110° to 135° C.
Claim 3
Dependent Claim
44 words
The process of claim 1 wherein said alcohol has about 10 to about 22 carbon atoms, said epihalohydrin is epichlorohydrin, and A is derived from a heteric mixture of ethylene oxide and 1,2-propylene oxide in the respective ratio by weight of 20:80 to 90:10.