Fluxless brazing of aluminum in inert gas
Assignee: Ford Motor Co
•
Filing: 1978-03-13
•
Granted: 1980-12-23
•
Expires: 1998-03-13
Abstract
Abstract A method of brazing aluminum parts in an inert gas atmosphere is disclosed. The brazed filler metal is controlled to contain a ternary alloy of aluminum-silicon-magnesium and the base aluminum parts are controlled to contain a binary alloy of aluminum-magnesium. Magnesium in the base metal is controlled to 0.4-1.2% and in the filler metal it is controlled to 0.2-0.6%; in the filler metal only, silicon is controlled to 7-12%. The assembled base metal parts and filler metal are subjected to differential heating rates, one rate being limited to at least 50° C./minute when the metal parts reach temperatures in the range of 400°-550° C., and a conventional rate when outside said temperature zone. As a result, three physical parameters are caused to occur simultaneously: initiation of porosity in oxide film on the metal parts, transport of magnesium to the oxide interface and reaction with the oxide, and initial melting of the filler metal as well as wettings of the oxide by the filler metal.
Inventors
- 👤 Duane J. Schmatz
- 👤 Walter L. Winterbottom
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:13
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/28; B23K35/286; B23K1/00; B23K1/008; B23K2101/00; B23K2101/04; B23K2101/14
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
134 words
A method of brazing of aluminum parts in a gas atmosphere containing gaseous species of O 2 in a concentration below 10 ppm and H 2 O in a concentration below 10 ppm, the method comprising: (a) preparing and structurally relating together aluminum or aluminum alloy parts to form an assembly having joining sites, (b) depositing a filler metal alloy at the joining sites of said assembly, said filler metal alloy consisting essentially of 7.5-12% silicon, 0.2-0.6% magnesium and the remainder essentially aluminum and normal residuals, (c) subjecting said assembly and deposited filler metal to heat to effect brazing while exposed to said gas atmosphere, said atmosphere being at or about an ambient pressure condition, said heat being applied at a rate to minimize formation of a magnesium oxide film at the joining sites.
Claim 2
Independent Claim
134 words
A method of brazing of aluminum parts in a gas atmosphere containing gaseous species of O 2 in a concentration below 10 ppm and H 2 O in a concentration below 10 ppm, the method comprising: (a) preparing and structurally relating together aluminum or aluminum alloy parts to form an assembly having joining sites, (b) depositing a filler metal alloy at the joining sites of said assembly, said filler metal alloy consisting essentially of 7.5-12% silicon, 0.2-0.6% magnesium and the remainder essentially aluminum and normal residuals, (c) subjecting said assembly and deposited filler metal to heat to effect brazing while exposed to said gas atmosphere, said atmosphere being at or about an ambient pressure condition, said heat being applied at a rate to minimize formation of a magnesium oxide film at the joining sites.
Claim 3
Dependent Claim
18 words
A method of brazing as in claim 1, in which the filler metal alloy additionally contains 0.1-0.15% bismuth.
Claim 4
Dependent Claim
56 words
A method of brazing as in claim 1, in which said parts comprise core cladded sheets, the core consisting of a binary alloy of aluminum-magnesium, the magnesium content in the core being limited to 0.4-1.2%, the clad consisting of a ternary alloy of aluminum-silicon-magnesium, with the magnesium being limited to 0.2-6% and silicon limited to 7-12%.
Claim 5
Dependent Claim
25 words
The method as in claim 1, in which said parts are comprised of an aluminum alloy selected from the group consisting of 6951,5005 and 3004.
Claim 6
Independent Claim
128 words
A method of brazing an assembly of aluminum or aluminum alloy parts requiring numerous joining sites, said brazing being carried out in a gas atmosphere containing gaseous species of O 2 and H 2 O, each in a concentration between 1-10 ppm, comprising: (a) depositing a filler metal alloy at the joining sites of said assembly, the latter consisting of Al-Si-Mg, said filler metal alloy having from 0.2 to 0.6% magnesium to (i) shorten the heating time to prevent runoff of liquid filler metal and (ii) to prevent generation of excess magnesium vapor that forms MgO, (b) heating said assembly and filler metal alloy in said gas atmosphere, said heating being continued to effect brazing without runoff of liquid filler metal and without generation of excess magnesium vapor.
Claim 7
Independent Claim
128 words
A method of brazing an assembly of aluminum or aluminum alloy parts requiring numerous joining sites, said brazing being carried out in a gas atmosphere containing gaseous species of O 2 and H 2 O, each in a concentration between 1-10 ppm, comprising: (a) depositing a filler metal alloy at the joining sites of said assembly, the latter consisting of Al-Si-Mg, said filler metal alloy having from 0.2 to 0.6% magnesium to (i) shorten the heating time to prevent runoff of liquid filler metal and (ii) to prevent generation of excess magnesium vapor that forms MgO, (b) heating said assembly and filler metal alloy in said gas atmosphere, said heating being continued to effect brazing without runoff of liquid filler metal and without generation of excess magnesium vapor.
Claim 8
Dependent Claim
39 words
A method of brazing as in claim 1, in which the heating rate is sufficient to provide a time period during which the said assembly is in a temperature zone of 400°-500° C. which is less than 2 minutes.
Claim 9
Dependent Claim
23 words
A method of brazing as in claim 1 in which said aluminum alloy parts are comprised of an aluminum alloy containing 0.4-1.2% Mg.
Claim 10
Dependent Claim
35 words
A method as in claim 1 in which said heating rate is arranged so that when the assembly experiences a temperature in the range of 400°-550° C., the heating rate is at least 50° C./minute.
References Cited (Backward Citations)
US3321828A
Cited
US3373482A
Cited
US3378914A
Cited
US3322517A
Cited
US3373483A
Cited
US4121750A
Cited
US3811177A
Cited
US3673678A
Cited
US3788824A
Cited
US3891400A
Cited
US3898053A
Cited
US3853547A
Cited
US4093782A
Cited
US4143802A
Cited
US4146163A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-23 | 1984-06-23 | 1984-12-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-23 | 1988-06-23 | 1988-12-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-23 | 1992-06-23 | 1992-12-23 | $7700.00 | Window Closed / Lapsed |