Fiber structures of split multicomponent fibers and process therefor
Assignee: Akzona Inc
•
Filing: 1979-03-01
•
Granted: 1980-12-16
•
Expires: 1999-03-01
Abstract
Abstract Fibrillatable multicomponent fibers of the matrix segment type and a process for production of fiber structures by splitting shrinkable, basically unset, multi-component fibers consisting of at least two incompatible components which in the fiber cross section are arranged in the form of a matrix and several segments, the latter accounting for about 20% to 80% of the total cross section. After having been processed into fiber structures such as staple fibers, yarns or fabrics, the multicomponent fibers are treated with a liquid or gaseous organic solvent, particularly chlorinated lower alkanes, to partially or completely split the segment filaments from the matrix component. Useful solvents are those which will reduce the zero-shrinkage temperature of the matrix or the segment polymer by at least 160° C. and in which the polymer components constituting the fiber show different shrinkage behaviour. Splitting may be further enhanced by the application of mechanical agitation, e.g. by ultrasonic waves. Fabrics made from the multicomponent fibers may be woven, knitted, non-woven, flocked and three-dimensional.
Inventors
- 👤 Klaus Gerlach
- 👤 Nikolaus Mathes
- 👤 Friedbert Wechs
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 11:59
CPC Classifications
D; D01; D01F; D01F8/00; D01F8/04; D01D; D01D5/00; D01D5/28; Y; Y10; Y10T; Y10T428/00; Y10T428/23907; Y10T428/23943; Y10T428/23993; Y10T428/29; Y10T428/2913; Y10T428/2929; Y10T428/2931; Y10T428/2973; Y10T442/00; Y10T442/30; Y10T442/3146; Y10T442/40; Y10T442/444; Y10T442/60; Y10T442/608
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
149 words
A process for making fiber structures by splitting multicomponent fibers by treatment with an organic solvent, comprising treating shrinkable, essentially nonset multicomponent fibers comprising at least two incompatible components, which are arranged over the cross section of the fiber so as to form as to form a matrix and a plurality of segments, said segments comprising from about 20% to about 80% of the total cross section and at least three segments being arranged peripherally without being completely embedded in the matrix component, with a liquid or gaseous organic solvent which will lower the zero shrinkage temperature of one of the matrix polymer or the segment polymer by at least 160° C., and in which the polymer components of the fiber exhibit a differential shrinkage, said treatment being carried out at a temperature and for a time sufficient to entirely or partly split said multicomponent fibers into separate segments.
Claim 2
Dependent Claim
149 words
A process for making fiber structures by splitting multicomponent fibers by treatment with an organic solvent, comprising treating shrinkable, essentially nonset multicomponent fibers comprising at least two incompatible components, which are arranged over the cross section of the fiber so as to form as to form a matrix and a plurality of segments, said segments comprising from about 20% to about 80% of the total cross section and at least three segments being arranged peripherally without being completely embedded in the matrix component, with a liquid or gaseous organic solvent which will lower the zero shrinkage temperature of one of the matrix polymer or the segment polymer by at least 160° C., and in which the polymer components of the fiber exhibit a differential shrinkage, said treatment being carried out at a temperature and for a time sufficient to entirely or partly split said multicomponent fibers into separate segments.
Claim 3
Dependent Claim
14 words
The process of claim 1, wherein said organic solvent is a chlorinated lower alkane.
Claim 4
Dependent Claim
23 words
The process of claim 1 wherein at least 20% of the circumference of the peripheral segments is not encased in the matrix component.
Claim 5
Dependent Claim
23 words
The process of claim 3, wherein at least 50% of the circumference of the peripheral segments is not encased in the matrix component.
Claim 6
Dependent Claim
22 words
Process of claim 3 wherein the circumferential portion of the peripheral segment encased in the matrix component has a substantially convex shape.
Claim 7
Dependent Claim
16 words
The process of claim 5 wherein the peripheral segments are symmetrically arranged over the cross section.
Claim 8
Dependent Claim
16 words
The process of claim 5, wherein the peripheral segments are symmetrically arranged over the cross section.
Claim 9
Dependent Claim
38 words
The process of claim 1 wherein the fiber cross section also comprises a central segment of the same polymer as the peripheral segments or of a third polymer, completely separated from said peripheral segments by the matrix polymer.
Claim 10
Dependent Claim
30 words
The process of claim 1 wherein the time of induction of the shrinkage of the matrix polymer in said solvent differs from that of the polymer of the peripheral segments.
Claim 11
Dependent Claim
30 words
The process of claim 1 wherein the shrinkage rate of the matrix in said solvent is lower or higher than the shrinkage rate of the peripheral segments in said solvent.
