Modified phenolic aldehyde resin to produce an improved adhesive coating and method of making same
Assignee: PPG Industries Inc
•
Filing: 1979-06-08
•
Granted: 1980-12-09
•
Expires: 1999-06-08
Abstract
Abstract Phenolic aldehyde resins used in adhesive coatings for binding substrates to rubber are modified to provide better adhesion and to decrease the problem of blowholes on the substrate coated with the adhesive coating. The resin is modified by incorporating into the resin a compound selected from the group consisting of urea, thiourea, thionamide having one to six carbon atoms or mixture thereof. In the method of preparing the modified phenolic aldehyde resin about 1 to about 10 weight percent based on the resin is added to the aqueous solution either simultaneously with or sequentially after the addition of the phenolic compond and aldehyde. The modified phenolic resin is then combined with an elastomeric latex or latices to produce the improved adhesive coating.
Inventors
- 👤 Mikhail M. Girgis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 23:27
CPC Classifications
C; C08; C08L; C08L61/00; C08L61/34; C08G; C08G14/00; C08G14/02; C08G14/04; C08G14/06; C09; C09J; C09J121/00; C09J121/02; C08L2666/00; C08L2666/02; C08L2666/14; C08L2666/16; Y; Y10; Y10S; Y10S156/00; Y10S156/91; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/294; Y10T428/2942; Y10T428/2945; Y10T428/2947; Y10T428/2964; Y10T428/2967; Y10T428/2973
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
183 words
A phenolic aldehyde resin comprising: a phenolic compound, a thionamide having 1 to 6 carbon atoms or said thionamide in combination with urea or thiourea in an amount to about 1 to about 10 weight percent of the resin, and an aldehyde selected from the group consisting of formaldehyde, paraformaldehyde, acetaldehyde, which is prepared by: a. reacting the phenolic compound with a thionamide having 1 to 6 carbon atoms or thionamide mixture of said thionamide and urea or thiourea and aldehyde in an amount to give a mole ratio of phenolic compound to aldehyde in the range of about 0.2 to about 2.0 and a mole ratio of phenolic compound to thionamide or thionamide mixture in the range of about 0.2 to about 2.0 and a mole ratio of the thionamide or thionamide mixture to aldehyde in the range of about 0.5 to about 5.0 at an acid or a basic pH at a temperature in the range of about 0° C. to about 100° C. and for a period of time in the range of about 1 hr. to about 20 hrs.
Claim 2
Dependent Claim
183 words
A phenolic aldehyde resin comprising: a phenolic compound, a thionamide having 1 to 6 carbon atoms or said thionamide in combination with urea or thiourea in an amount to about 1 to about 10 weight percent of the resin, and an aldehyde selected from the group consisting of formaldehyde, paraformaldehyde, acetaldehyde, which is prepared by: a. reacting the phenolic compound with a thionamide having 1 to 6 carbon atoms or thionamide mixture of said thionamide and urea or thiourea and aldehyde in an amount to give a mole ratio of phenolic compound to aldehyde in the range of about 0.2 to about 2.0 and a mole ratio of phenolic compound to thionamide or thionamide mixture in the range of about 0.2 to about 2.0 and a mole ratio of the thionamide or thionamide mixture to aldehyde in the range of about 0.5 to about 5.0 at an acid or a basic pH at a temperature in the range of about 0° C. to about 100° C. and for a period of time in the range of about 1 hr. to about 20 hrs.
Claim 3
Dependent Claim
44 words
Phenolic aldehyde resin according to claim 1 wherein the resin is prepared by reacting the phenolic compound with a stoichemetric excess of aldehyde and adding the thionamide in an amount in the range of about 1 to about 10 weight percent of the resin.
Claim 4
Dependent Claim
20 words
Phenolic aldehyde resin according to claim 1 wherein an amount of hexamethoxymethylmelamine is substituted for a portion of the aldehyde.
Claim 5
Dependent Claim
36 words
The phenolic aldehyde resin of claim 1 wherein after the reaction of the phenolic compound, the aldehyde and thionamide, the reaction product is neutralized to a pH in the range of about 7 to about 7.5.
Claim 6
Dependent Claim
61 words
The phenolic aldehyde resin of claim 1 wherein the neutralized phenolic aldehyde resin reaction product is aged at the pH in the range of about 7 to about 7.5 at a temperature in the range of about 50° F. (10° C.) to about 140° F. (60°) for a residence time in the range of about 0.75 hours to about 20 hours.
Claim 7
Dependent Claim
23 words
The phenolic aldehyde resin of claim 1 wherein the phenolic compound is selected from resorcinol, phenol, or a mixture of resorcinol and phenol.
Claim 8
Dependent Claim
12 words
The phenolic aldehyde resin of claim 1 wherein the thionamide is thioacetamide.
References Cited (Backward Citations)
US2302885A
Cited
US2483854A
Cited
US2873718A
Cited
US3031431A
Cited
US3194294A
Cited
US3037968A
Cited
US3509018A
Cited
US3539484A
Cited
US3336185A
Cited
US3459585A
Cited
US3619252A
Cited
US3852232A
Cited
US3734918A
Cited
US3895163A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-09 | 1984-06-09 | 1984-12-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-09 | 1988-06-09 | 1988-12-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-09 | 1992-06-09 | 1992-12-09 | $7700.00 | Window Closed / Lapsed |