Assignee: Ford Motor Co
•
Filing: 1977-10-05
•
Granted: 1979-03-13
•
Expires: 1997-10-05
Abstract
Abstract A method of fluxless brazing of aluminum parts is disclosed. Gaseous species, such as O 2 and H 2 O, which inhibit wetting are controlled by rapid heating (at least 100° C./min) through a critical temperature range (such as 400°-590° C.) during heat-up to brazing temperatures. The formation of porosity through the oxide film and the collection of a promoter and wetting agent at the interface with the oxide film will thus occur simultaneously precluding disruption of wetting action by gaseous O 2 or H 2 O. Wicking of the wetting agent through the film porosity in the critical temperature range will then take place because of the limited time available for the reaction of gaseous O 2 and H 2 O with the film to form a duplex oxide. Heating may be carried out in a vacuum of 10 -3 Torr or less or in an inert atmosphere with pulsed heating, provided the critical heating rate is observed in said critical temperature range.
Inventors
- 👤 Walter L. Winterbottom
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 03:23
CPC Classifications
B; B23; B23K; B23K20/00; B23K20/22; B23K20/233; B23K20/2336; B23K1/00; B23K1/19
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
138 words
A method of fluxless brazing of aluminum parts comprising: (a) preparing and structurally relating together base metal parts, consisting of at least aluminum or aluminum alloy, to form an assembly, (b) depositing a filler metal consisting essentially of an aluminum-silicon-magnesium alloy, said metal being deposited at joining sites for said assembly, (c) subjecting said assembly to heating within a furnace and controlling the heating rate of the assembly therein so that when the assembly experiences a temperature within the range of 400°-590° C., the heating rate is sufficiently rapid to avoid porosity in any oxide film on said assembly and avoid reactions of the aluminum in said assembly with gaseous oxygen or water in the environment surrounding said assembly within the furnace, and (d) continuing said heating of said assembly above said critical temperature range to effect brazing.
Claim 2
Independent Claim
138 words
A method of fluxless brazing of aluminum parts comprising: (a) preparing and structurally relating together base metal parts, consisting of at least aluminum or aluminum alloy, to form an assembly, (b) depositing a filler metal consisting essentially of an aluminum-silicon-magnesium alloy, said metal being deposited at joining sites for said assembly, (c) subjecting said assembly to heating within a furnace and controlling the heating rate of the assembly therein so that when the assembly experiences a temperature within the range of 400°-590° C., the heating rate is sufficiently rapid to avoid porosity in any oxide film on said assembly and avoid reactions of the aluminum in said assembly with gaseous oxygen or water in the environment surrounding said assembly within the furnace, and (d) continuing said heating of said assembly above said critical temperature range to effect brazing.
Claim 3
Independent Claim
169 words
A method of fluxless brazing of aluminum parts, comprising: (a) preparing and structurally relating together base metal parts consisting of aluminum or an alloy thereof to form an assembly, (b) depositing a filler metal alloy at joining sites of said assembly, said filler metal alloy having an aluminum base and containing a promoter and gettering agent selected from the group consisting of magnesium, rare earch metals, beryllium, scandium, yttrium, calcium, strontium, and lithium, (c) subjecting said assembly and deposited filler metal to heat while exposed to an inert or low vacuum environment, said low vacuum when employed being characterized by a pressure of less than 10 -3 Torr, said heat being applied so that when the assembly experiences a critical temperature in a range of 400°-590° C. the heating rate is at least 100° C. per minute whereby the time period during which said assembly is in said critical temperature range is less than two minutes and, (d) continuing said heating beyond said critical temperature range to effect brazing.
Claim 4
Independent Claim
169 words
A method of fluxless brazing of aluminum parts, comprising: (a) preparing and structurally relating together base metal parts consisting of aluminum or an alloy thereof to form an assembly, (b) depositing a filler metal alloy at joining sites of said assembly, said filler metal alloy having an aluminum base and containing a promoter and gettering agent selected from the group consisting of magnesium, rare earch metals, beryllium, scandium, yttrium, calcium, strontium, and lithium, (c) subjecting said assembly and deposited filler metal to heat while exposed to an inert or low vacuum environment, said low vacuum when employed being characterized by a pressure of less than 10 -3 Torr, said heat being applied so that when the assembly experiences a critical temperature in a range of 400°-590° C. the heating rate is at least 100° C. per minute whereby the time period during which said assembly is in said critical temperature range is less than two minutes and, (d) continuing said heating beyond said critical temperature range to effect brazing.
Claim 5
Dependent Claim
78 words
The method as in claim 2 in which said heat is applied by pulsing to delay the formation of porosity in the oxide film on said base metal parts as well as the filler metal until said promoter dissociates from said filler metal, said heat pulsing being carried out particularly to provide a fluctuating heating rate of between 50° C./minute to over 100° C./minute when the base metal parts are at a temperature condition less than 545° C.
Claim 6
Independent Claim
104 words
A method of brazing of assembly having base metal parts and a filler metal with magnesium disposed at the joining sites, comprising: (a) heating a brazing assembly in an inert atmosphere or vacuum of less than 10 -3 Torr to a temperature at which the oxide film on said base metal parts begins to form pores, (b) controlling the heating rate at the condition of (a) so as to be in excess of 100° C./minute until said metal parts exceed 535° C., and (c) continuing to heat said assembly until the metal parts have been wetted by the filler metal at the joining sites.
Claim 7
Independent Claim
104 words
A method of brazing of assembly having base metal parts and a filler metal with magnesium disposed at the joining sites, comprising: (a) heating a brazing assembly in an inert atmosphere or vacuum of less than 10 -3 Torr to a temperature at which the oxide film on said base metal parts begins to form pores, (b) controlling the heating rate at the condition of (a) so as to be in excess of 100° C./minute until said metal parts exceed 535° C., and (c) continuing to heat said assembly until the metal parts have been wetted by the filler metal at the joining sites.
References Cited (Backward Citations)
US3811177A
Cited
US3673678A
Cited
US3782929A
Cited
US3807033A
Cited
US3891400A
Cited
US3898053A
Cited
US3963453A
Cited
US3963454A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-03-12 | 1982-09-11 | 1983-03-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-03-12 | 1986-09-11 | 1987-03-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-03-12 | 1990-09-11 | 1991-03-13 | $7700.00 | Window Closed / Lapsed |