Claim 12
Dependent Claim
20 words
The process of claim 1 wherein the shrinkage of the matrix or of the peripheral segments is at least 10%.
Claim 13
Dependent Claim
19 words
The process of claim 1 wherein the shrinkage of the matrix of the peripheral segment is at least 15%.
Claim 14
Dependent Claim
27 words
The process of claim 1 wherein the zero shrinkage temperature of either matrix polymer or segment polymer is lowered by at least 200° C. by said solvent.
Claim 15
Dependent Claim
11 words
The process of claim 1 wherein said solvent is methylene chloride.
Claim 16
Dependent Claim
10 words
The process of claim 1 wherein said solvent is 1,1,2,2-tetrachloroethane.
Claim 17
Dependent Claim
10 words
The process of claim 1 wherein said solvent is 1,1,2-trichloroethane.
Claim 18
Dependent Claim
9 words
The process claim 1 wherein said solvent is chloroform.
Claim 19
Dependent Claim
21 words
The process of claim 1 wherein said solvent is selected from the group consisting of methylene chloride, 1,1,2-tetrachloroethane, 1,1,2-trichloroethane and chloroform.
Claim 20
Dependent Claim
18 words
The process of claim 1 wherein said matrix component is polyalkylene terephthalate and said segment component is polyamide.
Claim 21
Dependent Claim
18 words
The process of claim 1 wherein the matrix component is polyamide and said segment component is polyalkylane terephthalate.
Claim 22
Dependent Claim
13 words
The process of claim 19 wherein said segment component is a polyamide blend.
Claim 23
Dependent Claim
13 words
The process of claim 20 wherein said matrix component is a polyamide blend.
Claim 24
Dependent Claim
22 words
The process according to claims 21 or 22 wherein said polyamide blend is a copolymer based on ε-caprolactam and hexamethylene diamine/adipic acid.
Claim 25
Dependent Claim
27 words
The process of claim 3 wherein the surface area of a peripheral segment in the filament cross section represents up to 1/5th of the total surface area.
Claim 26
Dependent Claim
19 words
The process of claim 1 wherein said multicomponent fibers are dyed simultaneously with said treatment with the organic solvent.
Claim 27
Dependent Claim
20 words
The process of claim 1 wherein the multicomponent fibers are subjected to a mechanical treatment simultaneously with said solvent treatment.
Claim 28
Dependent Claim
40 words
The process of claim 1 for the manufacture of fiber structures comprising processing said multicomponent fibers into a woven, warp knit or circular knit fabric, setting selected areas of said fabric and subsequently treating said fiber structure with said solvent.
Claim 29
Dependent Claim
25 words
Process according to claim 27, wherein said selected areas are set by embossing with hot calender rolls having raised portions corresponding to said selected areas.
Claim 30
Dependent Claim
94 words
A process for the manufacture of a fibrillated fiber comprising treating a differentially shrinkable, essentially nonset, fiber, consisting of a matrix and a plurality of segments made of different polymer components incompatible with each other, with a liquid or gaseous chlorinated lower alkane solvent which will lower the zero shrinkage of one of said polymers by at least 160° C. and in which the polymer components exhibit a differential shrinkage, said treatment being carried out at a temperature and for a time sufficient to entirely or partly split said multicomponent fibers into separate segments.
Claim 31
Dependent Claim
94 words
A process for the manufacture of a fibrillated fiber comprising treating a differentially shrinkable, essentially nonset, fiber, consisting of a matrix and a plurality of segments made of different polymer components incompatible with each other, with a liquid or gaseous chlorinated lower alkane solvent which will lower the zero shrinkage of one of said polymers by at least 160° C. and in which the polymer components exhibit a differential shrinkage, said treatment being carried out at a temperature and for a time sufficient to entirely or partly split said multicomponent fibers into separate segments.
Claim 32
Dependent Claim
21 words
The process of claim 29, wherein said solvent is selected from the group consisting of methylene chloride, 1,1,2,2-tetrachloroethane, 1,1,2-trichloroethane and chloroform.
References Cited (Backward Citations)
US2464301A
Cited
US2856638A
Cited
US3350488A
Cited
US3117906A
Cited
US3418200A
Cited
US3917784A
Cited
US3966865A
Cited
US3973905A
Cited
US4073988A
Cited
US4051287A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-16 | 1984-06-16 | 1984-12-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-16 | 1988-06-16 | 1988-12-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-16 | 1992-06-16 | 1992-12-16 | $7700.00 | Window Closed / Lapsed |